In this paper, any two of the three anticorrosion agents, that is emulsifier (OP-10), soluble glass (Na2O·nSiO2) and glycerin (C3H8O3), were treated simultaneously on the surface of amorphous (a- ) MgNi + 5% Ml2M...In this paper, any two of the three anticorrosion agents, that is emulsifier (OP-10), soluble glass (Na2O·nSiO2) and glycerin (C3H8O3), were treated simultaneously on the surface of amorphous (a- ) MgNi + 5% Ml2Mg17(MI denotes the lanthanum-rich mish metal) electrode and the electrolyte. Effect of the synergistic anticorrosion treatment on charging/discharging cycle stability of the electrode was investigated. Contrasted with single treatment method, the cycling stability of the electrodes was further improved. The desirable synergistic anticorrosion method was that the electrode was treated by the soluble glass, and that OP-10 was added into the electrolyte. The cyclic voltammogram (CV) results of the electrode show clearly that the anticorrosion agent can change the electrochemical activity and mechanism of the electrode. The concentration of the anticorrosion agent in the electrolyte treated by the synergistic anticorrosion method was also investigated. The appropriate concentration of the anticorrosion agents in the electrolyte is 0.143% .展开更多
基金Project supported by the National Natural Science Foundation of China (20363001) the Project in Specific Technological R & D Fund Program for Research Institutes from Ministry of Science and Technology of the PRC (2004EG113030)the Key Project in International Science and Technology Cooperation from Ministry of Science and Technology of the PRC (2005DFA50250)
文摘In this paper, any two of the three anticorrosion agents, that is emulsifier (OP-10), soluble glass (Na2O·nSiO2) and glycerin (C3H8O3), were treated simultaneously on the surface of amorphous (a- ) MgNi + 5% Ml2Mg17(MI denotes the lanthanum-rich mish metal) electrode and the electrolyte. Effect of the synergistic anticorrosion treatment on charging/discharging cycle stability of the electrode was investigated. Contrasted with single treatment method, the cycling stability of the electrodes was further improved. The desirable synergistic anticorrosion method was that the electrode was treated by the soluble glass, and that OP-10 was added into the electrolyte. The cyclic voltammogram (CV) results of the electrode show clearly that the anticorrosion agent can change the electrochemical activity and mechanism of the electrode. The concentration of the anticorrosion agent in the electrolyte treated by the synergistic anticorrosion method was also investigated. The appropriate concentration of the anticorrosion agents in the electrolyte is 0.143% .