The Mg–Zn–Gd alloy with quasicrystal icosahedral phase was processed by high-pressure torsion (HPT). The effect of bimodal I-phase on the dynamic recrystallization was analyzed by transmission electron microscopy. T...The Mg–Zn–Gd alloy with quasicrystal icosahedral phase was processed by high-pressure torsion (HPT). The effect of bimodal I-phase on the dynamic recrystallization was analyzed by transmission electron microscopy. The results showed that the block I-phase can stimulate obvious particle-stimulated nucleation and dynamic recrystallization (DRX) grains were preferentially formed after HPT for 5 turns, while the granular I-phase only promoted the generation of sub-grains. The orientation relationship was determined as twofold//[1210] and fivefold//(0002)_(Mg). Moreover, after HPT for 9 turns, the DRX grains induced by block I-phase appeared to grow up and coarsened. Compared with block I-phase, the grains induced by granular I-phase presented much smaller size and distributed more homogeneous due to the strong pinning effect.展开更多
A high-strength AZ80 Mg alloy was prepared through multi-direction forging,thermal extrusion,and peak-aged heat treatment.The microstructure,crystallographic orientation and corrosion performance of extrusion-directio...A high-strength AZ80 Mg alloy was prepared through multi-direction forging,thermal extrusion,and peak-aged heat treatment.The microstructure,crystallographic orientation and corrosion performance of extrusion-direction,transverse-direction,and normal-direction specimens were investigated using scanning electron microscopy,electron backscatter diffraction,and atomic force microscopy,respectively.Experimental results showed that crystallographic orientation significantly influenced the corrosion performance of AZ80 Mg alloy.Corrosion rates largely increased with decreased(0001)crystallographic plane intensity,whereas the(10−10)and(2−1−10)crystallographic plane intensities increased.This study showed that the corrosion rates of alloy can be modified to some extent by controlling texture,thereby promoting the applications of high-strength AZ80 Mg alloys in the aerospace and national-defense fields.展开更多
基金supported by the National Natural Science Foundation of China(52125201 and 21975141)the National Key Basic Research and Development Program of China(2020YFA0210702)。
基金support from the National Natural Science Foundation of China(Grant Nos.51975175 and 52375329)the Projects of Natural Science Key Research of Anhui Province(2023AH051664).
文摘The Mg–Zn–Gd alloy with quasicrystal icosahedral phase was processed by high-pressure torsion (HPT). The effect of bimodal I-phase on the dynamic recrystallization was analyzed by transmission electron microscopy. The results showed that the block I-phase can stimulate obvious particle-stimulated nucleation and dynamic recrystallization (DRX) grains were preferentially formed after HPT for 5 turns, while the granular I-phase only promoted the generation of sub-grains. The orientation relationship was determined as twofold//[1210] and fivefold//(0002)_(Mg). Moreover, after HPT for 9 turns, the DRX grains induced by block I-phase appeared to grow up and coarsened. Compared with block I-phase, the grains induced by granular I-phase presented much smaller size and distributed more homogeneous due to the strong pinning effect.
基金The authors gratefully acknowledge the National Natural Science Foundation of China(grant no.51501181)
文摘A high-strength AZ80 Mg alloy was prepared through multi-direction forging,thermal extrusion,and peak-aged heat treatment.The microstructure,crystallographic orientation and corrosion performance of extrusion-direction,transverse-direction,and normal-direction specimens were investigated using scanning electron microscopy,electron backscatter diffraction,and atomic force microscopy,respectively.Experimental results showed that crystallographic orientation significantly influenced the corrosion performance of AZ80 Mg alloy.Corrosion rates largely increased with decreased(0001)crystallographic plane intensity,whereas the(10−10)and(2−1−10)crystallographic plane intensities increased.This study showed that the corrosion rates of alloy can be modified to some extent by controlling texture,thereby promoting the applications of high-strength AZ80 Mg alloys in the aerospace and national-defense fields.