The V/O5-WO3-MoOy＇TiO2 honeycomb catalyst was prepared with industrial grade chemicals. The structural and physico-chemical properties were analyzed with X-ray diffraction （XRD）, scanning electron micrograph （SEM...The V/O5-WO3-MoOy＇TiO2 honeycomb catalyst was prepared with industrial grade chemicals. The structural and physico-chemical properties were analyzed with X-ray diffraction （XRD）, scanning electron micrograph （SEM） and mercury porosimetry. The NOx conversion and durability were investigated on a pilot plant test set under the actual operational conditions of a coal fired boiler. The catalyst monolith had good formability with mass per- centage of V ： W ： Mo ： TiO2 ： fiber glass = 1 ： 4.5 ： 4.5 ： 72 ： 18. Vanadium, tungsten and molybdenum species were highly dispersed on anatase TiO2 without causing the transformation of anatase TiO2 to ruffle by calcining under a current of air at 450℃ for 4.5 h, but there were some degrees of crystal distortion. The catalyst particle sizes were almost uniform with close pile-up and the pore structure was regular with complete macro-pore formation and large specific surface area. The NOx conversion was sensitive to temperature but nearly insensitive to NH3. The catalyst showed strong adaptability to NOx concentration with activity above 80% in the range of 615 1640 mg.m-3. Within the range of 720-8640 h continuous operation, the NOx conversion dropped at a rate of about 1% reduction per 600 h.展开更多
基金Supported by the Science and Technology Development Planning of Shandong Province(2011GSF11716)China Scholarship Council for Researching in University of Birmingham
文摘The V/O5-WO3-MoOy＇TiO2 honeycomb catalyst was prepared with industrial grade chemicals. The structural and physico-chemical properties were analyzed with X-ray diffraction （XRD）, scanning electron micrograph （SEM） and mercury porosimetry. The NOx conversion and durability were investigated on a pilot plant test set under the actual operational conditions of a coal fired boiler. The catalyst monolith had good formability with mass per- centage of V ： W ： Mo ： TiO2 ： fiber glass = 1 ： 4.5 ： 4.5 ： 72 ： 18. Vanadium, tungsten and molybdenum species were highly dispersed on anatase TiO2 without causing the transformation of anatase TiO2 to ruffle by calcining under a current of air at 450℃ for 4.5 h, but there were some degrees of crystal distortion. The catalyst particle sizes were almost uniform with close pile-up and the pore structure was regular with complete macro-pore formation and large specific surface area. The NOx conversion was sensitive to temperature but nearly insensitive to NH3. The catalyst showed strong adaptability to NOx concentration with activity above 80% in the range of 615 1640 mg.m-3. Within the range of 720-8640 h continuous operation, the NOx conversion dropped at a rate of about 1% reduction per 600 h.
基金The Shanghai Committee of Scientific and Technical (0852nm01300, 07JC14052, 07DZ22302)National Natural Science Foundation of China (50752001)Shanghai Committee of Construction and Transportation
文摘采用溶胶凝胶技术分别制备了 WO3 和 MoO3溶胶,PdCl2作为催化剂被掺入 WO3-MoO3复合溶胶中,然后采用提拉浸渍镀膜法成功制备了 WO3-MoO3复合薄膜。采用原子力显微镜和 X 射线衍射仪分别研究了薄膜的表面形貌和薄膜的晶态结构。采用紫外可见分光光度计原位测试了 WO3-MoO3复合薄膜的气致变色性能。研究表明,该法制备的非晶体的 WO3-MoO3复合薄膜也具有很好的气致变色性能。