The microstructure evolution and mechanical properties of the as-deposited γ-TiAl-based alloy specimen fabricated via laser melting deposition and as-annealed specimens at different temperatures were investigated.The...The microstructure evolution and mechanical properties of the as-deposited γ-TiAl-based alloy specimen fabricated via laser melting deposition and as-annealed specimens at different temperatures were investigated.The results show that the microstructure of as-deposited specimen is composed of fineα2(Ti3Al)+γlamellae.With the increase of annealing temperature,the bulk γ m(TiAl)phase gradually changes from single γ phase toγphase+acicularα2 phase,finally small γ phase+lamellar α2+γ phase.Compared with the mechanical properties of as-depositedγ-TiAl alloy(tensile strength 469 MPa,elongation 1.1%),after annealing at 1260℃ for 30 min followed by furnace cooling(FC),the room-temperature tensile strength of the specimen is 543.4 MPa and the elongation is 3.7%,which are obviously improved.展开更多
A comparative study of amorphous electroless Ni-W-P coatings on mild steel substrate treated by a high power diode laser and furnace annealing was presented.Effects of different laser operating parameters and furnace-...A comparative study of amorphous electroless Ni-W-P coatings on mild steel substrate treated by a high power diode laser and furnace annealing was presented.Effects of different laser operating parameters and furnace-annealing conditions on microstructures,in terms of crystallisation,pores formation and grain growth,were investigated using SEM/EDX and XRD. Corrosion behaviours of these coatings before and after various treatments were evaluated with anodic polarisation in 0.5 mol/L H2SO4 solution.The results show that the furnace-annealing produces either a mixture of nanocrystallined Ni and amorphous phases or precipitated Ni3P phase distributed in nanocrystallined Ni-based matrix,depending on annealing temperatures,whilst the laser treatment under the operating conditions only produces nanocrystallined Ni-based matrix with Ni3P precipitates.Corrosion performance of the coatings treated by both the laser and the furnace-annealing is dependent on the annealing temperature and laser operating conditions.Corrosion mechanisms of various treated-coatings were discussed in the consideration of phase constitutes and proportion,grain sizes of both Ni and Ni3P phases,pores formation and residual stresses.展开更多
基金Project(2017YFB1103600)supported by the National Key Research and Development Program of China。
文摘The microstructure evolution and mechanical properties of the as-deposited γ-TiAl-based alloy specimen fabricated via laser melting deposition and as-annealed specimens at different temperatures were investigated.The results show that the microstructure of as-deposited specimen is composed of fineα2(Ti3Al)+γlamellae.With the increase of annealing temperature,the bulk γ m(TiAl)phase gradually changes from single γ phase toγphase+acicularα2 phase,finally small γ phase+lamellar α2+γ phase.Compared with the mechanical properties of as-depositedγ-TiAl alloy(tensile strength 469 MPa,elongation 1.1%),after annealing at 1260℃ for 30 min followed by furnace cooling(FC),the room-temperature tensile strength of the specimen is 543.4 MPa and the elongation is 3.7%,which are obviously improved.
基金Project(Y2006F40) supported by the Natural Science Foundation of Shandong Province, ChinaProject(N00003) supported by UK Northwest Science Council through Northwest Laser Engineering Consortium (NWLEC)
文摘A comparative study of amorphous electroless Ni-W-P coatings on mild steel substrate treated by a high power diode laser and furnace annealing was presented.Effects of different laser operating parameters and furnace-annealing conditions on microstructures,in terms of crystallisation,pores formation and grain growth,were investigated using SEM/EDX and XRD. Corrosion behaviours of these coatings before and after various treatments were evaluated with anodic polarisation in 0.5 mol/L H2SO4 solution.The results show that the furnace-annealing produces either a mixture of nanocrystallined Ni and amorphous phases or precipitated Ni3P phase distributed in nanocrystallined Ni-based matrix,depending on annealing temperatures,whilst the laser treatment under the operating conditions only produces nanocrystallined Ni-based matrix with Ni3P precipitates.Corrosion performance of the coatings treated by both the laser and the furnace-annealing is dependent on the annealing temperature and laser operating conditions.Corrosion mechanisms of various treated-coatings were discussed in the consideration of phase constitutes and proportion,grain sizes of both Ni and Ni3P phases,pores formation and residual stresses.