In this study,hydrogels of P(NIPA-co-NVP)/clay were synthesized byγ-ray radiation.Different thermo-sensitive hydrogels were made under different experimental conditions such as dose,monomer ratio,and con- tent of cla...In this study,hydrogels of P(NIPA-co-NVP)/clay were synthesized byγ-ray radiation.Different thermo-sensitive hydrogels were made under different experimental conditions such as dose,monomer ratio,and con- tent of clay.X-ray diffraction shows that the layer distance between Na-clays is changed from 1.6 to 2.7 nm because Na-clay pieces can be intercalated or exfoliated by HTMAB,and that between P(NIPA-co-NVP)/clay pieces is 3.4 nm. The swelling property tests show that the LCST of P(NIPA-co-NVP) is higher than PNIPA.With the increase of NVP content,LCST is higher.As the ratio of NIPA/NVP is 95/5,hydrogel shows the best swelling property and LCST is 37℃.LCST of P(NIPA-co-NVP)/clay hydrogel is not changed,but the strength and swelling properties are better.展开更多
The thermo- and pH-responsive hydrogels were synthesized via copolymerization of N-isopropylacrylamide and al-lylamine hydrochloride monomers. The equilibrium swelling of the hydrogels was studied as a function of tem...The thermo- and pH-responsive hydrogels were synthesized via copolymerization of N-isopropylacrylamide and al-lylamine hydrochloride monomers. The equilibrium swelling of the hydrogels was studied as a function of temperature and pH in aqueous solutions. It was shown that controlled alteration of the hydrogel phase transition temperature can be achieved by changing their composition and pH of the environment. Increase in content of hydrophilic allylamine from 10 to 60 wt% in monomer mixture causes a shift of the phase transition temperature from 35oC to 47oC. Hydrogels with N-isopropylacrylamide/allylamine hydrochloride mass ratio of 3:2 show the highest pH-response. Values of average molecular weight between polymer cross-links, , and Flory parameter, χ, were calculated using temperature dependences of the equilibrium swelling of the synthesized hydrogel.展开更多
Electrolyte hydrogels are perspective materials for applications in electrochemical devices, which work at ambient temperatures. In this work, hydrogel sulpho-modified membranes were formed by radical co-polymerizatio...Electrolyte hydrogels are perspective materials for applications in electrochemical devices, which work at ambient temperatures. In this work, hydrogel sulpho-modified membranes were formed by radical co-polymerization of sodium styrensulphonate and potassium sulphopropyl acrylate with acrylamide and acrylonitrile. The hydrogel membranes were obtained in the form of thin films. Properties of the membranes were studied by thermogravimetry, mass-spectrometry and IR-spectrometry. The prepared membranes were thermally stable up to 70°C - 90°C, and showed ion exchange capacity and swelling coefficients sufficient for use as ion-exchange or proton-conducting membranes.展开更多
基金Supported by Natural Science Foundation of Henan Province,China(0611023900)
文摘In this study,hydrogels of P(NIPA-co-NVP)/clay were synthesized byγ-ray radiation.Different thermo-sensitive hydrogels were made under different experimental conditions such as dose,monomer ratio,and con- tent of clay.X-ray diffraction shows that the layer distance between Na-clays is changed from 1.6 to 2.7 nm because Na-clay pieces can be intercalated or exfoliated by HTMAB,and that between P(NIPA-co-NVP)/clay pieces is 3.4 nm. The swelling property tests show that the LCST of P(NIPA-co-NVP) is higher than PNIPA.With the increase of NVP content,LCST is higher.As the ratio of NIPA/NVP is 95/5,hydrogel shows the best swelling property and LCST is 37℃.LCST of P(NIPA-co-NVP)/clay hydrogel is not changed,but the strength and swelling properties are better.
文摘The thermo- and pH-responsive hydrogels were synthesized via copolymerization of N-isopropylacrylamide and al-lylamine hydrochloride monomers. The equilibrium swelling of the hydrogels was studied as a function of temperature and pH in aqueous solutions. It was shown that controlled alteration of the hydrogel phase transition temperature can be achieved by changing their composition and pH of the environment. Increase in content of hydrophilic allylamine from 10 to 60 wt% in monomer mixture causes a shift of the phase transition temperature from 35oC to 47oC. Hydrogels with N-isopropylacrylamide/allylamine hydrochloride mass ratio of 3:2 show the highest pH-response. Values of average molecular weight between polymer cross-links, , and Flory parameter, χ, were calculated using temperature dependences of the equilibrium swelling of the synthesized hydrogel.
文摘Electrolyte hydrogels are perspective materials for applications in electrochemical devices, which work at ambient temperatures. In this work, hydrogel sulpho-modified membranes were formed by radical co-polymerization of sodium styrensulphonate and potassium sulphopropyl acrylate with acrylamide and acrylonitrile. The hydrogel membranes were obtained in the form of thin films. Properties of the membranes were studied by thermogravimetry, mass-spectrometry and IR-spectrometry. The prepared membranes were thermally stable up to 70°C - 90°C, and showed ion exchange capacity and swelling coefficients sufficient for use as ion-exchange or proton-conducting membranes.