The intensifying process of polarization effect at room temperature in a pixellated Cadmium zinc telluride （CdZnTe） monolithic detector is studied. The process is attributed to the increase in build up space charges...The intensifying process of polarization effect at room temperature in a pixellated Cadmium zinc telluride （CdZnTe） monolithic detector is studied. The process is attributed to the increase in build up space charges in the CdZnTe crystal, which causes an expansion of the space charge region under the irradiated area. The simulations of electric potential distributions indicate that the distorted electric potential due to the high X-ray flux is significantly changed and even deteriorated due to increasing space charges within the irradiated volume. An agreement between the space charge distribution and electric potential is discussed.展开更多
The growth of CdZnTe crystals with diameter up to 60 mm using bottom-seeded Bridgman method as well as Bridgman accelerated crucible rotation technique (ACRT-B) was investigated. Both ingots exhibit high yields, where...The growth of CdZnTe crystals with diameter up to 60 mm using bottom-seeded Bridgman method as well as Bridgman accelerated crucible rotation technique (ACRT-B) was investigated. Both ingots exhibit high yields, where single crystal with the volume exceeding 200 cm3 is produced. The crystal properties of two ingots were compared in the aspects of yields, crystalline quality and composition uniformity. For CdZnTe ingot grown by bottom-seeded Bridgman method, the full width at half-maximum (FWHM) of X-ray rocking curve was determined to be 36″, indicating a better crystalline quality than ingot grown by ACRT-B method, which gave FWHM of 56″. The composition distribution of Zn and In in CdZnTe was determined by using electron probe microanalysis (EPMA) and inductively coupled plasma mass spectrometry (ICP-MS), respectively. The effective segregation coefficients of Zn kZn and In kIn in the two ingots were evaluated by fitting the experimental data with the Pfann equation.展开更多
The mechanical characters of CdZnTe crystal were investigated by nanoscratch tests, and the effects of mechanical anisotropy on the material removal rate and surface quality were studied by polishing tests. There is a...The mechanical characters of CdZnTe crystal were investigated by nanoscratch tests, and the effects of mechanical anisotropy on the material removal rate and surface quality were studied by polishing tests. There is a peak of frictional coefficient at the early stage of scratch, and increasing the vertical force will result in the increase of peak value correspondingly. The fluctuation phenomenon of frictional coefficient is generated at high vertical force. The lateral forces show the apparent twofold and threefold symmetries on （110） and （111） planes, respectively. To obtain high surface quality, low polishing pressure and hard direction （〈 T10 〉 directions on （110） plane and 〈 112 〉 directions on （111） plane） should be selected, and to achieve high material removal rate, high polishing pressure and soft direction （〈001〉 directions on （110） plane and 〈 121 〉 directions on （111） plane） should be selected.展开更多
A high-quality Cr 3＋：CdWO4 single crystal at a size of approximatelyΦ25×80 mm is grown using the Bridgman method with CdO,WO3,and Cr2O3 as raw materials and their molar ratio of 100：100：0.5.The temperature g...A high-quality Cr 3＋：CdWO4 single crystal at a size of approximatelyΦ25×80 mm is grown using the Bridgman method with CdO,WO3,and Cr2O3 as raw materials and their molar ratio of 100：100：0.5.The temperature gradient of solid-liquid interface at growth is approximately 50？C/cm and the growth rate is 0.05 mm/h.The X-ray diffraction（XRD）,absorption,excitation,and emission spectra of different parts of the as-grown and O2-annealed crystals are investigated.Two strong broad optical absorption bands of about 472 and 708 nm are observed,and they are associated with the transitions 4 A2→ 4 T1 and 4 A2→ 4 T2.The weak 4 T2→ 2 E transition（the R-line）at 632 nm is also observed.The crystal-field parameter Dq and the Racah parameters B and C are estimated to be 1 412.4,776.8,and 3 427.6 cm？ 1,respectively,according to the absorption spectra and crystal-splitting theory.A broadband fluorescence at about 1 000 nm due to 4 T2→ 4 A2 transition is produced by exciting the samples at 675 nm.After being annealed in an O2 atmosphere,the crystals become more transparent,while the effective light absorption of Cr 3＋ ions is evidently enhanced and the emission intensity is also strengthened due to the reduction of oxygen vacancies in the CdWO4 crystal after annealing.展开更多
基金supported by the National Science Associated Foundation of China (No. 10876044)Fundamental Research Funds for the Central Universities (No. CDJXS11122219)
文摘The intensifying process of polarization effect at room temperature in a pixellated Cadmium zinc telluride （CdZnTe） monolithic detector is studied. The process is attributed to the increase in build up space charges in the CdZnTe crystal, which causes an expansion of the space charge region under the irradiated area. The simulations of electric potential distributions indicate that the distorted electric potential due to the high X-ray flux is significantly changed and even deteriorated due to increasing space charges within the irradiated volume. An agreement between the space charge distribution and electric potential is discussed.
