Effect of Mo and Mo2 C on the microstructure and properties of Ti（C,N）-based cermets was investigated in this article. The results have indicated that the weight percentage of Mo from 5 to 10 can reduce Ti（C,N） gr...Effect of Mo and Mo2 C on the microstructure and properties of Ti（C,N）-based cermets was investigated in this article. The results have indicated that the weight percentage of Mo from 5 to 10 can reduce Ti（C,N） grain diameter and thickness of the rim, and Ti（C,N） grain can be wetted by Ni-Cu-Mo liquid so as to get small contiguity of Ti（C,N） grain. In that way, the transverse rupture strength of Ti（C,N）-based cermets has reached 1800-1900 MPa; the fracture toughness has been due to 16-18 MPa.m1/2. But 15 wt pct Mo was not more effective on Ti（C,N）-based cermets, because the thickness of the rim becomes larger. In the circumstance of Mo2 C, 5 wt pct Mo2 C was good for microstructure and properties of Ti（C,N）-based cermets, but 11 wt pct Mo2C has resulted in larger contiguity of Ti（C,N） grain and big Ti（C,N） grain diameter so as to reduce transverse rupture strength and fracture toughness. So that, the effect of Mo on Ti（C,N）-based cermets is better than Mo2C.展开更多
This paper deals with the effects of codoped VC/Cr3C2 and sintering temperature on the magnetic and mechanical properties of ultra-fine grained WC-12%Co alloys. Results show that the synergistic action of doped VC/Cr3...This paper deals with the effects of codoped VC/Cr3C2 and sintering temperature on the magnetic and mechanical properties of ultra-fine grained WC-12%Co alloys. Results show that the synergistic action of doped VC/Cr3C2 in optimal proportion enhances both the hardness and transverse rupture strength （TRS） of the alloys, with more homogeneous microstructtLre. When the alloy is sintered at 1430℃ and with 0.5% Cr3C2/0.2% VC, the TRS reaches 3786 MPa, the hardness is 91.7 HRA and the grain size smaller than 0.6 μm. The numerical analyses on grain growth during the sintering process show that both VC precipitating on the WC grain boundary and Cr3C2 dissolving in the Co phase decrease the solid/liquid interfacial energy γ, the process of dissolution and reprecipitation is greatly retarded and the coarsening of WC grains is inhibited.展开更多
基金This work was supported by the National Natural Science Foundation of China （No.50074017/EO408)
文摘Effect of Mo and Mo2 C on the microstructure and properties of Ti（C,N）-based cermets was investigated in this article. The results have indicated that the weight percentage of Mo from 5 to 10 can reduce Ti（C,N） grain diameter and thickness of the rim, and Ti（C,N） grain can be wetted by Ni-Cu-Mo liquid so as to get small contiguity of Ti（C,N） grain. In that way, the transverse rupture strength of Ti（C,N）-based cermets has reached 1800-1900 MPa; the fracture toughness has been due to 16-18 MPa.m1/2. But 15 wt pct Mo was not more effective on Ti（C,N）-based cermets, because the thickness of the rim becomes larger. In the circumstance of Mo2 C, 5 wt pct Mo2 C was good for microstructure and properties of Ti（C,N）-based cermets, but 11 wt pct Mo2C has resulted in larger contiguity of Ti（C,N） grain and big Ti（C,N） grain diameter so as to reduce transverse rupture strength and fracture toughness. So that, the effect of Mo on Ti（C,N）-based cermets is better than Mo2C.
基金the National Natural Science Foundation of China (No. 50372043).
文摘This paper deals with the effects of codoped VC/Cr3C2 and sintering temperature on the magnetic and mechanical properties of ultra-fine grained WC-12%Co alloys. Results show that the synergistic action of doped VC/Cr3C2 in optimal proportion enhances both the hardness and transverse rupture strength （TRS） of the alloys, with more homogeneous microstructtLre. When the alloy is sintered at 1430℃ and with 0.5% Cr3C2/0.2% VC, the TRS reaches 3786 MPa, the hardness is 91.7 HRA and the grain size smaller than 0.6 μm. The numerical analyses on grain growth during the sintering process show that both VC precipitating on the WC grain boundary and Cr3C2 dissolving in the Co phase decrease the solid/liquid interfacial energy γ, the process of dissolution and reprecipitation is greatly retarded and the coarsening of WC grains is inhibited.