Experiments were conducted to evaluate the potential for improving the mechanical properties of Mg-Al-Zn alloy at room temperature by subjecting to accumulative roll-bonding(ARB).It is shown that ARB may be applied su...Experiments were conducted to evaluate the potential for improving the mechanical properties of Mg-Al-Zn alloy at room temperature by subjecting to accumulative roll-bonding(ARB).It is shown that ARB may be applied successfully to Mg-Al-Zn alloy at elevated temperatures and it leads to grain refinement and significant improvements in the ductility.The strength of the as-rolled Mg-Al-Zn alloy sheet after ARB processing is slightly decreased and basal texture is weakened by ARB processing.展开更多
In the present study, an Al/Cu/Mg multi-layered composite was produced by accumulative roll bonding(ARB) through seven passes, and its microstructure and mechanical properties were evaluated. The microstructure invest...In the present study, an Al/Cu/Mg multi-layered composite was produced by accumulative roll bonding(ARB) through seven passes, and its microstructure and mechanical properties were evaluated. The microstructure investigations show that plastic instability occurred in both the copper and magnesium reinforcements in the primary sandwich. In addition, a composite with a perfectly uniform distribution of copper and magnesium reinforcing layers was produced during the last pass. By increasing the number of ARB cycles, the microhardness of the layers including aluminum, copper, and magnesium was significantly increased. The ultimate tensile strength of the sandwich was enhanced continually and reached a maximum value of 355.5 MPa. This strength value was about 3.2, 2, and 2.1 times higher than the initial strength values for the aluminum, copper, and magnesium sheets, respectively. Investigation of tensile fracture surfaces during the ARB process indicated that the fracture mechanism changed to shear ductile at the seventh pass.展开更多
Ti/Cu multilayered composites were fabricated via accumulative roll bonding(ARB). During codeformation of the constituent metals, the hard Ti layers necked preferentially and then fragmented with the development of sh...Ti/Cu multilayered composites were fabricated via accumulative roll bonding(ARB). During codeformation of the constituent metals, the hard Ti layers necked preferentially and then fragmented with the development of shear bands. Transmission electron microscopy showed that with increasing ARB cycles, grains in Ti were significantly refined even though dynamic recrystallization has occurred. For Cu the significant grain refinement was only found within the shear banded region when the composite was processed after five ARB cycles. Due to the diffusion of Cu atoms into Ti at the heterophase interfaces, amorphization with a width less than 10 nm was identified even in the composite processed by one cycle. At higher ARB cycles, the width of amorphous region increased and intermetallic compounds CuTi appeared from the region. The lattice defects introduced at the heterophase interfaces under roll bonding was responsible for the formation of the nano-scaled compounds. X-ray diffraction showed that an abnormal {1120} fiber texture was developed in Ti layers, while significant brass-type textures were developed in Cu layers. Some orientations along the {1120} fiber favored the prismatic < a> slip for Ti.Tensile tests revealed the elevated strength without a substantial sacrifice of ductility in the composites during ARB. The unique mechanical properties were attributed to the significantly refined grains in individual metals, the good bonding between the constituent metals, as well as the development of an abnormal {1120} fiber texture in Ti layers.展开更多
In this study, a multilayer Al/Ni/Cu composite reinforced with Si C particles was produced using an accumulative roll bonding(ARB) process with different cycles. The microstructure and mechanical properties of this co...In this study, a multilayer Al/Ni/Cu composite reinforced with Si C particles was produced using an accumulative roll bonding(ARB) process with different cycles. The microstructure and mechanical properties of this composite were investigated using optical and scanning microscopy and hardness and tensile testing. The results show that by increasing the applied strain, the Al/Ni/Cu multilayer composite converted from layer features to near a particle-strengthening characteristic. After the fifth ARB cycle, a composite with a uniform distribution of reinforcements(Cu, Ni, and SiC) was fabricated. The tensile strength of the composite increased from the initial sandwich structure to the first ARB cycle and then decreased from the first to the third ARB cycle. Upon reaching five ARB cycles, the tensile strength of the composite increased again. The variation in the elongation of the composite exhibited a tendency similar to that of its tensile strength. It is observed that with increasing strain, the microhardness values of the Al, Cu, and Ni layers increased, and that the dominant fracture mechanisms of Al and Cu were dimple formation and ductile fracture. In contrast, brittle fracture in specific plains was the main characteristic of Ni fractures.展开更多
基金Project(36547)supported by the Natural Science Foundation of Guangdong Province,ChinaProject(2007001)supported by PublicFoundation of Guangdong Key Laboratory for Advanced Metallic Materials Processing,South China University of Technology,China
文摘Experiments were conducted to evaluate the potential for improving the mechanical properties of Mg-Al-Zn alloy at room temperature by subjecting to accumulative roll-bonding(ARB).It is shown that ARB may be applied successfully to Mg-Al-Zn alloy at elevated temperatures and it leads to grain refinement and significant improvements in the ductility.The strength of the as-rolled Mg-Al-Zn alloy sheet after ARB processing is slightly decreased and basal texture is weakened by ARB processing.
