The fracture behavior of polymer-bonded explosive(PBX) seriously affects the safety and reliability of weapon system.The effects of interface debonding and initial meso-damage on the fracture behavior of PBX under qua...The fracture behavior of polymer-bonded explosive(PBX) seriously affects the safety and reliability of weapon system.The effects of interface debonding and initial meso-damage on the fracture behavior of PBX under quasi-static tension are studied using numerical method.A twodimensional representative volume element(RVE) is established based on Voronoi model in which the component contents could be regulated and the particles are randomly distributed.A nonlinear damage model of polymer matrix relative to matrix depth between particles is constructed.The results show that the simulated strain-stress relation is coincident with experiment data.It is found that interface debonding leads to the nucleation and propagation of meso-cracks,and a main crack approximately perpendicular to the loading direction is generated finally.The interface debonding tends to occur in the interface perpendicular to the loading direction.There seems to be a phenomenon that strain softening and hardening alternatively appear around peak stress of stress and strain curve.It is shown that the initial damages of intragranular and interfacial cracks both decrease the modulus and failure stress,and the main crack tends to propagate toward the initial meso-cracks.展开更多
The authors study the large-time behaviour of global smooth solutions to initial-boundary value problems for the system of one-dimensional nonlinear thermoviscoelasticity. It is found that the solution may possess pha...The authors study the large-time behaviour of global smooth solutions to initial-boundary value problems for the system of one-dimensional nonlinear thermoviscoelasticity. It is found that the solution may possess phase transition phenomena when the material is not monotone, and the solution may decay to a stable state for the monotone case.展开更多
Understanding the impact of mining disturbances and creep deformation on the macroscopic deformation and the microscopic pore and fracture structures(MPFS)of coal is paramount for ensuring the secure extraction of coa...Understanding the impact of mining disturbances and creep deformation on the macroscopic deformation and the microscopic pore and fracture structures(MPFS)of coal is paramount for ensuring the secure extraction of coal resources.This study conducts cyclic loading-unloading and creep experiments on coal using a low-field nuclear magnetic resonance(NMR)experimental apparatus which is equipped with mechanical loading units,enabling real-time monitoring the T2spectrum.The experiments indicated that cyclic loading-unloading stress paths initiate internal damage within coal samples.Under identical creep stress conditions,coal samples with more initial damages had more substantial instantaneous deformation and creep deformation during the creep process.After undergoing nearly 35 h of staged creep,the total strains for coal samples CC01,CC02,and CC03 reach 2.160%,2.261%,and 2.282%,respectively.In the creep stage,the peak area ratio of seepage pores and microfractures(SPM)gradually diminishes.A higher degree of initial damage leads to a more pronounced compaction trend in the SPM of coal samples.Considering the porosity evolution of SPM during the creep process,this study proposes a novel fractional derivative model for the porosity evolution of SPM.The efficacy of the proposed model in predicting porosity evolution of SPM is substantiated through experimental validation.Furthermore,an analysis of the impact mechanisms on key parameters in the model was carried out.展开更多
文摘The fracture behavior of polymer-bonded explosive(PBX) seriously affects the safety and reliability of weapon system.The effects of interface debonding and initial meso-damage on the fracture behavior of PBX under quasi-static tension are studied using numerical method.A twodimensional representative volume element(RVE) is established based on Voronoi model in which the component contents could be regulated and the particles are randomly distributed.A nonlinear damage model of polymer matrix relative to matrix depth between particles is constructed.The results show that the simulated strain-stress relation is coincident with experiment data.It is found that interface debonding leads to the nucleation and propagation of meso-cracks,and a main crack approximately perpendicular to the loading direction is generated finally.The interface debonding tends to occur in the interface perpendicular to the loading direction.There seems to be a phenomenon that strain softening and hardening alternatively appear around peak stress of stress and strain curve.It is shown that the initial damages of intragranular and interfacial cracks both decrease the modulus and failure stress,and the main crack tends to propagate toward the initial meso-cracks.
文摘The authors study the large-time behaviour of global smooth solutions to initial-boundary value problems for the system of one-dimensional nonlinear thermoviscoelasticity. It is found that the solution may possess phase transition phenomena when the material is not monotone, and the solution may decay to a stable state for the monotone case.
基金the National Science Fund for Distinguished Young Scholars(No.52225403)the Natural Science Foundation of Shanxi Province(No.202303021212073)the National Natural Science Foundation of China(No.52104210)。
文摘Understanding the impact of mining disturbances and creep deformation on the macroscopic deformation and the microscopic pore and fracture structures(MPFS)of coal is paramount for ensuring the secure extraction of coal resources.This study conducts cyclic loading-unloading and creep experiments on coal using a low-field nuclear magnetic resonance(NMR)experimental apparatus which is equipped with mechanical loading units,enabling real-time monitoring the T2spectrum.The experiments indicated that cyclic loading-unloading stress paths initiate internal damage within coal samples.Under identical creep stress conditions,coal samples with more initial damages had more substantial instantaneous deformation and creep deformation during the creep process.After undergoing nearly 35 h of staged creep,the total strains for coal samples CC01,CC02,and CC03 reach 2.160%,2.261%,and 2.282%,respectively.In the creep stage,the peak area ratio of seepage pores and microfractures(SPM)gradually diminishes.A higher degree of initial damage leads to a more pronounced compaction trend in the SPM of coal samples.Considering the porosity evolution of SPM during the creep process,this study proposes a novel fractional derivative model for the porosity evolution of SPM.The efficacy of the proposed model in predicting porosity evolution of SPM is substantiated through experimental validation.Furthermore,an analysis of the impact mechanisms on key parameters in the model was carried out.