This paper describes pre-treatment methods to improve the bake-hardening response of naturally aged AA6022 （Al-0.6Mg-1.0Si）, which is an alloy used in automotive body panels. These methods are used to accelerate the...This paper describes pre-treatment methods to improve the bake-hardening response of naturally aged AA6022 （Al-0.6Mg-1.0Si）, which is an alloy used in automotive body panels. These methods are used to accelerate the artificial aging process, which proceeds 30-day period of natural aging. The precipitation behavior of the sheets of this aluminum alloy was analyzed by differential scanning calorimetry （DSC） and electrical conductivity measurements, and subsequently confirmed by microstructure observations by transmission electron microscopy （TEM）. Tensile tests and microhardness measurements were performed to determine the mechanical properties of the samples. Under simulated paint-baking conditions （30 min at 170℃）, the microhardness and the yield strength （YS） of the pre-strained ＋ pre-aged samples were found to be I13 HV and 225 MPa, respectively. These values are considerably higher than those of pre-aged samples, and they did not decrease significantly during the initial stage of artificial aging.展开更多
For a series of Al-0.34／%Mg-1.05／%Si-0.08／%Cu alloys, the effects of pre-treatment on natural aging, bake hardening response and plasticity were investigated using Vickers hardness test and tensile test. Differenti...For a series of Al-0.34／%Mg-1.05／%Si-0.08／%Cu alloys, the effects of pre-treatment on natural aging, bake hardening response and plasticity were investigated using Vickers hardness test and tensile test. Differential scanning calorimetry （DSC） analysis was conducted to reveal corresponding precipitation mechanisms. The results showed that pre-straining and pre-aging alone couldn＇t completely suppress natural aging and improve bake hardening response simultaneously. The sensitivity of the pre-straining and pre-aging on the mechanical properties was evaluated. It was found that pre-aging was the main factor which greatly improved bake hardening response and pre-treatment had a weak influence on plasticity in pre-treated samples. DSC analysis showed that the dissolution trough of clusters disappeared in pre-treated samples, both β”and β＇ precipitation peak shifted to lower temperature and were reduced in pre-strained and pre-aged samples. It was concluded that the formation of Mg/Si clusters was replaced by the accelerated precipitation ofβ” andβ＇ phases, which caused the suppression of natural aging and the improvement of bake hardening response （BHR）.展开更多
The effect of pre-straining on the structure and formation mechanism of precipitates in an Al−Mg−Si−Cu alloy was systematically investigated by atomic resolution high-angle annular dark-field scanning transmission ele...The effect of pre-straining on the structure and formation mechanism of precipitates in an Al−Mg−Si−Cu alloy was systematically investigated by atomic resolution high-angle annular dark-field scanning transmission electron microscopy(HAADF-STEM).Elongated and string-like precipitates are formed along the dislocations in the pre-strained Al−Mg−Si−Cu alloy.The precipitates formed along the dislocations exhibit three features:non-periodic atomic arrangement within the precipitate;Cu segregation occurring at the precipitate/α(Al)interface;different orientations presented in one individual precipitate.Four different formation mechanisms of these heterogeneous precipitates were proposed as follows:elongated precipitates are formed independently in the dislocation;string-like precipitates are formed directly along the dislocations;different precipitates encounter to form string-like precipitates;precipitates are connected by other phases or solute enrichment regions.These different formation mechanisms are responsible for forming different atomic structures and morphologies of precipitates.展开更多
The influences of high temperature pre-straining (HT-PS) on the natural aging and bake hardening of Al?Mg?Si alloys were investigated by Vickers microhardness measurements, differential scanning calorimetry (DSC) anal...The influences of high temperature pre-straining (HT-PS) on the natural aging and bake hardening of Al?Mg?Si alloys were investigated by Vickers microhardness measurements, differential scanning calorimetry (DSC) analysis and transmission electron microscopy (TEM) characterization. The results show that pre-straining at 170 °C immediately after quenching can effectively resolve the rather high T4 temper hardness caused by the conventional room temperature (RT) pre-straining treatment, and give a better bake hardening response (BHR) after paint-bake cycle. HT-PS 7% at 170 °C for 10 min is chosen as the optimum process as it provides lower T4 temper hardness and better BHR. The simultaneous introduction of dislocations and Cluster (2) can significantly suppress the natural aging and promote the precipitation of β″ phase, and reduce the effects of deformation hardening by dynamic recovery.展开更多
