The effect of synergistic action of ultrasonic vibration and solidification pressure on tensile properties of vacuum counter-pressure casting ZL114 A alloys was studied systemically through testing and analyzing the t...The effect of synergistic action of ultrasonic vibration and solidification pressure on tensile properties of vacuum counter-pressure casting ZL114 A alloys was studied systemically through testing and analyzing the tensile strength and elongation subjected to different ultrasonic powers and solidification pressures. The results indicate that the synergistic action of ultrasonic vibration and solidification pressure can result in the refinement of grains and improvement of tensile properties. Both the highest tensile strength and elongation of aluminum alloy were obtained under synergistic action of 600 W ultrasonic power and 350 kPa solidification pressure. Moreover, the tensile fracture morphology shows obvious ductile fracture characteristics. When the solidification pressure is lower than 300 kPa, the effect of ultrasonic power on tensile strength and elongation is more obvious, but when the solidification pressure is higher than 300 kPa, the effect of solidification pressure on tensile strength and elongation is greater. Meanwhile, the size and morphology of the eutectic silicon were improved significantly by the ultrasonic vibration and pressurized solidification. The strip and massive eutectic silicon phase are completely converted into small short rod-like and evenly distributed Si phases at the grain boundary of primary α-Al.展开更多
In a Rapid Cycling Synchrotron （RCS）, power loss due to an eddy current on the metal vacuum chamber would cause heating of the vacuum chamber. It is important to study the effect for estimating eddy current induced ...In a Rapid Cycling Synchrotron （RCS）, power loss due to an eddy current on the metal vacuum chamber would cause heating of the vacuum chamber. It is important to study the effect for estimating eddy current induced power loss and temperature growth. Analytical formulas for eddy current power loss for various types of vacuum chambers are derived for dipole and quadrupole repeetively. By using the prototype of dipole of CSNS/RCS, an experiment was done to test the analytical formula. The derived formulas were applied to calculating the eddy current power loss on some special structures of an RCS vacuum chamber.展开更多
文摘为揭示真空电弧的微观动态形成机理及其影响因素,利用气体动力学模型研究真空断路器触头间的电弧形成过程。采用的数学模型包括电子和正负离子漂移扩散方程、微观粒子的碰撞方程及电场的泊松方程。建立触头间距为10 mm,触头间电压分别为工频交流12 k V和400 V的真空断路器简化模型,通过仿真得到工频真空电弧形成过程和鞘层形成过程的电子密度、平均电子能量及碰撞能量损失分布等各项微观参数的时变规律,并计算电子迁移率、金属蒸气压力和初始电子密度对真空电弧形成过程的影响。仿真结果表明:粒子运动速度差异形成的鞘层是电弧形成的基础;高电压、强电场作用促使电子能量产生轴向集中;电子迁移率及金属蒸气压力影响电弧形成过程;而初始电子密度对真空电弧弧前导电通道形成过程的影响可忽略。
基金financially supported by the National Natural Science Foundation of China(No.51261025)the Aerospace Science and Technology Innovation Foundation of Shanghai,China(No.SAST2016046)the Key Projects of Superior Science and Technology Innovation Team of Jiangxi,China(No.20181BCB19001)
文摘The effect of synergistic action of ultrasonic vibration and solidification pressure on tensile properties of vacuum counter-pressure casting ZL114 A alloys was studied systemically through testing and analyzing the tensile strength and elongation subjected to different ultrasonic powers and solidification pressures. The results indicate that the synergistic action of ultrasonic vibration and solidification pressure can result in the refinement of grains and improvement of tensile properties. Both the highest tensile strength and elongation of aluminum alloy were obtained under synergistic action of 600 W ultrasonic power and 350 kPa solidification pressure. Moreover, the tensile fracture morphology shows obvious ductile fracture characteristics. When the solidification pressure is lower than 300 kPa, the effect of ultrasonic power on tensile strength and elongation is more obvious, but when the solidification pressure is higher than 300 kPa, the effect of solidification pressure on tensile strength and elongation is greater. Meanwhile, the size and morphology of the eutectic silicon were improved significantly by the ultrasonic vibration and pressurized solidification. The strip and massive eutectic silicon phase are completely converted into small short rod-like and evenly distributed Si phases at the grain boundary of primary α-Al.
文摘In a Rapid Cycling Synchrotron （RCS）, power loss due to an eddy current on the metal vacuum chamber would cause heating of the vacuum chamber. It is important to study the effect for estimating eddy current induced power loss and temperature growth. Analytical formulas for eddy current power loss for various types of vacuum chambers are derived for dipole and quadrupole repeetively. By using the prototype of dipole of CSNS/RCS, an experiment was done to test the analytical formula. The derived formulas were applied to calculating the eddy current power loss on some special structures of an RCS vacuum chamber.