Mesostructured Ce0.6Zr0.4O2 solid solutions were synthesized by coprecipitation combined with evaporation-induced self-assembly process. The obtained materials were characterized by X-ray diffractometer （XRD）, Raman...Mesostructured Ce0.6Zr0.4O2 solid solutions were synthesized by coprecipitation combined with evaporation-induced self-assembly process. The obtained materials were characterized by X-ray diffractometer （XRD）, Raman, transmission electron microscopy （TEM）, N2 sorption, and hydrogen temperature programmed reduction （H2-TPR）. The results showed that the solid solutions consisted of uniform nanocrystals, which piled homogeneous mesopores of about 4 nm. Furthermore, different surfactants had little influence on the mesoporous structures. All these samples exhibited high thermal stability.展开更多
Ce0.6Zr0.3RE0.1O2(RE = Y, La, Pr, Tb)solid solutions were prepared by co-precipitation technique and characterized by a series of methods. XRD and FT-Raman results show that Ce0.6Zr0.3RE0.1O2 has cubic fluorite struct...Ce0.6Zr0.3RE0.1O2(RE = Y, La, Pr, Tb)solid solutions were prepared by co-precipitation technique and characterized by a series of methods. XRD and FT-Raman results show that Ce0.6Zr0.3RE0.1O2 has cubic fluorite structure. The different dopant ion radii bring different effect on the cell parameter of Ce0.6Zr0.3RE0 1O2. The X-ray photoelectron spec-troscopy (XPS) results show that the binding energy of Ce3d, Zr3d and O1s for Ce0.6Zr0.3RE0.1O2 rises compared with that for Ce0.6Zr0.4O2, indicating that dopant elements change chemistry environment of solid solutions which is available to improve redox performance. Compared with Pd/Ce0.6Zr0.4O2, doping Y and La does not change air/fuel (A/F) characteristic of TWCs, but doping Pr and Tb widens A/F operating window and makes HC, CO and NO have higher conversion. The light-off temperature of Pd/Ce0.6Zr0.3La0.1O2 is corresponding to that of Pd/Ce0.6Zr0.4O2. However, the light-off temperatures of Pd/Ce0.6Zr0.3M0.1O2(M = Y, Pr, Tb) are lower than that of Pd/Ce0.6Zr0.4O2, which keep much lower after high temperature treatments. Among Pd/Ce0.6Zr0.3RE0.1 O2, Pd/Ce0.6Zr0.3Tb0.1 O2 represents wider A/F operating window, higher conversion, lower light-off temperature and better high-temperature resistance.展开更多
基金supported by 973 Project (2004CB719500)the New Century Excellent Talents in University (NCET-05-415)the Natural Science Foundation of China (20673037)
文摘Mesostructured Ce0.6Zr0.4O2 solid solutions were synthesized by coprecipitation combined with evaporation-induced self-assembly process. The obtained materials were characterized by X-ray diffractometer （XRD）, Raman, transmission electron microscopy （TEM）, N2 sorption, and hydrogen temperature programmed reduction （H2-TPR）. The results showed that the solid solutions consisted of uniform nanocrystals, which piled homogeneous mesopores of about 4 nm. Furthermore, different surfactants had little influence on the mesoporous structures. All these samples exhibited high thermal stability.
基金Project supported by the Doctoral Foundation of Shandong Province (2004BS08001 ) Science Foundation of Ludong University (042901)
文摘Ce0.6Zr0.3RE0.1O2(RE = Y, La, Pr, Tb)solid solutions were prepared by co-precipitation technique and characterized by a series of methods. XRD and FT-Raman results show that Ce0.6Zr0.3RE0.1O2 has cubic fluorite structure. The different dopant ion radii bring different effect on the cell parameter of Ce0.6Zr0.3RE0 1O2. The X-ray photoelectron spec-troscopy (XPS) results show that the binding energy of Ce3d, Zr3d and O1s for Ce0.6Zr0.3RE0.1O2 rises compared with that for Ce0.6Zr0.4O2, indicating that dopant elements change chemistry environment of solid solutions which is available to improve redox performance. Compared with Pd/Ce0.6Zr0.4O2, doping Y and La does not change air/fuel (A/F) characteristic of TWCs, but doping Pr and Tb widens A/F operating window and makes HC, CO and NO have higher conversion. The light-off temperature of Pd/Ce0.6Zr0.3La0.1O2 is corresponding to that of Pd/Ce0.6Zr0.4O2. However, the light-off temperatures of Pd/Ce0.6Zr0.3M0.1O2(M = Y, Pr, Tb) are lower than that of Pd/Ce0.6Zr0.4O2, which keep much lower after high temperature treatments. Among Pd/Ce0.6Zr0.3RE0.1 O2, Pd/Ce0.6Zr0.3Tb0.1 O2 represents wider A/F operating window, higher conversion, lower light-off temperature and better high-temperature resistance.
