Plasma carburization at two different methane-to-argon gas ratios (5:5 and 6:5) was carried out on the cast TiAl based alloy of Ti-46.5Al-2.5V-1Cr (mole fraction, %) in order to enhance its wear resistance. The result...Plasma carburization at two different methane-to-argon gas ratios (5:5 and 6:5) was carried out on the cast TiAl based alloy of Ti-46.5Al-2.5V-1Cr (mole fraction, %) in order to enhance its wear resistance. The results show that after carburization under both carburizing atmospheres, Ti2AlC and TiC are the main carbides in the carburized layer and the value of surface hardness reaches more than HK 822, but for the carburized TiAl treated at CH4:Ar of 5:5, the surface carbon concentration is higher and the carburized depth is slightly thicker than that of alloy carburized at CH4:Ar of 6:5. The result of the ball-on-disk test against hardening-steel counter bodies shows that the wear resistance of the TiAl based alloy carburized under two different carburizing atmospheres is improved compared with non-carburized TiAl. The tribological property is related to the carbon content, and the carburized layer obtained at CH4:Ar of 5:5 possesses a stable friction coefficient, lower volume loss or wear rate and narrow wear scar. The characteristic of the carburized layer was examined by using optical microscopy, glow discharge spectrum and micro-hardness tester.展开更多
基金Project(S0671071) supponed by the National Natural Science Foundation of ChinaProject(2006011052) supported by the National Natural Science Foundation of Shanxi Province, China
文摘Plasma carburization at two different methane-to-argon gas ratios (5:5 and 6:5) was carried out on the cast TiAl based alloy of Ti-46.5Al-2.5V-1Cr (mole fraction, %) in order to enhance its wear resistance. The results show that after carburization under both carburizing atmospheres, Ti2AlC and TiC are the main carbides in the carburized layer and the value of surface hardness reaches more than HK 822, but for the carburized TiAl treated at CH4:Ar of 5:5, the surface carbon concentration is higher and the carburized depth is slightly thicker than that of alloy carburized at CH4:Ar of 6:5. The result of the ball-on-disk test against hardening-steel counter bodies shows that the wear resistance of the TiAl based alloy carburized under two different carburizing atmospheres is improved compared with non-carburized TiAl. The tribological property is related to the carbon content, and the carburized layer obtained at CH4:Ar of 5:5 possesses a stable friction coefficient, lower volume loss or wear rate and narrow wear scar. The characteristic of the carburized layer was examined by using optical microscopy, glow discharge spectrum and micro-hardness tester.