基金Project(50772091) supported by the National Natural Science Foundation of ChinaProject(2008044185) supported by China Postdoctoral Science Foundation
文摘The growth of CdZnTe crystals with diameter up to 60 mm using bottom-seeded Bridgman method as well as Bridgman accelerated crucible rotation technique (ACRT-B) was investigated. Both ingots exhibit high yields, where single crystal with the volume exceeding 200 cm3 is produced. The crystal properties of two ingots were compared in the aspects of yields, crystalline quality and composition uniformity. For CdZnTe ingot grown by bottom-seeded Bridgman method, the full width at half-maximum (FWHM) of X-ray rocking curve was determined to be 36″, indicating a better crystalline quality than ingot grown by ACRT-B method, which gave FWHM of 56″. The composition distribution of Zn and In in CdZnTe was determined by using electron probe microanalysis (EPMA) and inductively coupled plasma mass spectrometry (ICP-MS), respectively. The effective segregation coefficients of Zn kZn and In kIn in the two ingots were evaluated by fitting the experimental data with the Pfann equation.
基金supported by the Key Project of the National Natural Science Foundation of China (No. 50535020)the Fund of the State Key Laboratory of Solidification Processing in Northwestern Polytechnical University (No. SKLSP200902)
文摘The mechanical characters of CdZnTe crystal were investigated by nanoscratch tests, and the effects of mechanical anisotropy on the material removal rate and surface quality were studied by polishing tests. There is a peak of frictional coefficient at the early stage of scratch, and increasing the vertical force will result in the increase of peak value correspondingly. The fluctuation phenomenon of frictional coefficient is generated at high vertical force. The lateral forces show the apparent twofold and threefold symmetries on （110） and （111） planes, respectively. To obtain high surface quality, low polishing pressure and hard direction （〈 T10 〉 directions on （110） plane and 〈 112 〉 directions on （111） plane） should be selected, and to achieve high material removal rate, high polishing pressure and soft direction （〈001〉 directions on （110） plane and 〈 121 〉 directions on （111） plane） should be selected.
基金supported by the National Natural Science Foundation of China(No.50972061)the Zhejiang Provincial Natural Science Foundation of China(No.R4100364)K.C.Wong Magna Fund at NingboUniversity
文摘A high-quality Cr 3＋：CdWO4 single crystal at a size of approximatelyΦ25×80 mm is grown using the Bridgman method with CdO,WO3,and Cr2O3 as raw materials and their molar ratio of 100：100：0.5.The temperature gradient of solid-liquid interface at growth is approximately 50？C/cm and the growth rate is 0.05 mm/h.The X-ray diffraction（XRD）,absorption,excitation,and emission spectra of different parts of the as-grown and O2-annealed crystals are investigated.Two strong broad optical absorption bands of about 472 and 708 nm are observed,and they are associated with the transitions 4 A2→ 4 T1 and 4 A2→ 4 T2.The weak 4 T2→ 2 E transition（the R-line）at 632 nm is also observed.The crystal-field parameter Dq and the Racah parameters B and C are estimated to be 1 412.4,776.8,and 3 427.6 cm？ 1,respectively,according to the absorption spectra and crystal-splitting theory.A broadband fluorescence at about 1 000 nm due to 4 T2→ 4 A2 transition is produced by exciting the samples at 675 nm.After being annealed in an O2 atmosphere,the crystals become more transparent,while the effective light absorption of Cr 3＋ ions is evidently enhanced and the emission intensity is also strengthened due to the reduction of oxygen vacancies in the CdWO4 crystal after annealing.
文摘通过介质膜 Zn S、Cd Te薄膜材料的 Ar+ 束溅射沉积研究 ,结合 Hg Cd Te器件工艺 ,成功制备了以 Zn S、Cd Te双层介质膜为绝缘层的 Hg Cd Te MIS器件 ;通过对器件的 C- V特性实验分析 ,获得了 Cd Te/ Hg Cd Te界面电学特性参数 .实验表明 :溅射沉积介质膜 Cd Te+Zn S对 Hg Cd Te的表面钝化已经可以满足 Hg Cd