Air nanobubbles(A-NBs)were used to inhibit the brass corrosion in circulating cooling water for the first time in the study.The results of mass loss method and electrochemical method showed that A-NBs had the obvious ...Air nanobubbles(A-NBs)were used to inhibit the brass corrosion in circulating cooling water for the first time in the study.The results of mass loss method and electrochemical method showed that A-NBs had the obvious corrosion inhibition effect.The inhibition rate reached 52%at 35℃.The impedance and surface characterization results of corrosion samples indicated that the corrosion inhibition mechanisms of A-NBs mainly included adsorption of corrosion ions,promoting the formation of the passivation film on metal surface and the formation of the bubble layer and scale film on metal surface.A-NBs are potential excellent corrosion inhibitors.展开更多
The effects of streaks on boundary layer transition depend on the initial amplitude of T-S waves introduced to excite the transition. This problem was studied in a flat-plate boundary layer in water tunnel by using hy...The effects of streaks on boundary layer transition depend on the initial amplitude of T-S waves introduced to excite the transition. This problem was studied in a flat-plate boundary layer in water tunnel by using hydrogen bubble method. Three T-S wave initial amplitudes were tested. The results show that both narrow and wide-spacing streaks depress the transition excited by T-S waves with lower initial amplitude. However, when transition is excited by T-S waves of higher initial amplitude, the narrow-spacing streaks depress the transition, while the wide-spacing streaks promote the transition. Futrther the underlying mechanisms were also analyzed.展开更多
基金supported by National Natural Science Foundation of China(52170074).
文摘Air nanobubbles(A-NBs)were used to inhibit the brass corrosion in circulating cooling water for the first time in the study.The results of mass loss method and electrochemical method showed that A-NBs had the obvious corrosion inhibition effect.The inhibition rate reached 52%at 35℃.The impedance and surface characterization results of corrosion samples indicated that the corrosion inhibition mechanisms of A-NBs mainly included adsorption of corrosion ions,promoting the formation of the passivation film on metal surface and the formation of the bubble layer and scale film on metal surface.A-NBs are potential excellent corrosion inhibitors.
基金supported by the National Natural Science Foundation of China (11072017)
文摘The effects of streaks on boundary layer transition depend on the initial amplitude of T-S waves introduced to excite the transition. This problem was studied in a flat-plate boundary layer in water tunnel by using hydrogen bubble method. Three T-S wave initial amplitudes were tested. The results show that both narrow and wide-spacing streaks depress the transition excited by T-S waves with lower initial amplitude. However, when transition is excited by T-S waves of higher initial amplitude, the narrow-spacing streaks depress the transition, while the wide-spacing streaks promote the transition. Futrther the underlying mechanisms were also analyzed.