文摘In the present study, an Al/Cu/Mg multi-layered composite was produced by accumulative roll bonding(ARB) through seven passes, and its microstructure and mechanical properties were evaluated. The microstructure investigations show that plastic instability occurred in both the copper and magnesium reinforcements in the primary sandwich. In addition, a composite with a perfectly uniform distribution of copper and magnesium reinforcing layers was produced during the last pass. By increasing the number of ARB cycles, the microhardness of the layers including aluminum, copper, and magnesium was significantly increased. The ultimate tensile strength of the sandwich was enhanced continually and reached a maximum value of 355.5 MPa. This strength value was about 3.2, 2, and 2.1 times higher than the initial strength values for the aluminum, copper, and magnesium sheets, respectively. Investigation of tensile fracture surfaces during the ARB process indicated that the fracture mechanism changed to shear ductile at the seventh pass.
基金financially supported by the National Natural Science Foundation of China(No.51571057)the Fundamental Research Funds for the Central Universities(No.N170204012)
文摘Ti/Cu multilayered composites were fabricated via accumulative roll bonding(ARB). During codeformation of the constituent metals, the hard Ti layers necked preferentially and then fragmented with the development of shear bands. Transmission electron microscopy showed that with increasing ARB cycles, grains in Ti were significantly refined even though dynamic recrystallization has occurred. For Cu the significant grain refinement was only found within the shear banded region when the composite was processed after five ARB cycles. Due to the diffusion of Cu atoms into Ti at the heterophase interfaces, amorphization with a width less than 10 nm was identified even in the composite processed by one cycle. At higher ARB cycles, the width of amorphous region increased and intermetallic compounds CuTi appeared from the region. The lattice defects introduced at the heterophase interfaces under roll bonding was responsible for the formation of the nano-scaled compounds. X-ray diffraction showed that an abnormal {1120} fiber texture was developed in Ti layers, while significant brass-type textures were developed in Cu layers. Some orientations along the {1120} fiber favored the prismatic < a> slip for Ti.Tensile tests revealed the elevated strength without a substantial sacrifice of ductility in the composites during ARB. The unique mechanical properties were attributed to the significantly refined grains in individual metals, the good bonding between the constituent metals, as well as the development of an abnormal {1120} fiber texture in Ti layers.
文摘In this study, a multilayer Al/Ni/Cu composite reinforced with Si C particles was produced using an accumulative roll bonding(ARB) process with different cycles. The microstructure and mechanical properties of this composite were investigated using optical and scanning microscopy and hardness and tensile testing. The results show that by increasing the applied strain, the Al/Ni/Cu multilayer composite converted from layer features to near a particle-strengthening characteristic. After the fifth ARB cycle, a composite with a uniform distribution of reinforcements(Cu, Ni, and SiC) was fabricated. The tensile strength of the composite increased from the initial sandwich structure to the first ARB cycle and then decreased from the first to the third ARB cycle. Upon reaching five ARB cycles, the tensile strength of the composite increased again. The variation in the elongation of the composite exhibited a tendency similar to that of its tensile strength. It is observed that with increasing strain, the microhardness values of the Al, Cu, and Ni layers increased, and that the dominant fracture mechanisms of Al and Cu were dimple formation and ductile fracture. In contrast, brittle fracture in specific plains was the main characteristic of Ni fractures.