A new kind of doped rare earth free phosphor Y 2O 2S∶xTi (0<x≤0.10) with doped Ti as activative center was synthesized by solid state reaction and sintered at 1200 ℃ for 2.5 h under reducing atmosphere. XRD pa...A new kind of doped rare earth free phosphor Y 2O 2S∶xTi (0<x≤0.10) with doped Ti as activative center was synthesized by solid state reaction and sintered at 1200 ℃ for 2.5 h under reducing atmosphere. XRD patterns, photoluminescence spectra, time-resolved phosphorescence spectra and decay curves of the phosphor were investigated. XRD results reveal that a single Y 2O 2S phase exists with Ti content up to 6% (mol fraction). Yellow long lasting phosphorescence for present materials was observed in the dark with naked eye after the removal of the excitation light. From the time-resolved phosphorescence spectra the broad emission band centered at 565 nm was confirmed to be responsible for the long lasting phosphorescence which could maintain above 1 h. The possible mechanism responsible for the long lasting phosphorescence of the Y 2O 2S∶Ti phosphor was proposed.展开更多
A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method. The effects of rare earth oxide (La2O3, CeO2, Nd2O3, Sm2O3, Eu2O3, Gd2O3 and Dy2O3) and Nd2O3 doping content on th...A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method. The effects of rare earth oxide (La2O3, CeO2, Nd2O3, Sm2O3, Eu2O3, Gd2O3 and Dy2O3) and Nd2O3 doping content on the microstructure and dielectric properties of Y2Ti2O7 ceramics were investigated. The experimental results showed that the rare earth ions were considered to dissolve in Y-sites of the pyrochlore structure, different rare earth oxides and concentration had different influences on Y2Ti2O7 cerami...展开更多
A comparative study of cascades in nanostructured ferritic alloys and pure Fe is performed to reveal the influence of Y_2Ti_2O_7 nanocluster on cascades by molecular dynamics simulations. The cascades with energies of...A comparative study of cascades in nanostructured ferritic alloys and pure Fe is performed to reveal the influence of Y_2Ti_2O_7 nanocluster on cascades by molecular dynamics simulations. The cascades with energies of primary knock-on atom（PKA） ranging from 0.5 keV to 4.0 keV and PKA＇s distances to the interface from 0 to 50 are simulated. It turns out that the Y_2Ti_2O_7 nanocluster can absorb the kinetic energy of cascade atoms, prevent the cascade from extending and reduce the defect production significantly when the cascades overlap with the nanocluster. When the cascade affects seriously the nanocluster, the weak sub-cascade collisions are rebounded by the nanocluster and thus leave more interstitials in the matrix. On the contrary, when the cascade contacts weakly the nanocluster, the interface can pin the arrived interstitials and this leaves more vacancies in the matrix. Moreover, the results indicate that the Y_2Ti_2O_7 nanocluster keeps stable upon the displacement cascade damage.展开更多
The present work aimed to explore a kind of microwave dielectric materials with middle-permittivity, high Qf, near-zero τf, and lower sintering temperature. A series of Y2Ti2O7 microwave dielectric ceramics were synt...The present work aimed to explore a kind of microwave dielectric materials with middle-permittivity, high Qf, near-zero τf, and lower sintering temperature. A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method. For improving the dielectric properties of Y2Ti2O7 system, Bi2O3, Nd2O3 and Nb2O5 were added and their effects on phase composition, micro-structure, and dielectric properties at microwave frequencies were investigated by means of X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The queuing score method for multi-target orthogonal design was used to obtain the optimum prescription. The results showed that the Y2Ti2O7 ceramics with 8 wt.% Bi2O3 and 1 mol.% Nd2O3-Nb2O5 were well sintered at 1350 ℃, exhibiting excellent dielectric characteristics, i.e. εr≈76, Qf≈18980 GHz, τf =＋25.5 ppm/℃.展开更多
文摘A new kind of doped rare earth free phosphor Y 2O 2S∶xTi (0<x≤0.10) with doped Ti as activative center was synthesized by solid state reaction and sintered at 1200 ℃ for 2.5 h under reducing atmosphere. XRD patterns, photoluminescence spectra, time-resolved phosphorescence spectra and decay curves of the phosphor were investigated. XRD results reveal that a single Y 2O 2S phase exists with Ti content up to 6% (mol fraction). Yellow long lasting phosphorescence for present materials was observed in the dark with naked eye after the removal of the excitation light. From the time-resolved phosphorescence spectra the broad emission band centered at 565 nm was confirmed to be responsible for the long lasting phosphorescence which could maintain above 1 h. The possible mechanism responsible for the long lasting phosphorescence of the Y 2O 2S∶Ti phosphor was proposed.
基金Project supported by the Key University Science Research Project of Jiangsu Province (08KJA430002)
文摘A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method. The effects of rare earth oxide (La2O3, CeO2, Nd2O3, Sm2O3, Eu2O3, Gd2O3 and Dy2O3) and Nd2O3 doping content on the microstructure and dielectric properties of Y2Ti2O7 ceramics were investigated. The experimental results showed that the rare earth ions were considered to dissolve in Y-sites of the pyrochlore structure, different rare earth oxides and concentration had different influences on Y2Ti2O7 cerami...
基金Project supported by the Science Challenge Project of China(Grant No.TZ2016002)the National Natural Science Foundation of China(Grant No.50871057)
文摘A comparative study of cascades in nanostructured ferritic alloys and pure Fe is performed to reveal the influence of Y_2Ti_2O_7 nanocluster on cascades by molecular dynamics simulations. The cascades with energies of primary knock-on atom（PKA） ranging from 0.5 keV to 4.0 keV and PKA＇s distances to the interface from 0 to 50 are simulated. It turns out that the Y_2Ti_2O_7 nanocluster can absorb the kinetic energy of cascade atoms, prevent the cascade from extending and reduce the defect production significantly when the cascades overlap with the nanocluster. When the cascade affects seriously the nanocluster, the weak sub-cascade collisions are rebounded by the nanocluster and thus leave more interstitials in the matrix. On the contrary, when the cascade contacts weakly the nanocluster, the interface can pin the arrived interstitials and this leaves more vacancies in the matrix. Moreover, the results indicate that the Y_2Ti_2O_7 nanocluster keeps stable upon the displacement cascade damage.
基金supported by the Key University Science Research of Jiangsu Province (08KJA430002)the Priority Academic Program D velopment of Jiangsu Higher Education Institute
文摘The present work aimed to explore a kind of microwave dielectric materials with middle-permittivity, high Qf, near-zero τf, and lower sintering temperature. A series of Y2Ti2O7 microwave dielectric ceramics were synthesized by conventional solid-state method. For improving the dielectric properties of Y2Ti2O7 system, Bi2O3, Nd2O3 and Nb2O5 were added and their effects on phase composition, micro-structure, and dielectric properties at microwave frequencies were investigated by means of X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The queuing score method for multi-target orthogonal design was used to obtain the optimum prescription. The results showed that the Y2Ti2O7 ceramics with 8 wt.% Bi2O3 and 1 mol.% Nd2O3-Nb2O5 were well sintered at 1350 ℃, exhibiting excellent dielectric characteristics, i.e. εr≈76, Qf≈18980 GHz, τf =＋25.5 ppm/℃.