A new quaternary ammonium salt monomer was synthesized and a quaternary amination of lignin（ noted as QL）, with the monomer was carried out by grafting copolymerization. The products were characterized by Fourier Tr...A new quaternary ammonium salt monomer was synthesized and a quaternary amination of lignin（ noted as QL）, with the monomer was carried out by grafting copolymerization. The products were characterized by Fourier Transform Infrared spectroscopy（ FTIR）. The experimental results indicate that the yield of the monomer was 99.06%, and the conversion of the monomer and the grafting yield of QL were 93.69% and 185.78%, respectively. The feasibility of QL as the flocculant to be applied in color removal of five artificial dyes, erioehrome black T（dye A）, gongo red（dye B ）, direct fast black G （dye C ）, cuprofix blue green B （dye D ）, and acid black ATT （dye E ） was examined. Results show that OL exhihits the favorable flocculation nerformance and high stability.展开更多
Cationic fluorinated acrylate latex was prepared via semi-continuous emulsion copolymerization of cationic monomer and other monomers. The resultant latex and its film were characterized with dynamic light scattering ...Cationic fluorinated acrylate latex was prepared via semi-continuous emulsion copolymerization of cationic monomer and other monomers. The resultant latex and its film were characterized with dynamic light scattering detector and contact angle meter. Influences of amount of DMDAAC on the properties of resultant latex and its film were investigated in detail. Results show that the particle size of the latex has the minimum value knd the zeta potential of the latex is increased when the amount of DMDAAC is increased. In addition, the particle size of the latex is unimodal distribution when the amount of DMDAAC is not more than 2.5%. However, the particle size of the latex is bimodal distribution when the amount of DMDAAC is more than 2.5%. The contact angle is varied slightly with the increase of amount of DMDAAC when it is not more than 2.5%. Nevertheless, the contact angle is decreased with the increase of the amount of DMDAAC when it is more than 2.5%.展开更多
基金Supported by the National Nature Science Technology Item of of China(No.2005DC105005-01).
文摘A new quaternary ammonium salt monomer was synthesized and a quaternary amination of lignin（ noted as QL）, with the monomer was carried out by grafting copolymerization. The products were characterized by Fourier Transform Infrared spectroscopy（ FTIR）. The experimental results indicate that the yield of the monomer was 99.06%, and the conversion of the monomer and the grafting yield of QL were 93.69% and 185.78%, respectively. The feasibility of QL as the flocculant to be applied in color removal of five artificial dyes, erioehrome black T（dye A）, gongo red（dye B ）, direct fast black G （dye C ）, cuprofix blue green B （dye D ）, and acid black ATT （dye E ） was examined. Results show that OL exhihits the favorable flocculation nerformance and high stability.
基金supported by the Science and Technology Department of Zhejiang Province under Grant No. 2010C31040the financial support of Zhejiang Provincial Natural Science Foundation of China(No. Y4100152)Zhejiang University of Technology Natural Science Foundation(No.20100202)
文摘Cationic fluorinated acrylate latex was prepared via semi-continuous emulsion copolymerization of cationic monomer and other monomers. The resultant latex and its film were characterized with dynamic light scattering detector and contact angle meter. Influences of amount of DMDAAC on the properties of resultant latex and its film were investigated in detail. Results show that the particle size of the latex has the minimum value knd the zeta potential of the latex is increased when the amount of DMDAAC is increased. In addition, the particle size of the latex is unimodal distribution when the amount of DMDAAC is not more than 2.5%. However, the particle size of the latex is bimodal distribution when the amount of DMDAAC is more than 2.5%. The contact angle is varied slightly with the increase of amount of DMDAAC when it is not more than 2.5%. Nevertheless, the contact angle is decreased with the increase of the amount of DMDAAC when it is more than 2.5%.