Nickel-phosphorus （Ni-P） composite coatings containing potassium titanate （K2Ti6O13） whiskers （PTWs） were prepared by electroless plating. The surface morphology and component of coatings were investigated by sc...Nickel-phosphorus （Ni-P） composite coatings containing potassium titanate （K2Ti6O13） whiskers （PTWs） were prepared by electroless plating. The surface morphology and component of coatings were investigated by scanning electron microscopy （SEM） and energy dispersive X-ray spectroscopy （EDX）, respectively before and after wear test. The tribological performance was evaluated using a pin-on-disk wear tester under dry conditions. It is found that the Ni-P-PTWs composite coatings exhibit higher wear resistance than Ni-P and Ni-P-SiC electroless coatings. The favorable effects of PTWs on the tribological properties of the composite coatings are attributed to the super-strong mechanical properties and the specific tunneling structures of PTWs. The PTWs greatly reinforce the structure of the Ni-P-based composite coatings and thereby greatly reduce the adhesive and plough wear of Ni-P-PTWs composite coatings.展开更多
A group of poly (phthalazinone ether sulfone ketone)/potassium-titanate-whisker (PPSEK/whisker) composites was prepared by coprecipitation from solution. The whisker surface was modified using titanate coupling agent ...A group of poly (phthalazinone ether sulfone ketone)/potassium-titanate-whisker (PPSEK/whisker) composites was prepared by coprecipitation from solution. The whisker surface was modified using titanate coupling agent prior to blending. The tensile, impact, morphology and thermal properties of the moulded composites were investigated. The measurements showed that the tensile strength and impact strength of the composites increased with increasing whiskers content up to 10 to 20 phr, thereafter they showed a decrease in the whiskers content reached 40 phr. At the same time, the modulus of the composites increased with increasing whiskers content. Scanning electron microscopy studies revealed that the whiskers within the composites were dispersed uniformly by treated with coupling agent. Finally, thermogravimetric analysis showed that the heat resistance of the composites tended to increase with increasing whisker content. The results were analysed and discussed in terms of established models of the behaviour of short-fiber reinforced composites.展开更多
基金This work was supported by the National Natural Science Foundation of China(Grant No.50335060)the Excellent Young Teacher Award of the Education Ministry of China(No.[2002]383).
文摘Nickel-phosphorus （Ni-P） composite coatings containing potassium titanate （K2Ti6O13） whiskers （PTWs） were prepared by electroless plating. The surface morphology and component of coatings were investigated by scanning electron microscopy （SEM） and energy dispersive X-ray spectroscopy （EDX）, respectively before and after wear test. The tribological performance was evaluated using a pin-on-disk wear tester under dry conditions. It is found that the Ni-P-PTWs composite coatings exhibit higher wear resistance than Ni-P and Ni-P-SiC electroless coatings. The favorable effects of PTWs on the tribological properties of the composite coatings are attributed to the super-strong mechanical properties and the specific tunneling structures of PTWs. The PTWs greatly reinforce the structure of the Ni-P-based composite coatings and thereby greatly reduce the adhesive and plough wear of Ni-P-PTWs composite coatings.
基金the National Natural Science Foundation of China under grant No.59473901 Educational Office Fesearch Project of Liaoning Provice under grant No.2020701095.
文摘A group of poly (phthalazinone ether sulfone ketone)/potassium-titanate-whisker (PPSEK/whisker) composites was prepared by coprecipitation from solution. The whisker surface was modified using titanate coupling agent prior to blending. The tensile, impact, morphology and thermal properties of the moulded composites were investigated. The measurements showed that the tensile strength and impact strength of the composites increased with increasing whiskers content up to 10 to 20 phr, thereafter they showed a decrease in the whiskers content reached 40 phr. At the same time, the modulus of the composites increased with increasing whiskers content. Scanning electron microscopy studies revealed that the whiskers within the composites were dispersed uniformly by treated with coupling agent. Finally, thermogravimetric analysis showed that the heat resistance of the composites tended to increase with increasing whisker content. The results were analysed and discussed in terms of established models of the behaviour of short-fiber reinforced composites.