A hydrometallurgical process for refractory gold-bearing arsenosulfide concentrates at ambient temperature and pressure was presented, including fine grinding with intensified alkali-leaching （FGIAL）, enhanced agita...A hydrometallurgical process for refractory gold-bearing arsenosulfide concentrates at ambient temperature and pressure was presented, including fine grinding with intensified alkali-leaching （FGIAL）, enhanced agitation alkali-leaching （EAAL）, thiosulfate leaching and displacement. Experimental results on a refractory gold concentrate showed that the total consumption of NaOH in alkaline leaching is only 41% of those theoretically calculated under the conditions of full oxidization for the same amount of arse- nides and sulfides transformed into arsenates and sulfates, and 72.3% of gold is synchro-dissoluted by thiosulfate self-generated during alkaline leaching. After alkaline leaching, thiosulfate leaching was carried out for 24 h. The dissolution of gold is increased to 91.9% from 4.6% by cyanide without the pretreatment. The displacement of gold by zinc powder in the solution gets to 99.2%. Due to an amount of thiosulfate self-generated during alkaline leaching, the reagent addition in thiosulfate leaching afterwards is lower than the normal.展开更多
A new process for the hydrometallurgy of refractory gold concentrates was presented. The process comprises grinding leaching, intensified alkaline leaching (IAL), cyanidation and adsorption. In a stirring type pulveri...A new process for the hydrometallurgy of refractory gold concentrates was presented. The process comprises grinding leaching, intensified alkaline leaching (IAL), cyanidation and adsorption. In a stirring type pulverizing leaching tower mill, the concentrate is ground to <35.6 μm of 95.5 % while simultaneously leached by NaOH of 12 kg/t, then carried out intensified alkaline leaching for 48 h by NaOH of 108 kg/t in enhanced agitation tanks with the pulp concentration of 40% solids at the environmental temperature of 9.5 ～ 13.5 ℃ and the environmental pressure of 10 5 Pa. The oxidation rate of As is 94.9%, and 47.6% for S. The total consumption of NaOH is only 20% of that theoretically calculated under the conditions of full oxidation at the same oxidation rates of arsenic to arsenate and sulfur to sulfate. The gold leaching rate by NaCN in 24 h is increased from 9.2% before pretreatment to 94.2%. The consumption of NaCN is 7.5 kg/t, which is one times less than that before pretreatment. The extraction cost of gold is about 422 Yuan/t.展开更多
基金This project was financially supported by the Natural Science Foundation of Liaoning Province of China (No.2001101015) and theFree Study Item of the Institute of Metal Research, Chinese Academy of Sciences (No.AM05-0866)
文摘A hydrometallurgical process for refractory gold-bearing arsenosulfide concentrates at ambient temperature and pressure was presented, including fine grinding with intensified alkali-leaching （FGIAL）, enhanced agitation alkali-leaching （EAAL）, thiosulfate leaching and displacement. Experimental results on a refractory gold concentrate showed that the total consumption of NaOH in alkaline leaching is only 41% of those theoretically calculated under the conditions of full oxidization for the same amount of arse- nides and sulfides transformed into arsenates and sulfates, and 72.3% of gold is synchro-dissoluted by thiosulfate self-generated during alkaline leaching. After alkaline leaching, thiosulfate leaching was carried out for 24 h. The dissolution of gold is increased to 91.9% from 4.6% by cyanide without the pretreatment. The displacement of gold by zinc powder in the solution gets to 99.2%. Due to an amount of thiosulfate self-generated during alkaline leaching, the reagent addition in thiosulfate leaching afterwards is lower than the normal.
文摘A new process for the hydrometallurgy of refractory gold concentrates was presented. The process comprises grinding leaching, intensified alkaline leaching (IAL), cyanidation and adsorption. In a stirring type pulverizing leaching tower mill, the concentrate is ground to <35.6 μm of 95.5 % while simultaneously leached by NaOH of 12 kg/t, then carried out intensified alkaline leaching for 48 h by NaOH of 108 kg/t in enhanced agitation tanks with the pulp concentration of 40% solids at the environmental temperature of 9.5 ～ 13.5 ℃ and the environmental pressure of 10 5 Pa. The oxidation rate of As is 94.9%, and 47.6% for S. The total consumption of NaOH is only 20% of that theoretically calculated under the conditions of full oxidation at the same oxidation rates of arsenic to arsenate and sulfur to sulfate. The gold leaching rate by NaCN in 24 h is increased from 9.2% before pretreatment to 94.2%. The consumption of NaCN is 7.5 kg/t, which is one times less than that before pretreatment. The extraction cost of gold is about 422 Yuan/t.