Based on four-year field inspection and investigation on deck pavement of mastic asphalt on Jiangyin Bridge, cracking causes of mastic asphalt are studied. Cracks of deck pavement are summarized on crack length and wi...Based on four-year field inspection and investigation on deck pavement of mastic asphalt on Jiangyin Bridge, cracking causes of mastic asphalt are studied. Cracks of deck pavement are summarized on crack length and width to get a clear view of their propagations. Traffic surveys including traffic volume, axle load and vehicle speed were also conducted to assess their influences. Samples taken on-site were tested with pulling-out test and fatigue test to benchmark their properties. According to the inspection and tests results, it is concluded that the cracks are induced by rutting and fatigue. Lack of fatigue resistance, not well bonded to the steel deck and insufficient high temperature stability are supposed to be the main reasons as well as high density of low speed, excessively overloaded trucks.展开更多
Based on the analysis of the main failures discovered in pavement on steel deck plate and the demanding service condition of the pavement on steel deck, high-temperature rutting test, low-temperature bending test and ...Based on the analysis of the main failures discovered in pavement on steel deck plate and the demanding service condition of the pavement on steel deck, high-temperature rutting test, low-temperature bending test and controlled stress flexural fatigue test are used to study the performance of asphalt mixtures modified by epoxy resin including high-temperature stability, low-temperature cracking-resistance, and fatigue cracking-resistance, which are served to evaluate the modification effect of epoxy resin of different contents. With the addition of epoxy resin, all the three performances are improved greatly. However, when the amount of epoxy resin added is over a certain value, the modification effect will be stable with no extra benefit detected. Finally, in terms of the properties of the three respects, 20%, 30%, 30% are given separately as the proposal adding contents.展开更多
文摘Based on four-year field inspection and investigation on deck pavement of mastic asphalt on Jiangyin Bridge, cracking causes of mastic asphalt are studied. Cracks of deck pavement are summarized on crack length and width to get a clear view of their propagations. Traffic surveys including traffic volume, axle load and vehicle speed were also conducted to assess their influences. Samples taken on-site were tested with pulling-out test and fatigue test to benchmark their properties. According to the inspection and tests results, it is concluded that the cracks are induced by rutting and fatigue. Lack of fatigue resistance, not well bonded to the steel deck and insufficient high temperature stability are supposed to be the main reasons as well as high density of low speed, excessively overloaded trucks.
文摘Based on the analysis of the main failures discovered in pavement on steel deck plate and the demanding service condition of the pavement on steel deck, high-temperature rutting test, low-temperature bending test and controlled stress flexural fatigue test are used to study the performance of asphalt mixtures modified by epoxy resin including high-temperature stability, low-temperature cracking-resistance, and fatigue cracking-resistance, which are served to evaluate the modification effect of epoxy resin of different contents. With the addition of epoxy resin, all the three performances are improved greatly. However, when the amount of epoxy resin added is over a certain value, the modification effect will be stable with no extra benefit detected. Finally, in terms of the properties of the three respects, 20%, 30%, 30% are given separately as the proposal adding contents.