Non-porous carbon sphere was used as support to synthesize supported cobalt Fischer-Tropsch catalysts with high activity and durability. Strong metal-support interaction was avoided and intrinsic activity of pristine ...Non-porous carbon sphere was used as support to synthesize supported cobalt Fischer-Tropsch catalysts with high activity and durability. Strong metal-support interaction was avoided and intrinsic activity of pristine cobalt nano-particles was studied. Thermal decomposition synthesis method was applied to obtain cobalt catalysts with high dispersion and narrow particle size distribution. Furthermore the cobalt size can be controlled by the molar ratio of o-dichlorobenzene/benzylamine. Compared with supported cobalt catalysts prepared by incipient wetness impregnation method and ultrasonic impregnation method,the catalyst prepared by thermal decomposition method showed higher catalytic activity, higher long chain hydrocarbons selectivity and lower methane selectivity.展开更多
Different kinds of aluminum precursors were obtained from precipitating ammonium bicarbonate, ammonium carbonate, and saturated ammonium bicarbonate, then, boehmite (AlO(OH)), ammonium alumina carbonate hydroxide (AAC...Different kinds of aluminum precursors were obtained from precipitating ammonium bicarbonate, ammonium carbonate, and saturated ammonium bicarbonate, then, boehmite (AlO(OH)), ammonium alumina carbonate hydroxide (AACH) and their mixture were obtained, and then, different kinds of alumina were obtained after calcination. Three catalysts supported on the different alumina were obtained via impregnating cobalt and ruthenium by incipient wetness. The effects of different precipitants on composition of precursors were?studied by XRD, FTIR, and TGA. The property and structure of alumina were studied by XRD and BET. The supported catalysts were studied by characterizations of XRD and H2-TPR, and the catalytic performance for Fischer-Tropsch synthesis (FTS) were evaluated at a fix-bed reactor. The relations among the composition of precursors, the property of alumina and the catalytic performance of supported catalysts were researched thoroughly.展开更多
Surface chemical properties of supports have an important influence on active sites and their catalytic behavio r.Here,we fabricated a series of cobalt-based catalysts supported by carbon layer-coated ordered mesoporo...Surface chemical properties of supports have an important influence on active sites and their catalytic behavio r.Here,we fabricated a series of cobalt-based catalysts supported by carbon layer-coated ordered mesoporous silica(OMS) composites for higher alcohol synthesis(HAS).The carbon layers were derived from different sources and uniformly coated on the porous surface of OMS.Combined with the characterization results of carbonized catalysts,it is demonstrated that the carbon layer-coated supports significantly enhanced the metal dispersion and increased the ratio of Co2+ to Co0 sites,which further increased the CO conversion and alcohols selectivity.Moreover,it is found that the catalytic activity changed in line with the amount of defects and surface oxygenic groups of carbon layers,which re sulted from the different carbon sources.The highest space time yield of C2+OH was 27.5 mmol gcat-1h-1)obtained by the catalyst coated with glucose-derived carbon layer.But the carbon source is not the key factor influencing the distribution of Co-Co2+ dual sites and shows little effect on selectivity in HAS.These results may guide for further design of carbon supported catalysts.展开更多
基金supported by the Key Program project of the NSFC and China Petrochemical Corporation Joint Fund (Grant No. U1463210)the Natural Science Foundation of Hubei Province of China (2013CFA089)the Fundamental Research Funds for the Central Universities, South-Central University for Nationalities (CZZ13002 and CZW15099)
文摘Non-porous carbon sphere was used as support to synthesize supported cobalt Fischer-Tropsch catalysts with high activity and durability. Strong metal-support interaction was avoided and intrinsic activity of pristine cobalt nano-particles was studied. Thermal decomposition synthesis method was applied to obtain cobalt catalysts with high dispersion and narrow particle size distribution. Furthermore the cobalt size can be controlled by the molar ratio of o-dichlorobenzene/benzylamine. Compared with supported cobalt catalysts prepared by incipient wetness impregnation method and ultrasonic impregnation method,the catalyst prepared by thermal decomposition method showed higher catalytic activity, higher long chain hydrocarbons selectivity and lower methane selectivity.
文摘Different kinds of aluminum precursors were obtained from precipitating ammonium bicarbonate, ammonium carbonate, and saturated ammonium bicarbonate, then, boehmite (AlO(OH)), ammonium alumina carbonate hydroxide (AACH) and their mixture were obtained, and then, different kinds of alumina were obtained after calcination. Three catalysts supported on the different alumina were obtained via impregnating cobalt and ruthenium by incipient wetness. The effects of different precipitants on composition of precursors were?studied by XRD, FTIR, and TGA. The property and structure of alumina were studied by XRD and BET. The supported catalysts were studied by characterizations of XRD and H2-TPR, and the catalytic performance for Fischer-Tropsch synthesis (FTS) were evaluated at a fix-bed reactor. The relations among the composition of precursors, the property of alumina and the catalytic performance of supported catalysts were researched thoroughly.
基金support from the National Natural Science Foundation of China(Nos.U1462204,21706184)the National Postdoctoral Program for Innovative Talents of China(No.BX20180221)。
文摘Surface chemical properties of supports have an important influence on active sites and their catalytic behavio r.Here,we fabricated a series of cobalt-based catalysts supported by carbon layer-coated ordered mesoporous silica(OMS) composites for higher alcohol synthesis(HAS).The carbon layers were derived from different sources and uniformly coated on the porous surface of OMS.Combined with the characterization results of carbonized catalysts,it is demonstrated that the carbon layer-coated supports significantly enhanced the metal dispersion and increased the ratio of Co2+ to Co0 sites,which further increased the CO conversion and alcohols selectivity.Moreover,it is found that the catalytic activity changed in line with the amount of defects and surface oxygenic groups of carbon layers,which re sulted from the different carbon sources.The highest space time yield of C2+OH was 27.5 mmol gcat-1h-1)obtained by the catalyst coated with glucose-derived carbon layer.But the carbon source is not the key factor influencing the distribution of Co-Co2+ dual sites and shows little effect on selectivity in HAS.These results may guide for further design of carbon supported catalysts.