Y2O3-doped ZnO-based varistor ceramics were prepared using high-energy ball milling （HEBM） and low-temperature sin- tering technique, with voltage-gradient of 1934-2197 V/mm, non-linear coefficients of 20.8-21.8, le...Y2O3-doped ZnO-based varistor ceramics were prepared using high-energy ball milling （HEBM） and low-temperature sin- tering technique, with voltage-gradient of 1934-2197 V/mm, non-linear coefficients of 20.8-21.8, leakage currents of 0.59-1.04 μA, and densities of 5.46-5.57 g/cm3. With increasing Y2O3 content, the voltage-gradient increases because of the decrease of ZnO grain size; the non-linear coefficient and the leakage current improve but the density decreases because of more porosity; the donor con- centration and density of interface states decrease, whereas the barrier height and width increase because of the acceptor effect of Y2O3 in varistor ceramics.展开更多
以硝酸钇为原料,尿素为沉淀剂,低分子量聚丙烯酸钠为分散剂,研究了采用均匀沉淀法合成纳米Y2O3的工艺过程。制备条件为:钇离子浓度0.3m o l/L;尿素与硝酸钇的摩尔比为4∶1;分散剂聚丙烯酸钠的用量为1%(体积分数);反应时间4h,反应温度95...以硝酸钇为原料,尿素为沉淀剂,低分子量聚丙烯酸钠为分散剂,研究了采用均匀沉淀法合成纳米Y2O3的工艺过程。制备条件为:钇离子浓度0.3m o l/L;尿素与硝酸钇的摩尔比为4∶1;分散剂聚丙烯酸钠的用量为1%(体积分数);反应时间4h,反应温度95℃;煅烧温度为850℃,煅烧时间3 h。制备得到粒径为32nm、无团聚、粒径均匀的纳米Y2O3。展开更多
文摘Y2O3-doped ZnO-based varistor ceramics were prepared using high-energy ball milling （HEBM） and low-temperature sin- tering technique, with voltage-gradient of 1934-2197 V/mm, non-linear coefficients of 20.8-21.8, leakage currents of 0.59-1.04 μA, and densities of 5.46-5.57 g/cm3. With increasing Y2O3 content, the voltage-gradient increases because of the decrease of ZnO grain size; the non-linear coefficient and the leakage current improve but the density decreases because of more porosity; the donor con- centration and density of interface states decrease, whereas the barrier height and width increase because of the acceptor effect of Y2O3 in varistor ceramics.
文摘以硝酸钇为原料,尿素为沉淀剂,低分子量聚丙烯酸钠为分散剂,研究了采用均匀沉淀法合成纳米Y2O3的工艺过程。制备条件为:钇离子浓度0.3m o l/L;尿素与硝酸钇的摩尔比为4∶1;分散剂聚丙烯酸钠的用量为1%(体积分数);反应时间4h,反应温度95℃;煅烧温度为850℃,煅烧时间3 h。制备得到粒径为32nm、无团聚、粒径均匀的纳米Y2O3。