Electro-spark deposition（ESD） was adopted for preparing high property coatings by depositing WC-8Co cemented carbide on an spheroidal graphite roll substrate.The microstructure and properties of the coating were inv...Electro-spark deposition（ESD） was adopted for preparing high property coatings by depositing WC-8Co cemented carbide on an spheroidal graphite roll substrate.The microstructure and properties of the coating were investigated by X-ray diffraction（XRD）, scanning electron microscopy（SEM） with energy dispersive X-ray（EDX） and ball-disc configuration wear tester.The results show that nanosized particles and amorphous structures prevail in the coating which is metallurgically bonded to the substrate.The microstructures of the transition zone include columnar structure and equiaxed structure.The primary phases of the coating contain W2C, W6C2.54, Fe3W3C, and Co3W3C.The results of abrasive test show that the coating has low friction coefficients（μaverage = 0.18） and the wear mechanisms are mainly abrasive wear, fatigue wear, and oxidation wear.The maximum microhardness value of the coating is about 17410 N/mm2.The study reveals that the electro-spark deposition process has better coating quality and the coating has high wear resistance and hardness.展开更多
To prepare high wear resistance and high hardness coatings, electro-spark deposition was adopted for depositing an electrode of a mixture of 92wt%WC＋8wt%Co on a cast steel roll substrate. The coating was characterize...To prepare high wear resistance and high hardness coatings, electro-spark deposition was adopted for depositing an electrode of a mixture of 92wt%WC＋8wt%Co on a cast steel roll substrate. The coating was characterized by classical X-ray diffractometer （XRD） and scanning electron microscopy （SEM） with energy dispersive X-ray analysis （EDX）. The results indicate that the coating shows nanosized particulate structure and dendritic structure including columnar structure and equiaxed structure. The primary phases of the coating contain Fe3W3C, Co3W3C, Fe2C and Si2W. The coating has a low friction coefficient of 0.13, its average wear-resistance is 3.3 times that of the cast steel roll substrate and the main mechanism is abrasive wear. The maximum microhardness value of the coating is about 1573.9 Hv0.3. The study reveals that the electro-spark deposition process has the characteristic of better coating quality and the coating has higher wear resistance and hardness.展开更多
基金supported by the International Science and Technology Cooperation Project of the Ministry of Science and Technology of China (No. 2006DFA52240)
文摘Electro-spark deposition（ESD） was adopted for preparing high property coatings by depositing WC-8Co cemented carbide on an spheroidal graphite roll substrate.The microstructure and properties of the coating were investigated by X-ray diffraction（XRD）, scanning electron microscopy（SEM） with energy dispersive X-ray（EDX） and ball-disc configuration wear tester.The results show that nanosized particles and amorphous structures prevail in the coating which is metallurgically bonded to the substrate.The microstructures of the transition zone include columnar structure and equiaxed structure.The primary phases of the coating contain W2C, W6C2.54, Fe3W3C, and Co3W3C.The results of abrasive test show that the coating has low friction coefficients（μaverage = 0.18） and the wear mechanisms are mainly abrasive wear, fatigue wear, and oxidation wear.The maximum microhardness value of the coating is about 17410 N/mm2.The study reveals that the electro-spark deposition process has better coating quality and the coating has high wear resistance and hardness.
基金supported by the International Science and Technology Cooperation Project of the Ministry of Science and Technology of China (No.2006DFA52240)
文摘To prepare high wear resistance and high hardness coatings, electro-spark deposition was adopted for depositing an electrode of a mixture of 92wt%WC＋8wt%Co on a cast steel roll substrate. The coating was characterized by classical X-ray diffractometer （XRD） and scanning electron microscopy （SEM） with energy dispersive X-ray analysis （EDX）. The results indicate that the coating shows nanosized particulate structure and dendritic structure including columnar structure and equiaxed structure. The primary phases of the coating contain Fe3W3C, Co3W3C, Fe2C and Si2W. The coating has a low friction coefficient of 0.13, its average wear-resistance is 3.3 times that of the cast steel roll substrate and the main mechanism is abrasive wear. The maximum microhardness value of the coating is about 1573.9 Hv0.3. The study reveals that the electro-spark deposition process has the characteristic of better coating quality and the coating has higher wear resistance and hardness.