TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The ...TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The results show that the TA2 part of exhibiting near-equiaxed grains was Widmanst？tten α-laths microstructure. The TA15 part containing large columnar grains was fine basket-weave microstructure. The graded zone was divided into four deposited layers with 3000 μm in thickness. As the distance from the TA2 part increases, the alloy element contents and the β phase volume fraction increase, the α phase volume fraction decreases and the microstructure shows the evolution from Widmanst？tten α-laths to basket-weave α-laths gradually. The micro-hardness increases from the TA2 part to the TA15 part due to the solid solution strengthening and grain boundary strengthening.展开更多
In order to optimize the microstructure and composition of N18 zirconium alloy （Zr-1Sn-0.35Nb-0.35Fe-0.1Cr, in mass fraction, %）, which was developed in China in 1990s, the effect of microstructure and composition v...In order to optimize the microstructure and composition of N18 zirconium alloy （Zr-1Sn-0.35Nb-0.35Fe-0.1Cr, in mass fraction, %）, which was developed in China in 1990s, the effect of microstructure and composition variation on the corrosion resistance of the N18 alloy has been investigated. The autoclave corrosion tests were carried out in super heated steam at 400 ~C/10.3 MPa, in deionized water or lithiated water with 0.01 mol/L LiOH at 360 ~C/18.6 MPa. The exposure time lasted for 300-550 days according to the test temperature. The results show that the microstructure with a fine and uniform distribution of second phase particles （SPPs）, and the decrease of Sn content from 1% （in mass fraction, the same as follows） to 0.8% are of benefit to improving the corrosion resistance; It is detrimental to the corrosion resistance if no Cr addition. The addition of Nb content with upper limit （0.35%） is beneficial to improving the corrosion resistance. The addition of Cu less than 0.1% shows no remarkable influence upon the corrosion resistance for N18 alloy. Comparing the corrosion resistance of the optimized N18 with other commercial zirconium alloys, such as Zircaloy-4, ZIRLO, E635 and Ell0, the former shows superior corrosion resistance in all autoclave testing conditions mentioned above. Although the data of the corrosion resistance as fuel cladding for high burn-up has not been obtained yet, it is believed that the optimized N18 alloy is promising for the candidate of fuel cladding materials as high burn-up fuel assemblies. Based on the theory that the microstructural evolution of oxide layer during corrosion process will affect the corrosion resistance of zirconium alloys, the improvement of corrosion resistance of the N18 alloy by obtaining the microstructure with nano-size and uniform distribution of SPPs, and by decreasing the content of Sn and maintaining the content of Cr is discussed.展开更多
基金Project(2010CB731705)supported by the National Basic Research Program of China
文摘TA2/TA15 graded structural material（GSM） was fabricated by the laser additive manufacturing（LAM） process. The chemical composition, microstructure and micro-hardness of the as-deposited GSM were investigated. The results show that the TA2 part of exhibiting near-equiaxed grains was Widmanst？tten α-laths microstructure. The TA15 part containing large columnar grains was fine basket-weave microstructure. The graded zone was divided into four deposited layers with 3000 μm in thickness. As the distance from the TA2 part increases, the alloy element contents and the β phase volume fraction increase, the α phase volume fraction decreases and the microstructure shows the evolution from Widmanst？tten α-laths to basket-weave α-laths gradually. The micro-hardness increases from the TA2 part to the TA15 part due to the solid solution strengthening and grain boundary strengthening.
基金supported by the National Natural Science Foundation of China (Nos.50871064 and 50971084)Shanghai Leading Academic Discipline Project (No.S30107)
文摘In order to optimize the microstructure and composition of N18 zirconium alloy （Zr-1Sn-0.35Nb-0.35Fe-0.1Cr, in mass fraction, %）, which was developed in China in 1990s, the effect of microstructure and composition variation on the corrosion resistance of the N18 alloy has been investigated. The autoclave corrosion tests were carried out in super heated steam at 400 ~C/10.3 MPa, in deionized water or lithiated water with 0.01 mol/L LiOH at 360 ~C/18.6 MPa. The exposure time lasted for 300-550 days according to the test temperature. The results show that the microstructure with a fine and uniform distribution of second phase particles （SPPs）, and the decrease of Sn content from 1% （in mass fraction, the same as follows） to 0.8% are of benefit to improving the corrosion resistance; It is detrimental to the corrosion resistance if no Cr addition. The addition of Nb content with upper limit （0.35%） is beneficial to improving the corrosion resistance. The addition of Cu less than 0.1% shows no remarkable influence upon the corrosion resistance for N18 alloy. Comparing the corrosion resistance of the optimized N18 with other commercial zirconium alloys, such as Zircaloy-4, ZIRLO, E635 and Ell0, the former shows superior corrosion resistance in all autoclave testing conditions mentioned above. Although the data of the corrosion resistance as fuel cladding for high burn-up has not been obtained yet, it is believed that the optimized N18 alloy is promising for the candidate of fuel cladding materials as high burn-up fuel assemblies. Based on the theory that the microstructural evolution of oxide layer during corrosion process will affect the corrosion resistance of zirconium alloys, the improvement of corrosion resistance of the N18 alloy by obtaining the microstructure with nano-size and uniform distribution of SPPs, and by decreasing the content of Sn and maintaining the content of Cr is discussed.
