Four ZSM-5 zeolite catalysts with different Si/Al ratios for the catalytic cracking of C4 fractions to produce ethylene and propylene were prepared in this study.First,the adsorption isotherms of pure n-butane and but...Four ZSM-5 zeolite catalysts with different Si/Al ratios for the catalytic cracking of C4 fractions to produce ethylene and propylene were prepared in this study.First,the adsorption isotherms of pure n-butane and butene-1 and their mixtures on these catalysts at 300K and p=0—100kPa were measured using the intelligent gra- vimetric analyzer.The experimental results indicate that the presence of Al can significantly affect the adsorption of butene-1 than that of n-butane on ZSM-5 zeolites.Then,the double Langmuir(DL)model was applied to study the pure gas adsorption on ZSM-5 zeolites for pure n-butane and butene-1.By combining the DL model with the ideal adsorbed solution theory(IAST),the IAST-DL model was applied to model the butene-1(1)/n-butane(2)binary mixture adsorption on ZSM-5 zeolites with different Si/Al ratios.The calculated results are in good agreement with the experimental data,indicating that the IAST-DL model is effective for the present systems.Finally,the adsorp- tion over a wide range of variables was predicted at low pressure and 300K by the model proposed.It is found that the selectivity of butene-1 over n-butane increases linearly with the decrease of Si/Al ratio.A correlation between the selectivity and Si/Al ratio of the sample was proposed at 300K and p=0.08MPa.展开更多
Nitrogen oxide(NO_(x))is one of the most critical contaminants in the air,and the control of NO_(x)emission from diesel vehicles is very important.Cu-based small-pore zeolites have already been applied for NO_(x)abate...Nitrogen oxide(NO_(x))is one of the most critical contaminants in the air,and the control of NO_(x)emission from diesel vehicles is very important.Cu-based small-pore zeolites have already been applied for NO_(x)abatement on diesel vehicles.Among the small-pore zeolites,Cu-SSZ-50 catalysts with good NH_(3)-SCR catalytic activity were believed to have potential for application.In this study,a one-pot synthesis method for Cu-SSZ-50 catalysts was developed for the first time,using the co-templates of Cu-TEPA and 2,6-dimethyl-N-methylpyridinium hydroxide.In this synthesis method,Cu-SSZ-50 with various Cu contents can be obtained by adjusting the amount of Cu-TEPA without the need for a further after-treatment process.The addition of Cu-TEPA affected the framework atoms and Cu species,and a lower Si/Al ratio and more SCR active Cu species were obtained.The synthesized catalyst with a Cu/Al ratio of 0.40 exhibited over 90%NO_(x)conversion between 200℃and 450℃for the selective catalytic reduction of NO_(x)with NH_(3)(NH_(3)-SCR).Meanwhile,over 80%NO_(x)conversion could be obtained from 250℃to 450℃after hydrothermal aging at 750℃for 16 h.In addition,both L-H and E-R mechanisms were proven to exist for the one-pot-synthesized Cu-SSZ-50 by in situ DRIFTS experiments.The simple synthesis procedure,excellent catalytic activity and hydrothermal stability brighten the prospects for the application of Cu-SSZ-50.展开更多
基金Supported by the National Natural Science Foundation of China （Nos.20236010,20476004） and China Petroleum ＆ Chemical Corporation （No.X504023）.
文摘Four ZSM-5 zeolite catalysts with different Si/Al ratios for the catalytic cracking of C4 fractions to produce ethylene and propylene were prepared in this study.First,the adsorption isotherms of pure n-butane and butene-1 and their mixtures on these catalysts at 300K and p=0—100kPa were measured using the intelligent gra- vimetric analyzer.The experimental results indicate that the presence of Al can significantly affect the adsorption of butene-1 than that of n-butane on ZSM-5 zeolites.Then,the double Langmuir(DL)model was applied to study the pure gas adsorption on ZSM-5 zeolites for pure n-butane and butene-1.By combining the DL model with the ideal adsorbed solution theory(IAST),the IAST-DL model was applied to model the butene-1(1)/n-butane(2)binary mixture adsorption on ZSM-5 zeolites with different Si/Al ratios.The calculated results are in good agreement with the experimental data,indicating that the IAST-DL model is effective for the present systems.Finally,the adsorp- tion over a wide range of variables was predicted at low pressure and 300K by the model proposed.It is found that the selectivity of butene-1 over n-butane increases linearly with the decrease of Si/Al ratio.A correlation between the selectivity and Si/Al ratio of the sample was proposed at 300K and p=0.08MPa.
基金financially supported by the National Natural Science Foundation of China(Nos.52200136,52225004 and 51978640)the Science and Technology Innovation“2025”major program in Ningbo(No.2020Z103)。
文摘Nitrogen oxide(NO_(x))is one of the most critical contaminants in the air,and the control of NO_(x)emission from diesel vehicles is very important.Cu-based small-pore zeolites have already been applied for NO_(x)abatement on diesel vehicles.Among the small-pore zeolites,Cu-SSZ-50 catalysts with good NH_(3)-SCR catalytic activity were believed to have potential for application.In this study,a one-pot synthesis method for Cu-SSZ-50 catalysts was developed for the first time,using the co-templates of Cu-TEPA and 2,6-dimethyl-N-methylpyridinium hydroxide.In this synthesis method,Cu-SSZ-50 with various Cu contents can be obtained by adjusting the amount of Cu-TEPA without the need for a further after-treatment process.The addition of Cu-TEPA affected the framework atoms and Cu species,and a lower Si/Al ratio and more SCR active Cu species were obtained.The synthesized catalyst with a Cu/Al ratio of 0.40 exhibited over 90%NO_(x)conversion between 200℃and 450℃for the selective catalytic reduction of NO_(x)with NH_(3)(NH_(3)-SCR).Meanwhile,over 80%NO_(x)conversion could be obtained from 250℃to 450℃after hydrothermal aging at 750℃for 16 h.In addition,both L-H and E-R mechanisms were proven to exist for the one-pot-synthesized Cu-SSZ-50 by in situ DRIFTS experiments.The simple synthesis procedure,excellent catalytic activity and hydrothermal stability brighten the prospects for the application of Cu-SSZ-50.