Ethylene-Vinyl Acetate （EVA） redispersible powder and latex were used to modify mortar. Three kinds of curing regimes： standard curing, high temperature curing and freeze-thaw circle curing were adopted to cure the...Ethylene-Vinyl Acetate （EVA） redispersible powder and latex were used to modify mortar. Three kinds of curing regimes： standard curing, high temperature curing and freeze-thaw circle curing were adopted to cure the bonded samples. Bonding strength of EVA modified mortar was tested at 28 days. The development of bonding strengths under all three curing regimes were discussed and compared. The experimental results show that bonding strength increases with the increase of EVA content in mortar. The curing regime used within 28 days is critical according to the bonding strengths values under three curing regimes for different ages. The reasons of that the EVA can improve the bonding strength were analyzed.展开更多
The reducing water effectiveness of EVA latex and powder was observed. Adhesive strength of EVA modified mortar to tile under different curing condition was studied. And the adhesive strengths of mortars modified by E...The reducing water effectiveness of EVA latex and powder was observed. Adhesive strength of EVA modified mortar to tile under different curing condition was studied. And the adhesive strengths of mortars modified by EVA latex and by EVA powder were compared. The results show that the reducing water effectiveness is improved by 36.12% and 21.55%, respectively, when the content of EVA latex and powder are 8% and 4%. EVA latex and powder can improve the adhesive strength of modified mortar to tile under the standard curing, high temperature curing, and freeze-thaw circle curing. EVA latex can improve the water resistance obviously, besides improve the adhesive strengths of standard curing and high temperature curing, comparing with EVA powder.展开更多
文摘Ethylene-Vinyl Acetate （EVA） redispersible powder and latex were used to modify mortar. Three kinds of curing regimes： standard curing, high temperature curing and freeze-thaw circle curing were adopted to cure the bonded samples. Bonding strength of EVA modified mortar was tested at 28 days. The development of bonding strengths under all three curing regimes were discussed and compared. The experimental results show that bonding strength increases with the increase of EVA content in mortar. The curing regime used within 28 days is critical according to the bonding strengths values under three curing regimes for different ages. The reasons of that the EVA can improve the bonding strength were analyzed.
文摘The reducing water effectiveness of EVA latex and powder was observed. Adhesive strength of EVA modified mortar to tile under different curing condition was studied. And the adhesive strengths of mortars modified by EVA latex and by EVA powder were compared. The results show that the reducing water effectiveness is improved by 36.12% and 21.55%, respectively, when the content of EVA latex and powder are 8% and 4%. EVA latex and powder can improve the adhesive strength of modified mortar to tile under the standard curing, high temperature curing, and freeze-thaw circle curing. EVA latex can improve the water resistance obviously, besides improve the adhesive strengths of standard curing and high temperature curing, comparing with EVA powder.