Owing to their attractive structure and mechanical properties,high-entropy alloys(HEAs) and mediumentropy alloys(MEAs) have attracted considerable research interest.The strength of HEAs/MEAs with a single face-centere...Owing to their attractive structure and mechanical properties,high-entropy alloys(HEAs) and mediumentropy alloys(MEAs) have attracted considerable research interest.The strength of HEAs/MEAs with a single face-centered cubic(FCC) phase,on the other hand,requires improvement.Therefore,in this study,we demonstrate a strategy for increasing the room-temperature strength of FCC-phase HEAs/MEAs by tuning cryo-pre-straining-induced crystal defects via the temperature-dependent stacking fault energyregulated plasticity mechanism.Through neutron diffraction line profile analysis and electron microscope observation,the effect of the tuned defects on the tensile strength was clarified.Due to the cryorolling-induced high dislocation density,mechanical twins,and stacking faults,the room-temperature yield strength of an equiatomic CoCrFeNi HEA was increased by ~290%,from 243 MPa(as-recrystallized)to 941.6 MPa(30% cryo-rolled),while maintaining a tensile elongation of 18%.After partial recovery via heat treatment,the yield strength and ultimate tensile strength decreased slightly to 869 and 936 MPa,respectively.Conversely,the elongation increased to 25.6%,The dislocation density and distribution of the dislocations were found to contribute to the strengthening caused by forest dislocations,which warrants further investigation.This study discussed the possibility of developing single-phase high-performance HEAs by tuning pre-straining-induced crystal defects.展开更多
文摘This paper describes pre-treatment methods to improve the bake-hardening response of naturally aged AA6022 （Al-0.6Mg-1.0Si）, which is an alloy used in automotive body panels. These methods are used to accelerate the artificial aging process, which proceeds 30-day period of natural aging. The precipitation behavior of the sheets of this aluminum alloy was analyzed by differential scanning calorimetry （DSC） and electrical conductivity measurements, and subsequently confirmed by microstructure observations by transmission electron microscopy （TEM）. Tensile tests and microhardness measurements were performed to determine the mechanical properties of the samples. Under simulated paint-baking conditions （30 min at 170℃）, the microhardness and the yield strength （YS） of the pre-strained ＋ pre-aged samples were found to be I13 HV and 225 MPa, respectively. These values are considerably higher than those of pre-aged samples, and they did not decrease significantly during the initial stage of artificial aging.
基金supported by the Fundamental Research Fund for the Central Universities(No.CDJZR10130018)the Chongqing Science and Technology Commission (No.2011GZ0039)
文摘For a series of Al-0.34／%Mg-1.05／%Si-0.08／%Cu alloys, the effects of pre-treatment on natural aging, bake hardening response and plasticity were investigated using Vickers hardness test and tensile test. Differential scanning calorimetry （DSC） analysis was conducted to reveal corresponding precipitation mechanisms. The results showed that pre-straining and pre-aging alone couldn＇t completely suppress natural aging and improve bake hardening response simultaneously. The sensitivity of the pre-straining and pre-aging on the mechanical properties was evaluated. It was found that pre-aging was the main factor which greatly improved bake hardening response and pre-treatment had a weak influence on plasticity in pre-treated samples. DSC analysis showed that the dissolution trough of clusters disappeared in pre-treated samples, both β”and β＇ precipitation peak shifted to lower temperature and were reduced in pre-strained and pre-aged samples. It was concluded that the formation of Mg/Si clusters was replaced by the accelerated precipitation ofβ” andβ＇ phases, which caused the suppression of natural aging and the improvement of bake hardening response （BHR）.
