The Ti Bw reinforced near-α titanium matrix composite（Ti-5.8 Al-3.4 Zr-4.0 Sn-0.4 Mo-0.4 Nb-0.4 Si-0.06 C） was successfully synthesized by powder metallurgy and hot extrusion route. The effects of solution and agin...The Ti Bw reinforced near-α titanium matrix composite（Ti-5.8 Al-3.4 Zr-4.0 Sn-0.4 Mo-0.4 Nb-0.4 Si-0.06 C） was successfully synthesized by powder metallurgy and hot extrusion route. The effects of solution and aging temperature on the microstructure and high temperature tensile properties of the composite were investigated. The results revealed that the fine transformed β phase can be obtained by the solution treatment at β phase region and aging treatment, no other precipitates were observed. The α2 phase（Ti3 Al） can be acquired when the solution treated at α＋β phase region followed by aging treatment. With increasing the aging temperature from 500 to 700℃ for 5 h, the size of α2 precipitates increases from about 5 to about 30 nm. The Ti Bw are stable without any interfacial reaction during the heat treatments. The high temperature tensile properties show that the composite performed by solution and aging treatment exhibits good strengthening effects. With increasing the aging temperature from 500 to 700℃, the strength of the composite increases at the expense of elongation due to the increment of α2 precipitates.The strength of the composite at 600℃ increases by 17% to 986 MPa after 1000℃/2 h/AC and 700℃/5 h/AC heat treatment.展开更多
Carbon nanotube（CNT）-reinforced 6061 Al（CNT/6061 Al） composites were fabricated via powder metallurgy combined with friction stir processing（FSP）. CNTs were dispersed after FSP and accelerated the precipitation ...Carbon nanotube（CNT）-reinforced 6061 Al（CNT/6061 Al） composites were fabricated via powder metallurgy combined with friction stir processing（FSP）. CNTs were dispersed after FSP and accelerated the precipitation process of the CNT/6061 Al composites. However, the strengthening effect of CNTs on the T6-treated materials was insignificant,while the composites under the FSP and solution treatment conditions exhibited increased strength compared to the matrix.Precipitate-free zones（PFZs） were detected around CNTs in the T6-treated CNT/6061 Al composites, and a model was proposed to describe the effect of PFZs on strength. The calculations indicated that the strength of PFZs was similar to that of the T6-treated 6061 Al. As a result, the strengthening effect of CNTs on the T6-treated CNT/6061 Al composites was insignificant.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.51701114,11604204,51471063,51271111)the Youth Teacher Development Program of Shanghai Universities(Grant No.ZZGCD15101)+1 种基金Scientific Research Project of Shanghai University of Engineering ScienceTalents Project of Shanghai University of Engineering Science
文摘The Ti Bw reinforced near-α titanium matrix composite（Ti-5.8 Al-3.4 Zr-4.0 Sn-0.4 Mo-0.4 Nb-0.4 Si-0.06 C） was successfully synthesized by powder metallurgy and hot extrusion route. The effects of solution and aging temperature on the microstructure and high temperature tensile properties of the composite were investigated. The results revealed that the fine transformed β phase can be obtained by the solution treatment at β phase region and aging treatment, no other precipitates were observed. The α2 phase（Ti3 Al） can be acquired when the solution treated at α＋β phase region followed by aging treatment. With increasing the aging temperature from 500 to 700℃ for 5 h, the size of α2 precipitates increases from about 5 to about 30 nm. The Ti Bw are stable without any interfacial reaction during the heat treatments. The high temperature tensile properties show that the composite performed by solution and aging treatment exhibits good strengthening effects. With increasing the aging temperature from 500 to 700℃, the strength of the composite increases at the expense of elongation due to the increment of α2 precipitates.The strength of the composite at 600℃ increases by 17% to 986 MPa after 1000℃/2 h/AC and 700℃/5 h/AC heat treatment.
基金support of National Key Research & Development Plan under Grant No.2017YFB0703100Key Research Program of Frontier Sciences, CAS+1 种基金the CAS/SAFEA International Partnership Program for Creative Research Teamsthe National Natural Science Foundation of China under Grant No. 51501189
文摘Carbon nanotube（CNT）-reinforced 6061 Al（CNT/6061 Al） composites were fabricated via powder metallurgy combined with friction stir processing（FSP）. CNTs were dispersed after FSP and accelerated the precipitation process of the CNT/6061 Al composites. However, the strengthening effect of CNTs on the T6-treated materials was insignificant,while the composites under the FSP and solution treatment conditions exhibited increased strength compared to the matrix.Precipitate-free zones（PFZs） were detected around CNTs in the T6-treated CNT/6061 Al composites, and a model was proposed to describe the effect of PFZs on strength. The calculations indicated that the strength of PFZs was similar to that of the T6-treated 6061 Al. As a result, the strengthening effect of CNTs on the T6-treated CNT/6061 Al composites was insignificant.