Single cold rolling and double cold rolling were applied to hot rolled strips with different reduction ratios. The evolutions of { 100}, { 111} and Goss face texture during double rolling were investigated by comparin...Single cold rolling and double cold rolling were applied to hot rolled strips with different reduction ratios. The evolutions of { 100}, { 111} and Goss face texture during double rolling were investigated by comparing the orientation distribution function （ODF） of the double rolled sample with that of the single rolled one. The double cold rolling texture is characterized by a higher γ-texture and a lower α-texture, and the { 111}〈112〉 component is improved remarkably. Based on the TEM observation and mechanical properties test, it is found that the reduction ratio assignment significantly affects the texture variation, as-annealing microstructures, and properties of the double cold rolled samples. These results may provide a theoretical guide for the industrial production of double cold rolled IF steel.展开更多
The relationships among the deformation, texture and deep drawing properties of IF steel were investigated. By adopting double cold rolling (DCR) technology, the deep drawing property has been developed evidently. Wit...The relationships among the deformation, texture and deep drawing properties of IF steel were investigated. By adopting double cold rolling (DCR) technology, the deep drawing property has been developed evidently. With the aid of orientation distribution function (ODF) analysis, it was found that he main reason for good property is the counterbalance in intensity of the ideal texture component {111} < 011 > and {111} < 112 >.展开更多
The structure and texture formation for single cold rolling （SCR） with annealing and double cold rolling （DCR） with annealing were investigated based on optical microscope and X-ray diffraction （XRD） with a Nb＋...The structure and texture formation for single cold rolling （SCR） with annealing and double cold rolling （DCR） with annealing were investigated based on optical microscope and X-ray diffraction （XRD） with a Nb＋Ti bearing interstitial free （IF） steel. The results indicated that DCR recrystallization grain was smaller than that of SCR sample and double cold rolling process resulted in better mechanical properties than those resulted from single cold rolling process with the same total reduction conducted. The plastic strain ratio increases from 2.23 for single cold rolling process to 3.2 for double rolling process. The fish-bone structure was observed in all SCR and DCR samples. DCR annealed sample is made up of equiaxed grains of almost uniform size, whereas SCR annealed sample shows a duplex grain structure, consisting of both large and small-sized grains. （Ti＋Nb）C and Fe（Ti＋Nb）P type precipitates were very rarely observed in SCR annealed and DCR annealed steels. The intensity of {111}∥ND for the DCR annealing was higher than that for SCR annealing.展开更多
文摘Single cold rolling and double cold rolling were applied to hot rolled strips with different reduction ratios. The evolutions of { 100}, { 111} and Goss face texture during double rolling were investigated by comparing the orientation distribution function （ODF） of the double rolled sample with that of the single rolled one. The double cold rolling texture is characterized by a higher γ-texture and a lower α-texture, and the { 111}〈112〉 component is improved remarkably. Based on the TEM observation and mechanical properties test, it is found that the reduction ratio assignment significantly affects the texture variation, as-annealing microstructures, and properties of the double cold rolled samples. These results may provide a theoretical guide for the industrial production of double cold rolled IF steel.
基金This work was supported by the National Natural Science Foundation of China under Grant No.59995440 and by the State Ministry of Science and Technology of China, the High Technology Development Plan (863) Project No.2001AA332020.
文摘The relationships among the deformation, texture and deep drawing properties of IF steel were investigated. By adopting double cold rolling (DCR) technology, the deep drawing property has been developed evidently. With the aid of orientation distribution function (ODF) analysis, it was found that he main reason for good property is the counterbalance in intensity of the ideal texture component {111} < 011 > and {111} < 112 >.
基金Sponsored by National Natural Science Foundation of China(51174020)Fundamental Research Funds for Central Universities of China(FRF-SD-12-010A)
文摘The structure and texture formation for single cold rolling （SCR） with annealing and double cold rolling （DCR） with annealing were investigated based on optical microscope and X-ray diffraction （XRD） with a Nb＋Ti bearing interstitial free （IF） steel. The results indicated that DCR recrystallization grain was smaller than that of SCR sample and double cold rolling process resulted in better mechanical properties than those resulted from single cold rolling process with the same total reduction conducted. The plastic strain ratio increases from 2.23 for single cold rolling process to 3.2 for double rolling process. The fish-bone structure was observed in all SCR and DCR samples. DCR annealed sample is made up of equiaxed grains of almost uniform size, whereas SCR annealed sample shows a duplex grain structure, consisting of both large and small-sized grains. （Ti＋Nb）C and Fe（Ti＋Nb）P type precipitates were very rarely observed in SCR annealed and DCR annealed steels. The intensity of {111}∥ND for the DCR annealing was higher than that for SCR annealing.