Ni-based alloy coating on 21-4-N heat-resistant steel was prepared using CO2 laser, and the high-temperature abrasion wear was tested. The microstructure of this cladding layer and its abrasion wear behavior at high t...Ni-based alloy coating on 21-4-N heat-resistant steel was prepared using CO2 laser, and the high-temperature abrasion wear was tested. The microstructure of this cladding layer and its abrasion wear behavior at high temperature by changing compositions and temperatures were investigated by means of optical microscope and scanning electron microscope. Among the three compositions of cladding layer, i.e. Ni21+20%WC+0.5%CeO2, Ni25+20%WC+0.5%CeO2 and Ni60+20%WC+0.5%CeO2, the experimental results show that Ni21+20%WC+ 0.5%CeO2 cladding layer is made up of finer grains, and presents the best abrasion wear behavior at high temperature. The wear pattern of laser cladding layer is mainly grain abrasion at lower temperature, and it would be changed to adhesive abrasion and oxide abrasion at higher temperature.展开更多
Investigated the effect of an addition of CaF2 on the crystallization of a glass-ceramic with abrasion resistance. X-ray diffraction, differential thermal analysis and scanning electron microscopy were used to determi...Investigated the effect of an addition of CaF2 on the crystallization of a glass-ceramic with abrasion resistance. X-ray diffraction, differential thermal analysis and scanning electron microscopy were used to determine the effect. The results showed that a suitable addition of CaF2 promoted crystallization by forming an interme- diate crystalline phase. CaF2 can decrease the temperature and active energy of the base-glass for crystallization. When 4 mass-% of CaF2-fraction is added in the glass, the crystallization temperature and active energy is 936 ℃and 172.75 kJ/mol respectively. When CaF2 is increased to 6 mass-%, the temperature and active energy decrease to 890 ℃ and 88.81 kJ/mol. CaF2 is an efficient nucleating agent for the glass-ceramics with abrasion resistant, the optimal content of CaF2 is about 6 mass-%.展开更多
文摘Ni-based alloy coating on 21-4-N heat-resistant steel was prepared using CO2 laser, and the high-temperature abrasion wear was tested. The microstructure of this cladding layer and its abrasion wear behavior at high temperature by changing compositions and temperatures were investigated by means of optical microscope and scanning electron microscope. Among the three compositions of cladding layer, i.e. Ni21+20%WC+0.5%CeO2, Ni25+20%WC+0.5%CeO2 and Ni60+20%WC+0.5%CeO2, the experimental results show that Ni21+20%WC+ 0.5%CeO2 cladding layer is made up of finer grains, and presents the best abrasion wear behavior at high temperature. The wear pattern of laser cladding layer is mainly grain abrasion at lower temperature, and it would be changed to adhesive abrasion and oxide abrasion at higher temperature.
基金Supported by National Natural Science Foundation of China and Shanghai Baosteel Group Corporation(50174024)
文摘Investigated the effect of an addition of CaF2 on the crystallization of a glass-ceramic with abrasion resistance. X-ray diffraction, differential thermal analysis and scanning electron microscopy were used to determine the effect. The results showed that a suitable addition of CaF2 promoted crystallization by forming an interme- diate crystalline phase. CaF2 can decrease the temperature and active energy of the base-glass for crystallization. When 4 mass-% of CaF2-fraction is added in the glass, the crystallization temperature and active energy is 936 ℃and 172.75 kJ/mol respectively. When CaF2 is increased to 6 mass-%, the temperature and active energy decrease to 890 ℃ and 88.81 kJ/mol. CaF2 is an efficient nucleating agent for the glass-ceramics with abrasion resistant, the optimal content of CaF2 is about 6 mass-%.