The electrochemical reduction of solid TiO2 directly to solid metal is a promising alternative to the current Kroll process. The present work is aimed at studying the effect of electrolysis voltage on the rate of elec...The electrochemical reduction of solid TiO2 directly to solid metal is a promising alternative to the current Kroll process. The present work is aimed at studying the effect of electrolysis voltage on the rate of electrochemical reduction. The products of electrochemical reduction of TiO2 and Ti2O were examined using the scanning electron microscopy （SEM） and X-ray diffraction （XRD） techniques. The results show that Ti2O was reduced to low valent titanium oxide at 1.5 -1.7 V, which was the result of ionization of oxygen. TiO2 and Ti20 were reduced to titanium metal at 2.1-3.1 V, which was the co-action of ionization of oxygen and calciothermic reduction. The oxygen content decreased rapidly with voltage increasing from 2.1 to 2.6 V, while it changed little from 2.6 to 3.1 V. The optimized cell voltage was 2.6-3.1 V.展开更多
A novel and environmentally friendly route to directly prepare metallic vanadium from NaV03 by molten salt electrolysis is proposed. The feasibility about the direct electro-reduction of NaV03 to metallic vanadi- um i...A novel and environmentally friendly route to directly prepare metallic vanadium from NaV03 by molten salt electrolysis is proposed. The feasibility about the direct electro-reduction of NaV03 to metallic vanadi- um is analyzed based on the thermodynamic calculations and experimental verifications. The theoretical decomposition voltage of NaV03 to metallic vanadium is only 0.47 V at 800 ℃ and much lower than that of the alkali and alkali earth metal chloride salts. The value is slightly higher than that of low-valence vanadium oxides such as V203, V305 and VO. However, the low-valence vanadium oxides can he further electro-reduced to metallic vanadium thermodynamically. The thermodynamic analysis is verified by the experimental results. The direct preparation of metallic vanadium from NaV03 by molten salt electrolysis is feasible.展开更多
基金the Postdoctoral Science Foundation of China (No. 20060400409).
文摘The electrochemical reduction of solid TiO2 directly to solid metal is a promising alternative to the current Kroll process. The present work is aimed at studying the effect of electrolysis voltage on the rate of electrochemical reduction. The products of electrochemical reduction of TiO2 and Ti2O were examined using the scanning electron microscopy （SEM） and X-ray diffraction （XRD） techniques. The results show that Ti2O was reduced to low valent titanium oxide at 1.5 -1.7 V, which was the result of ionization of oxygen. TiO2 and Ti20 were reduced to titanium metal at 2.1-3.1 V, which was the co-action of ionization of oxygen and calciothermic reduction. The oxygen content decreased rapidly with voltage increasing from 2.1 to 2.6 V, while it changed little from 2.6 to 3.1 V. The optimized cell voltage was 2.6-3.1 V.
基金Supported by the National Basic Research Program of China(2013CB632606)the National Natural Science Foundation of China(51474200)+1 种基金the Youth Innovation Promotion AssociationCAS(2015036)
文摘A novel and environmentally friendly route to directly prepare metallic vanadium from NaV03 by molten salt electrolysis is proposed. The feasibility about the direct electro-reduction of NaV03 to metallic vanadi- um is analyzed based on the thermodynamic calculations and experimental verifications. The theoretical decomposition voltage of NaV03 to metallic vanadium is only 0.47 V at 800 ℃ and much lower than that of the alkali and alkali earth metal chloride salts. The value is slightly higher than that of low-valence vanadium oxides such as V203, V305 and VO. However, the low-valence vanadium oxides can he further electro-reduced to metallic vanadium thermodynamically. The thermodynamic analysis is verified by the experimental results. The direct preparation of metallic vanadium from NaV03 by molten salt electrolysis is feasible.