基金the Natural Science Foundation of Jiangsu Province,China(No.BK20201035)the Talent Research Fund in Nanjing Institute of Technology,China(No.YKJ201957)+1 种基金the National Natural Science Foundation of China(Nos.51871035,52001159)the Natural Science Foundation of the Jiangsu Higher Education Institutions of China(Nos.20KJB430016,20KJB430012).
文摘The effect of pre-straining on the structure and formation mechanism of precipitates in an Al−Mg−Si−Cu alloy was systematically investigated by atomic resolution high-angle annular dark-field scanning transmission electron microscopy(HAADF-STEM).Elongated and string-like precipitates are formed along the dislocations in the pre-strained Al−Mg−Si−Cu alloy.The precipitates formed along the dislocations exhibit three features:non-periodic atomic arrangement within the precipitate;Cu segregation occurring at the precipitate/α(Al)interface;different orientations presented in one individual precipitate.Four different formation mechanisms of these heterogeneous precipitates were proposed as follows:elongated precipitates are formed independently in the dislocation;string-like precipitates are formed directly along the dislocations;different precipitates encounter to form string-like precipitates;precipitates are connected by other phases or solute enrichment regions.These different formation mechanisms are responsible for forming different atomic structures and morphologies of precipitates.
基金Project(2014DFA51270)supported by the International Science and Technology Cooperation Program of ChinaProject(51421001)supported by the Foundation for Innovative Research Groups of the National Natural Science Foundation of China
文摘The influences of high temperature pre-straining (HT-PS) on the natural aging and bake hardening of Al?Mg?Si alloys were investigated by Vickers microhardness measurements, differential scanning calorimetry (DSC) analysis and transmission electron microscopy (TEM) characterization. The results show that pre-straining at 170 °C immediately after quenching can effectively resolve the rather high T4 temper hardness caused by the conventional room temperature (RT) pre-straining treatment, and give a better bake hardening response (BHR) after paint-bake cycle. HT-PS 7% at 170 °C for 10 min is chosen as the optimum process as it provides lower T4 temper hardness and better BHR. The simultaneous introduction of dislocations and Cluster (2) can significantly suppress the natural aging and promote the precipitation of β″ phase, and reduce the effects of deformation hardening by dynamic recovery.
基金supported by a Grant-in-Aid for Scientific Research from the Japan Society for the Promotion of Science(JSPS)KAKENHI(Nos.19K14838 and 21K03766)the“Creation of Life Innovation Materials for Interdisciplinary and International Researcher Development”project。
文摘Owing to their attractive structure and mechanical properties,high-entropy alloys(HEAs) and mediumentropy alloys(MEAs) have attracted considerable research interest.The strength of HEAs/MEAs with a single face-centered cubic(FCC) phase,on the other hand,requires improvement.Therefore,in this study,we demonstrate a strategy for increasing the room-temperature strength of FCC-phase HEAs/MEAs by tuning cryo-pre-straining-induced crystal defects via the temperature-dependent stacking fault energyregulated plasticity mechanism.Through neutron diffraction line profile analysis and electron microscope observation,the effect of the tuned defects on the tensile strength was clarified.Due to the cryorolling-induced high dislocation density,mechanical twins,and stacking faults,the room-temperature yield strength of an equiatomic CoCrFeNi HEA was increased by ~290%,from 243 MPa(as-recrystallized)to 941.6 MPa(30% cryo-rolled),while maintaining a tensile elongation of 18%.After partial recovery via heat treatment,the yield strength and ultimate tensile strength decreased slightly to 869 and 936 MPa,respectively.Conversely,the elongation increased to 25.6%,The dislocation density and distribution of the dislocations were found to contribute to the strengthening caused by forest dislocations,which warrants further investigation.This study discussed the possibility of developing single-phase high-performance HEAs by tuning pre-straining-induced crystal defects.