Experimental study is performed on the probabilistic models for the long fatigue crack growth rates （da/dN） of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity...Experimental study is performed on the probabilistic models for the long fatigue crack growth rates （da/dN） of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity factor range going down to the threshold and the average stress effect. The probabilistic models were presented on the equation. They consist of the probabilistic da/dN-△K relations, the confidence-based da/dN-△K relations, and the probabilistic- and confidence-based da/dN-△K relations. Efforts were made respectively to characterize the effects of probabilistic assessments due to the scattering regularity of test data, the number of sampling, and both of them. These relations can provide wide selections for practice. Analysis on the test data of LZ50 steel indicates that the present models are available and feasible.展开更多
Threshold stress values, muging from ～8 to 16MPa·m1/2 can be obtained in a Ni-base alloy GH586 by varying the microstructure through heat treatments. The threshold and low crack growth rate behaviors at room tem...Threshold stress values, muging from ～8 to 16MPa·m1/2 can be obtained in a Ni-base alloy GH586 by varying the microstructure through heat treatments. The threshold and low crack growth rate behaviors at room temperature, with varying groin size and γ'-distribution, have been investigated. The results indicate that grain size is an important microstructurol parameter that affects fatigue crack growth threshold and propagation behaviors, as the values of △Kth increase with increasing grain size, but the γ' -distribution also has important effect. Analyses show that the effects of groin size on threshold and low crack-growth rate behavior result from heterogeneous deformation and roughness-induced crack closure due to crystallographic slipping and cracking in coarse microstructure. The higher △Kth and lower fatigue crack growth rate with increasing amounts of fine γ' phases are closely related to less damage accumulation level in deformation zone of crack-tip resulted from heterogeneous deformation due to dislocations' shearing γ' precipitates.展开更多
Experimental study is performed on the probabilistic models for the long fatigue crack growth rates (da/dN) of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity f...Experimental study is performed on the probabilistic models for the long fatigue crack growth rates (da/dN) of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity factor range going down to the threshold and the average stress effect. The probabilistic models were presented on the equation. They consist of the probabilistic da/dN-ΔK relations, the confidence-based da/dN-ΔK relations, and the probabilistic- and confidence-based da/dN-ΔK relations. Efforts were made respectively to characterize the effects of probabilistic assessments due to the scattering regularity of test data, the number of sampling, and both of them. These relations can provide wide selections for practice. Analysis on the test data of LZ50 steel indicates that the present models are available and feasible.展开更多
基金国家自然科学基金，Special Foundation of National Excellent Ph.D.Thesis，Outstanding Young Teachers of Ministry of Education of China
文摘Experimental study is performed on the probabilistic models for the long fatigue crack growth rates （da/dN） of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity factor range going down to the threshold and the average stress effect. The probabilistic models were presented on the equation. They consist of the probabilistic da/dN-△K relations, the confidence-based da/dN-△K relations, and the probabilistic- and confidence-based da/dN-△K relations. Efforts were made respectively to characterize the effects of probabilistic assessments due to the scattering regularity of test data, the number of sampling, and both of them. These relations can provide wide selections for practice. Analysis on the test data of LZ50 steel indicates that the present models are available and feasible.
文摘Threshold stress values, muging from ～8 to 16MPa·m1/2 can be obtained in a Ni-base alloy GH586 by varying the microstructure through heat treatments. The threshold and low crack growth rate behaviors at room temperature, with varying groin size and γ'-distribution, have been investigated. The results indicate that grain size is an important microstructurol parameter that affects fatigue crack growth threshold and propagation behaviors, as the values of △Kth increase with increasing grain size, but the γ' -distribution also has important effect. Analyses show that the effects of groin size on threshold and low crack-growth rate behavior result from heterogeneous deformation and roughness-induced crack closure due to crystallographic slipping and cracking in coarse microstructure. The higher △Kth and lower fatigue crack growth rate with increasing amounts of fine γ' phases are closely related to less damage accumulation level in deformation zone of crack-tip resulted from heterogeneous deformation due to dislocations' shearing γ' precipitates.
基金Project supported by the National Natural Science Foundation of China (Nos.50375130and50323003), the Special Foundation of National Excellent Ph.D.Thesis (No.200234) and thePlanned Itemforthe Outstanding Young Teachers ofMinistry ofEducationofChina (No.2101)
文摘Experimental study is performed on the probabilistic models for the long fatigue crack growth rates (da/dN) of LZ50 axle steel. An equation for crack growth rate was derived to consider the trend of stress intensity factor range going down to the threshold and the average stress effect. The probabilistic models were presented on the equation. They consist of the probabilistic da/dN-ΔK relations, the confidence-based da/dN-ΔK relations, and the probabilistic- and confidence-based da/dN-ΔK relations. Efforts were made respectively to characterize the effects of probabilistic assessments due to the scattering regularity of test data, the number of sampling, and both of them. These relations can provide wide selections for practice. Analysis on the test data of LZ50 steel indicates that the present models are available and feasible.