Bearing ring is the crucial component of bearing. With regard to such problems as material waste, low efficiency and high energy consumption in current process of producing large bearing ring, a new process named ＂ca...Bearing ring is the crucial component of bearing. With regard to such problems as material waste, low efficiency and high energy consumption in current process of producing large bearing ring, a new process named ＂casting-rolling compound forming technology＂ is researched by taking the typical 42CrMo slew bearing as object. Through theoretical analysis, the design criteria of the main casting-rolling forming parameters are put forward at first. Then the constitutive relationship model of as-cast 42CrMo steel and its mathematical model of dynamic recrystallization are obtained according to the results of the hot compression experiment. By a coupled thermal-mechanical finite element model for radial-axial rolling of bearing ring, the fraction of dynamic recrystallization is calculated and recrystallized grains size are predicated. Meanwhile, the effects of the initial rolling temperature and feed rate of idle roll on material microstructure evolution are analyzed. Finally, the industrial rolling experiment is designed and performed, based on the simulation results. In addition, mechanical and metallographic tests are conducted on rolled bearing ring to get the mechanical parameters and metallographic structure. The experimental data and results show that the mechanical properties of bearing ring produced by casting-rolling compound forming technology are up to industrial standard, and a qualified bearing ring can be successfully formed by employing this new technology. Through the study, a process of forming large bearing ring directly by using casting ring blank is obtained, which could provide an effective theoretical guidance for manufacturing large ring parts. It also has an edge in saving material, lowering energy and improving efficiency.展开更多
The conjugation of semi-solid process technique and casting-rolling technique applied to produce the magnesium strips was studied. The semi-solid slurry has been prepared continuously by the mechanical method and its ...The conjugation of semi-solid process technique and casting-rolling technique applied to produce the magnesium strips was studied. The semi-solid slurry has been prepared continuously by the mechanical method and its temperature was controlled strictly at the same time. AZ91D and AZ31 casting magnesium alloys were applied to the experiment. The casting-rolling strips with non-dendritic structure were obtained and its main mechanical property is better. The process ability of the casting-rolling strips was studied. It is significative to link the semi-solid process techniques and casting-rolling techniques, through which we can get high quality magnesium alloy strips with non-dendritic structure and improve the overall properties of the products.展开更多
Fe-3Si steel strip was produced by thin slab casting and rolling （TSCR） process in the laboratory. The microstructure and texture of hot rolled strip by different total reduction and rolling schedules were observed ...Fe-3Si steel strip was produced by thin slab casting and rolling （TSCR） process in the laboratory. The microstructure and texture of hot rolled strip by different total reduction and rolling schedules were observed through EBSD technique and X-ray diffraction method. The rule of texture density for the a,ε and γ fibers was analyzed. When the total reduction was increased from 82.9% to 97.1%, the gradient of microstrueture and texture for A steel surface layer and center layer was found, {001}〈110〉 texture had higher intensity, and {001}〈110〉texture was changed to { 110 } 〈 001 〉 and { 112 } 〈 111 〉. The texture distribution with different reduction schedules for B steel was basically similar, but the Goss texture orientation density and volume fraction for B steel were higher, the hot rolling reduction schedule of C1 was effective for the formation of Goss texture. The research work was useful theoretical basis and reference data to develop electrical steel by thin slab continuous casting and direct rolling technology.展开更多
After the billet of Casting and Rolling GH4169 alloy was directly aged (DA) treated at 720 ℃ and 620 ℃, creep behavior and deformed features of the alloy were investigated by means of the measurement of creep curves...After the billet of Casting and Rolling GH4169 alloy was directly aged (DA) treated at 720 ℃ and 620 ℃, creep behavior and deformed features of the alloy were investigated by means of the measurement of creep curves and microstructure observation. Results show that the DA Casting and Rolling GH4169 Superalloy displays a lower strain rate during creep and longer lifetimes under the condition of the applied stress of 700 MPa at 650 ℃ , the creep lifetimes of the alloy decrease to 127 h as temperature is elevated to 660 ℃ , and therefore the alloy exhibits an obvious sensitivity of the applied temperatures. During creep, the deformation mechanism of the alloy is thought to be the twinning deformation and slipping of dislocation within the twinning regions. Thereinto, the dislocation slipping of the single and double orientations occur within the twins. As creep enters the tertiary steady state stage, the micro-crack appears on the grains boundaries along the direction vertical to the applied stress axis, and expands along the grain boundary up to fracture.展开更多
