The secondary reinforcement,crbon whiskers,may grow on the surface of parent rein- forcement,carbon fibres,by chemical vapour growth from acetylene using Fe salt as catalyzer.The optimal growing temperature is about 1...The secondary reinforcement,crbon whiskers,may grow on the surface of parent rein- forcement,carbon fibres,by chemical vapour growth from acetylene using Fe salt as catalyzer.The optimal growing temperature is about 1000℃,and while the concentra- tion of catalytic solution is appropriate,the carbon whiskers may deposite uniformly and link each other on the parent carbon fibre surface.If the temperature or concentration is too high,the coarse clusters of carbon may deposite on the fibre surface.The mechanism of carbon whisker growth is believed that the carbon atoms in vapour phase dissolve in the Fe salt drops over fibres,then the solid carbon grains precipitate on the fibre surface.展开更多
Carbon whiskers with new structure and morphology were observed when heating the milled graphite. Transmission electron microscopy and high resolution electron microscopy (HREM) show that carbon layers are almost perp...Carbon whiskers with new structure and morphology were observed when heating the milled graphite. Transmission electron microscopy and high resolution electron microscopy (HREM) show that carbon layers are almost perpendicular to the growth axes of carbon whiskers. Field emission scanning electron microscopy (FESEM) indicates that there are spirals appearing on the surface of the whiskers. The structure analysis shows that the growth mechanism of carbon whiskers is related to the trace amount of ZrC in the heated samples.展开更多
文摘The secondary reinforcement,crbon whiskers,may grow on the surface of parent rein- forcement,carbon fibres,by chemical vapour growth from acetylene using Fe salt as catalyzer.The optimal growing temperature is about 1000℃,and while the concentra- tion of catalytic solution is appropriate,the carbon whiskers may deposite uniformly and link each other on the parent carbon fibre surface.If the temperature or concentration is too high,the coarse clusters of carbon may deposite on the fibre surface.The mechanism of carbon whisker growth is believed that the carbon atoms in vapour phase dissolve in the Fe salt drops over fibres,then the solid carbon grains precipitate on the fibre surface.
文摘Carbon whiskers with new structure and morphology were observed when heating the milled graphite. Transmission electron microscopy and high resolution electron microscopy (HREM) show that carbon layers are almost perpendicular to the growth axes of carbon whiskers. Field emission scanning electron microscopy (FESEM) indicates that there are spirals appearing on the surface of the whiskers. The structure analysis shows that the growth mechanism of carbon whiskers is related to the trace amount of ZrC in the heated samples.