The effect of ground steel-making slag on microstructure and composition of hydration products of ordinary Portland cement (OPC) was investigated by mercury intrusion porosimetry (MIP),X-ray diffraction (XRD) and diff...The effect of ground steel-making slag on microstructure and composition of hydration products of ordinary Portland cement (OPC) was investigated by mercury intrusion porosimetry (MIP),X-ray diffraction (XRD) and differential thermal analysis (DTA).Results show that ground steel-making slag is a kind of high activity mineral additives and it can raise the longer-age strength of OPC mortar.The total porosity and average pore diameter of OPC paste with ground steel-making slag increase with the increase of the amount of ground steel-making slag replacing OPC at various ages,while after 28 days most pores in OPC paste with ground steel-making slag do not influence the strength because the diameter of those pores is in the rang of 20 to 50nm.The hydration mechanism of ground steel-making slag is similar to that of OPC but different from that of fly ash and blast furnace slag.The hydration products of ground steel-making slag contain quite a lot of Ca(OH) 2 in long age.展开更多
文摘The effect of ground steel-making slag on microstructure and composition of hydration products of ordinary Portland cement (OPC) was investigated by mercury intrusion porosimetry (MIP),X-ray diffraction (XRD) and differential thermal analysis (DTA).Results show that ground steel-making slag is a kind of high activity mineral additives and it can raise the longer-age strength of OPC mortar.The total porosity and average pore diameter of OPC paste with ground steel-making slag increase with the increase of the amount of ground steel-making slag replacing OPC at various ages,while after 28 days most pores in OPC paste with ground steel-making slag do not influence the strength because the diameter of those pores is in the rang of 20 to 50nm.The hydration mechanism of ground steel-making slag is similar to that of OPC but different from that of fly ash and blast furnace slag.The hydration products of ground steel-making slag contain quite a lot of Ca(OH) 2 in long age.