A high-entropy silicide(HES),(Ti_(0.2) Zr_(0.2) Nb_(0.2) Mo_(0.2) W_(0.2))Si_2 with close-packed hexagonal structure is successfully manufactured through reactive spark plasma sintering at 1300 ℃ for 15 min.The eleme...A high-entropy silicide(HES),(Ti_(0.2) Zr_(0.2) Nb_(0.2) Mo_(0.2) W_(0.2))Si_2 with close-packed hexagonal structure is successfully manufactured through reactive spark plasma sintering at 1300 ℃ for 15 min.The elements in this HES are uniformly distributed in the specimen based on the energy dispersive spectrometer analysis except a small amount of zirconium that is combined with oxygen as impurity particles. The Young's modulus, Poisson's ratio,and Vickers hardness of the obtained(Ti_(0.2) Zr_(0.2) Nb_(0.2) Mo_(0.2) W_(0.2))Si_2 are also measured.展开更多
基金Financial support from the National Natural Science Foundation of China (Nos. 51532009 and 51872045)the Science and Technology Commission of Shanghai Municipality (No. 18ZR1401400) are gratefully acknowledged
文摘A high-entropy silicide(HES),(Ti_(0.2) Zr_(0.2) Nb_(0.2) Mo_(0.2) W_(0.2))Si_2 with close-packed hexagonal structure is successfully manufactured through reactive spark plasma sintering at 1300 ℃ for 15 min.The elements in this HES are uniformly distributed in the specimen based on the energy dispersive spectrometer analysis except a small amount of zirconium that is combined with oxygen as impurity particles. The Young's modulus, Poisson's ratio,and Vickers hardness of the obtained(Ti_(0.2) Zr_(0.2) Nb_(0.2) Mo_(0.2) W_(0.2))Si_2 are also measured.