基金supported by Key Program of National Natural Science Foundation of China(Grant No.51135007)National Natural Science Foundation of China(Grant No.51075290)
文摘Bearing ring is the crucial component of bearing. With regard to such problems as material waste, low efficiency and high energy consumption in current process of producing large bearing ring, a new process named ＂casting-rolling compound forming technology＂ is researched by taking the typical 42CrMo slew bearing as object. Through theoretical analysis, the design criteria of the main casting-rolling forming parameters are put forward at first. Then the constitutive relationship model of as-cast 42CrMo steel and its mathematical model of dynamic recrystallization are obtained according to the results of the hot compression experiment. By a coupled thermal-mechanical finite element model for radial-axial rolling of bearing ring, the fraction of dynamic recrystallization is calculated and recrystallized grains size are predicated. Meanwhile, the effects of the initial rolling temperature and feed rate of idle roll on material microstructure evolution are analyzed. Finally, the industrial rolling experiment is designed and performed, based on the simulation results. In addition, mechanical and metallographic tests are conducted on rolled bearing ring to get the mechanical parameters and metallographic structure. The experimental data and results show that the mechanical properties of bearing ring produced by casting-rolling compound forming technology are up to industrial standard, and a qualified bearing ring can be successfully formed by employing this new technology. Through the study, a process of forming large bearing ring directly by using casting ring blank is obtained, which could provide an effective theoretical guidance for manufacturing large ring parts. It also has an edge in saving material, lowering energy and improving efficiency.
基金National Natural Science Foundation of China(Grant Nos.50175006,50374014).
文摘The conjugation of semi-solid process technique and casting-rolling technique applied to produce the magnesium strips was studied. The semi-solid slurry has been prepared continuously by the mechanical method and its temperature was controlled strictly at the same time. AZ91D and AZ31 casting magnesium alloys were applied to the experiment. The casting-rolling strips with non-dendritic structure were obtained and its main mechanical property is better. The process ability of the casting-rolling strips was studied. It is significative to link the semi-solid process techniques and casting-rolling techniques, through which we can get high quality magnesium alloy strips with non-dendritic structure and improve the overall properties of the products.
基金Item Sponsored by National Natural Science Foundation of China(50534020)
文摘Fe-3Si steel strip was produced by thin slab casting and rolling （TSCR） process in the laboratory. The microstructure and texture of hot rolled strip by different total reduction and rolling schedules were observed through EBSD technique and X-ray diffraction method. The rule of texture density for the a,ε and γ fibers was analyzed. When the total reduction was increased from 82.9% to 97.1%, the gradient of microstrueture and texture for A steel surface layer and center layer was found, {001}〈110〉 texture had higher intensity, and {001}〈110〉texture was changed to { 110 } 〈 001 〉 and { 112 } 〈 111 〉. The texture distribution with different reduction schedules for B steel was basically similar, but the Goss texture orientation density and volume fraction for B steel were higher, the hot rolling reduction schedule of C1 was effective for the formation of Goss texture. The research work was useful theoretical basis and reference data to develop electrical steel by thin slab continuous casting and direct rolling technology.
文摘After the billet of Casting and Rolling GH4169 alloy was directly aged (DA) treated at 720 ℃ and 620 ℃, creep behavior and deformed features of the alloy were investigated by means of the measurement of creep curves and microstructure observation. Results show that the DA Casting and Rolling GH4169 Superalloy displays a lower strain rate during creep and longer lifetimes under the condition of the applied stress of 700 MPa at 650 ℃ , the creep lifetimes of the alloy decrease to 127 h as temperature is elevated to 660 ℃ , and therefore the alloy exhibits an obvious sensitivity of the applied temperatures. During creep, the deformation mechanism of the alloy is thought to be the twinning deformation and slipping of dislocation within the twinning regions. Thereinto, the dislocation slipping of the single and double orientations occur within the twins. As creep enters the tertiary steady state stage, the micro-crack appears on the grains boundaries along the direction vertical to the applied stress axis, and expands along the grain boundary up to fracture.