Stress corrosion cracking(SCC)may lead to brittle,unexpected failure of medical devices.However,available researches are limited to Mg-based biodegradable metals(BM)and pure Zn.The stress corrosion behaviors of newly-...Stress corrosion cracking(SCC)may lead to brittle,unexpected failure of medical devices.However,available researches are limited to Mg-based biodegradable metals(BM)and pure Zn.The stress corrosion behaviors of newly-developed Zn alloys remain unclear.In the present work,we conducted slow strain rate testing(SSRT)and constant-load immersion test on a promising Zn-0.8 wt%Li alloy in order to investigate its SCC susceptibility and examine its feasibility as BM with pure Zn as control group.We observed that Zn-0.8 wt%Li alloy exhibited low SCC susceptibility.This was attributed to variations in microstructure and deformation mechanism after alloying with Li.In addition,both pure Zn and Zn-0.8 wt%Li alloy did not fracture over a period of 28 days during constant-load immersion test.The magnitude of applied stress was close to physiological condition and thus,we proved the feasibility of both materials as BM.展开更多
Ti-V-based alloys are proved of huge potential in storing hydrogen,but the incomplete reversible hydrogen storage capacity caused by overstability of V hydride has limited the large-scale application.In this study,Ti_...Ti-V-based alloys are proved of huge potential in storing hydrogen,but the incomplete reversible hydrogen storage capacity caused by overstability of V hydride has limited the large-scale application.In this study,Ti_(32)V_(40+x)Fe_(23-x)Mn_(5)(x=0,4,8,12,at.%)alloys were designed,and the effects of V/Fe ratio on phase constitution and hydrogen storage properties were investigated.The main phase of the alloys is body-centered cubic(BCC)phase,and the lattice constants of the BCC phase decrease with the decrease of V/Fe ratio.Moreover,C14 Laves phase exists in alloys with a Fe content of 19at.%to 23at.%.For hydrogenation,the C14 Laves phase can accelerate the hydrogen absorption rate,but the hydrogen absorption capacity is reduced.With the decrease of V/Fe ratio,the hydride gradually destabilizes.Owing to its large lattice constant and high hydrogen absorption phase content,the Ti_(32)V_(52)Fe_(11)Mn_(5)alloy shows the most enhanced hydrogen storage properties with hydrogenation and dehydrogenation capacities of 3.588wt.%at 298 K and 1.688wt.%at 343 K,respectively.The hydrogen absorption capacity of this alloy can be reserved to 3.574wt.%after 20 cycles of hydrogen absorption and desorption.展开更多
In order to check the traditional core loss formula, the core loss spectrum P(f) of Co-based amorphous soft magnetic alloy with constant permeability has been studied. It is found that within a high frequency range fr...In order to check the traditional core loss formula, the core loss spectrum P(f) of Co-based amorphous soft magnetic alloy with constant permeability has been studied. It is found that within a high frequency range from 10 kHz to 200 kHz and at Bm = 0. 1 T,the P(f) has the fractal structure P (f) = Po, and with the increasing of induced anisotropy energy Ku, the fractal dimension Dfrises, thus the total power loss at high frequency increases and the frequency characteristic of P(f) becomes worse.展开更多
基金supported by National Natural Science Foundation of China(Grant No.51931001).
文摘Stress corrosion cracking(SCC)may lead to brittle,unexpected failure of medical devices.However,available researches are limited to Mg-based biodegradable metals(BM)and pure Zn.The stress corrosion behaviors of newly-developed Zn alloys remain unclear.In the present work,we conducted slow strain rate testing(SSRT)and constant-load immersion test on a promising Zn-0.8 wt%Li alloy in order to investigate its SCC susceptibility and examine its feasibility as BM with pure Zn as control group.We observed that Zn-0.8 wt%Li alloy exhibited low SCC susceptibility.This was attributed to variations in microstructure and deformation mechanism after alloying with Li.In addition,both pure Zn and Zn-0.8 wt%Li alloy did not fracture over a period of 28 days during constant-load immersion test.The magnitude of applied stress was close to physiological condition and thus,we proved the feasibility of both materials as BM.
基金supported by the National Key Research and Development Program of China(2023YFB4005401)the National Natural Science Foundation of China(52425401,52204386)the Natural Science Foundation of Heilongjiang Province(JQ2023E003).
文摘Ti-V-based alloys are proved of huge potential in storing hydrogen,but the incomplete reversible hydrogen storage capacity caused by overstability of V hydride has limited the large-scale application.In this study,Ti_(32)V_(40+x)Fe_(23-x)Mn_(5)(x=0,4,8,12,at.%)alloys were designed,and the effects of V/Fe ratio on phase constitution and hydrogen storage properties were investigated.The main phase of the alloys is body-centered cubic(BCC)phase,and the lattice constants of the BCC phase decrease with the decrease of V/Fe ratio.Moreover,C14 Laves phase exists in alloys with a Fe content of 19at.%to 23at.%.For hydrogenation,the C14 Laves phase can accelerate the hydrogen absorption rate,but the hydrogen absorption capacity is reduced.With the decrease of V/Fe ratio,the hydride gradually destabilizes.Owing to its large lattice constant and high hydrogen absorption phase content,the Ti_(32)V_(52)Fe_(11)Mn_(5)alloy shows the most enhanced hydrogen storage properties with hydrogenation and dehydrogenation capacities of 3.588wt.%at 298 K and 1.688wt.%at 343 K,respectively.The hydrogen absorption capacity of this alloy can be reserved to 3.574wt.%after 20 cycles of hydrogen absorption and desorption.
文摘In order to check the traditional core loss formula, the core loss spectrum P(f) of Co-based amorphous soft magnetic alloy with constant permeability has been studied. It is found that within a high frequency range from 10 kHz to 200 kHz and at Bm = 0. 1 T,the P(f) has the fractal structure P (f) = Po, and with the increasing of induced anisotropy energy Ku, the fractal dimension Dfrises, thus the total power loss at high frequency increases and the frequency characteristic of P(f) becomes worse.