Continuous SiC fiber reinforced copper matrix （SiC~/Cu） composites were prepared by fiber coating method, and Ti6A14V interlayer was introduced as an interfacial modification coating to improve the interfacial bondi...Continuous SiC fiber reinforced copper matrix （SiC~/Cu） composites were prepared by fiber coating method, and Ti6A14V interlayer was introduced as an interfacial modification coating to improve the interfacial bonding strength. The interfacial reaction characteristics were investigated by transmission electron microscopy （TEM）. The results show that nearly all the titanium atoms reacted with the carbon coating of SiC fibers to form two layers of TiC. Also, a thin copper layer that is sandwiched between these two layers was detected. No Ti-Cu interfacial reaction product was observed. The formation process of the interfacial reaction along with its mechanism was discussed.展开更多
Using melt infiltration casting at different temperatures （965, 990 and 1015 °C） for different time （10 and 15 min）, the composites of （Cu50Zr43Al7）99.5Si0.5 bulk metallic glass reinforced with tungsten wir...Using melt infiltration casting at different temperatures （965, 990 and 1015 °C） for different time （10 and 15 min）, the composites of （Cu50Zr43Al7）99.5Si0.5 bulk metallic glass reinforced with tungsten wires were produced. X-ray diffraction （XRD）, scanning electron microscopy （SEM） and quasi-static compression tests were carried out to evaluate the microstructure and mechanical properties. The results show that the maximum ultimate compressive strength and strain-to-failure of about 1880 MPa and 16.7% were achieved, respectively, at the infiltration temperature of 965 °C for 15 min.展开更多
Cu47Ti33Zr11Ni6Sn2Si1-based bulk metallic glass matrix composites reinforced with tungsten wires were fabricated by infiltration process at different temperatures （850, 900, 950 and 1000 °C） and time （10, 20 a...Cu47Ti33Zr11Ni6Sn2Si1-based bulk metallic glass matrix composites reinforced with tungsten wires were fabricated by infiltration process at different temperatures （850, 900, 950 and 1000 °C） and time （10, 20 and 30 min） in a quartz or a steel tube. The mechanical tests were carried out by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The results show that the maximum strength and total strain of the composite are 1778 MPa and 2.8% fabricated in steel tube at 900 °C for 10 min, and 1582 MPa and 3.6% fabricated in quartz tube at 850 °C for 10 min, respectively.展开更多
基金supported by authors thank the Postdoctoral Science Foundation of China (No. 20090451393)the Aviation Science Foundation of China (No. 2009ZF53062)
文摘Continuous SiC fiber reinforced copper matrix （SiC~/Cu） composites were prepared by fiber coating method, and Ti6A14V interlayer was introduced as an interfacial modification coating to improve the interfacial bonding strength. The interfacial reaction characteristics were investigated by transmission electron microscopy （TEM）. The results show that nearly all the titanium atoms reacted with the carbon coating of SiC fibers to form two layers of TiC. Also, a thin copper layer that is sandwiched between these two layers was detected. No Ti-Cu interfacial reaction product was observed. The formation process of the interfacial reaction along with its mechanism was discussed.
文摘Using melt infiltration casting at different temperatures （965, 990 and 1015 °C） for different time （10 and 15 min）, the composites of （Cu50Zr43Al7）99.5Si0.5 bulk metallic glass reinforced with tungsten wires were produced. X-ray diffraction （XRD）, scanning electron microscopy （SEM） and quasi-static compression tests were carried out to evaluate the microstructure and mechanical properties. The results show that the maximum ultimate compressive strength and strain-to-failure of about 1880 MPa and 16.7% were achieved, respectively, at the infiltration temperature of 965 °C for 15 min.
文摘Cu47Ti33Zr11Ni6Sn2Si1-based bulk metallic glass matrix composites reinforced with tungsten wires were fabricated by infiltration process at different temperatures （850, 900, 950 and 1000 °C） and time （10, 20 and 30 min） in a quartz or a steel tube. The mechanical tests were carried out by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The results show that the maximum strength and total strain of the composite are 1778 MPa and 2.8% fabricated in steel tube at 900 °C for 10 min, and 1582 MPa and 3.6% fabricated in quartz tube at 850 °C for 10 min, respectively.