The influence of two novel aging treatments, T6I6 (130 ℃, 80 min + 65 ℃, 240 h+130 ℃, 18 h) and high-temperature pre-precipitation(HTPP) aging (445 ℃, 30 min+120 ℃, 24 h) on the tensile properties, intergranular ...The influence of two novel aging treatments, T6I6 (130 ℃, 80 min + 65 ℃, 240 h+130 ℃, 18 h) and high-temperature pre-precipitation(HTPP) aging (445 ℃, 30 min+120 ℃, 24 h) on the tensile properties, intergranular corrosion, exfoliation corrosion behaviors and microstructures of 7075 Al alloy was studied, which were compared with the T6, T73 and RRA treatments. Fine η′ precipitate with high density was obtained in the alloy with the T6 and RRA treatments. The η′ precipitate density in the HTPP aged alloy is decreased due to the formation of coarse particles during the pre-precipitation process at high temperature of 445 ℃. The 7075-T6I6 alloy possesses higher precipitate density and whole precipitate volume fraction within the grain than the 7075-T73 alloy, and its whole precipitate volume fraction is even greater than that of the 7075-T6 alloy. Compared with T6 treatment, the RRA, T73, T6I6 and HTPP aging treatments cause the discontinuous distribution of the η precipitates at the grain boundary, which decreases the intergranular corrosion and exfoliation corrosion susceptibility of the alloy. Meanwhile, the T6I6 and RRA treatments can keep the high strength of the 7075 Al alloy, but the studied HTPP aging and T73 treatments lower its strength.展开更多
In the past decade, the sudden rise of high-entropy alloys(HEAs) has become a research hotspot in the domain of metal materials. HEAs break through the design concept of traditional single-principal element alloys, an...In the past decade, the sudden rise of high-entropy alloys(HEAs) has become a research hotspot in the domain of metal materials. HEAs break through the design concept of traditional single-principal element alloys, and the four core effects, especially the high entropy and cocktail effects, make HEAs exhibit much better corrosion resistance than traditional corrosion-resistant metal materials, e.g., stainless steels, copper-nickel alloys, and high-nickel alloys. Currently, the corrosion resistance of HEAs causes great concern in the field of corrosion research. This article reviews the corrosion behavior and mechanism of HEAs in various aqueous solutions, revealing the correlation among the composition, microstructure and corrosion resistance of HEAs, and elaborates the influence of heat treatment, anodizing treatment and preparation methods on the corrosion behavior of HEAs. This knowledge will benefit the on-demand design of corrosion-resistant HEAs, which is an important trend of future development. Finally, perspectives regarding the corrosion research of HEAs are outlined to guide future studies.展开更多
基金Project(2005CB623700) supported by the National Basic Research Program of China
文摘The influence of two novel aging treatments, T6I6 (130 ℃, 80 min + 65 ℃, 240 h+130 ℃, 18 h) and high-temperature pre-precipitation(HTPP) aging (445 ℃, 30 min+120 ℃, 24 h) on the tensile properties, intergranular corrosion, exfoliation corrosion behaviors and microstructures of 7075 Al alloy was studied, which were compared with the T6, T73 and RRA treatments. Fine η′ precipitate with high density was obtained in the alloy with the T6 and RRA treatments. The η′ precipitate density in the HTPP aged alloy is decreased due to the formation of coarse particles during the pre-precipitation process at high temperature of 445 ℃. The 7075-T6I6 alloy possesses higher precipitate density and whole precipitate volume fraction within the grain than the 7075-T73 alloy, and its whole precipitate volume fraction is even greater than that of the 7075-T6 alloy. Compared with T6 treatment, the RRA, T73, T6I6 and HTPP aging treatments cause the discontinuous distribution of the η precipitates at the grain boundary, which decreases the intergranular corrosion and exfoliation corrosion susceptibility of the alloy. Meanwhile, the T6I6 and RRA treatments can keep the high strength of the 7075 Al alloy, but the studied HTPP aging and T73 treatments lower its strength.
基金the financial support from the National Key Research and Development Program of China(No.2017YFB0702100)the National Natural Science Foundation of China(No.52071014)。
文摘In the past decade, the sudden rise of high-entropy alloys(HEAs) has become a research hotspot in the domain of metal materials. HEAs break through the design concept of traditional single-principal element alloys, and the four core effects, especially the high entropy and cocktail effects, make HEAs exhibit much better corrosion resistance than traditional corrosion-resistant metal materials, e.g., stainless steels, copper-nickel alloys, and high-nickel alloys. Currently, the corrosion resistance of HEAs causes great concern in the field of corrosion research. This article reviews the corrosion behavior and mechanism of HEAs in various aqueous solutions, revealing the correlation among the composition, microstructure and corrosion resistance of HEAs, and elaborates the influence of heat treatment, anodizing treatment and preparation methods on the corrosion behavior of HEAs. This knowledge will benefit the on-demand design of corrosion-resistant HEAs, which is an important trend of future development. Finally, perspectives regarding the corrosion research of HEAs are outlined to guide future studies.