The first exothermic peak of cement-based material occurs a few minutes after mixing,and the properties of three dimensional(3D)printed concrete,such as setting time,are very sensitive to this.Against this background,...The first exothermic peak of cement-based material occurs a few minutes after mixing,and the properties of three dimensional(3D)printed concrete,such as setting time,are very sensitive to this.Against this background,based on the classical Park cement exothermic model of hydration,we propose and construct a numerical model of the first exothermic peak,taking into account the proportions of C_(3)S,C_(3)A and quicklime in particular.The calculated parameters are calibrated by means of relevant published exothermic test data.It is found that this developed model offers a good simulation of the first exothermic peak of hydration for C_(3)S and C_(3)A proportions from 0 to 100% of cement clinker and reflects the effect of quicklime content at 8%-10%.The unique value of this research is provision of an important computational tool for applications that are sensitive to the first exothermic peak of hydration,such as 3D printing.展开更多
The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied. These experiments were carried out in MoSi 2 laboratory furnace with 0 2?kg...The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied. These experiments were carried out in MoSi 2 laboratory furnace with 0 2?kg molten steel for equilibrium test and 2?kg molten steel for simulation test respectively. These results showed that the adjusting basicity of top slag with CaO is effective to prevent rephosphorization and resulphurization, and it is possible to dephosphorize and desulphurize and remove the inclusions from molten steel when basicity R of the top slag is adjusted to 2 0-3 10, and SiCaBa alloy is better than SiFe alloy in this relation.展开更多
The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied.These experiments were carried out in MoSi_2 laboratory furnace with 0.2 kg mo...The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied.These experiments were carried out in MoSi_2 laboratory furnace with 0.2 kg molten steel for equilibrium test and 2 kg molten steel for simulation test respectively.These results showed that the adjusting basicity of top slag with CaO is effective to prevent rephosphorization and resulphurization,and it is possible to dephosphorize and desulphurize and remove the inclusions from molten steel when basicity R of the top slag is adjusted to 2.0 — 3.10,and SiCaBa alloy is better than SiFe alloy in this relation.展开更多
基金financially supported by the National Natural Science Foundation of China(Grant No.52178240)the Shanghai Scientific Research Program(No.21DZ1200401).
文摘The first exothermic peak of cement-based material occurs a few minutes after mixing,and the properties of three dimensional(3D)printed concrete,such as setting time,are very sensitive to this.Against this background,based on the classical Park cement exothermic model of hydration,we propose and construct a numerical model of the first exothermic peak,taking into account the proportions of C_(3)S,C_(3)A and quicklime in particular.The calculated parameters are calibrated by means of relevant published exothermic test data.It is found that this developed model offers a good simulation of the first exothermic peak of hydration for C_(3)S and C_(3)A proportions from 0 to 100% of cement clinker and reflects the effect of quicklime content at 8%-10%.The unique value of this research is provision of an important computational tool for applications that are sensitive to the first exothermic peak of hydration,such as 3D printing.
文摘The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied. These experiments were carried out in MoSi 2 laboratory furnace with 0 2?kg molten steel for equilibrium test and 2?kg molten steel for simulation test respectively. These results showed that the adjusting basicity of top slag with CaO is effective to prevent rephosphorization and resulphurization, and it is possible to dephosphorize and desulphurize and remove the inclusions from molten steel when basicity R of the top slag is adjusted to 2 0-3 10, and SiCaBa alloy is better than SiFe alloy in this relation.
基金Sponsored by National Natural Science Foundation(59874014)
文摘The effect of top slag basicity on quality of steel treated with SiFe and SiCaBa alloy as exothermic agent in chemical heating was studied.These experiments were carried out in MoSi_2 laboratory furnace with 0.2 kg molten steel for equilibrium test and 2 kg molten steel for simulation test respectively.These results showed that the adjusting basicity of top slag with CaO is effective to prevent rephosphorization and resulphurization,and it is possible to dephosphorize and desulphurize and remove the inclusions from molten steel when basicity R of the top slag is adjusted to 2.0 — 3.10,and SiCaBa alloy is better than SiFe alloy in this relation.