A novel reactive polycarboxylic acid dye was synthesized by the reaction of polymaleic anhydride（PMA） with 3-methyl-1-（4- sulfonylphenyl）-4-（4-aminophenylazo）-2-pyrazoline-5-one.The structure of the novel dye wa...A novel reactive polycarboxylic acid dye was synthesized by the reaction of polymaleic anhydride（PMA） with 3-methyl-1-（4- sulfonylphenyl）-4-（4-aminophenylazo）-2-pyrazoline-5-one.The structure of the novel dye was characterized by FTIR,UV-vis and ^（13）C NMR spectra.The dyeing properties of dye on cotton were tested,and the novel dye possessed high fixation and good fastness.展开更多
Aluminum nitride(AlN)is considered one of the most desirable materials for integrated circuits and electronic packaging substrates.However,raw AlN powder reacts easily with water,forming Al(OH)3 or AlOOH on the surfac...Aluminum nitride(AlN)is considered one of the most desirable materials for integrated circuits and electronic packaging substrates.However,raw AlN powder reacts easily with water,forming Al(OH)3 or AlOOH on the surface and hindering the development of an aqueous tape-casting process for preparing AlN ceramic substrates.In this study,hydrolyzed polymaleic anhydride(HPMA)was used to modify AlN powder,which has good water solubility and dispersibility.The AlN powder was modified with 5 wt%HPMA remained stable in water for at least 90 h under magnetic stirring condition and 24 h under ball milling condition,indicating that HPMA-modified AlN powder has good resistance to hydrolysis.The action mechanism of HPMA is revealed.Firstly,–COOH of the HPMA polymer and the oxide layer on the surface of the AlN powder underwent a dehydration condensation reaction to form a compound.Secondly,long chains of the polymer further coated the surface of the AlN powder,forming an anti-hydration layer with a thickness of about 7.0 nm on the surface of the AlN particles.In addition,AlN green sheets were successfully prepared by aqueous tape casting using the HPMA-modified AlN powder without additional dispersants.Subsequently,AlN ceramic substrates were obtained by sintering at 1750℃for 4 h under an N2 atmosphere with a pressure of 0.2 MPa.The relative density and thermal conductivity were tested to be 97.3%and 122 W/(m·K),respectively.展开更多
基金supported by the State Key Program of National Natural Science Foundation of China(No. 20836001)the Program for Changjiang Scholars and Innovative Research Team in the University(No.IRT0711)
文摘A novel reactive polycarboxylic acid dye was synthesized by the reaction of polymaleic anhydride（PMA） with 3-methyl-1-（4- sulfonylphenyl）-4-（4-aminophenylazo）-2-pyrazoline-5-one.The structure of the novel dye was characterized by FTIR,UV-vis and ^（13）C NMR spectra.The dyeing properties of dye on cotton were tested,and the novel dye possessed high fixation and good fastness.
文摘研究了聚马来酸酐应用于棉织物的抗皱整理工艺.采用单因素实验考察了聚马来酸酐浓度、次亚磷酸钠浓度、焙烘温度以及焙烘时间对折皱回复角的影响,以L9(34)正交试验对其进行了优化.确定了最佳整理工艺条件:聚马来酸酐用量120 g·L-1、次亚磷酸钠用量30 g·L-1、焙烘温度170℃、焙烘时间7 min.
基金This work was financially supported by the National Natural Science Foundation of China(Nos.52102101,52267001)the Natural Science Foundation of Jiangxi Province(No.20212BAB204019).
文摘Aluminum nitride(AlN)is considered one of the most desirable materials for integrated circuits and electronic packaging substrates.However,raw AlN powder reacts easily with water,forming Al(OH)3 or AlOOH on the surface and hindering the development of an aqueous tape-casting process for preparing AlN ceramic substrates.In this study,hydrolyzed polymaleic anhydride(HPMA)was used to modify AlN powder,which has good water solubility and dispersibility.The AlN powder was modified with 5 wt%HPMA remained stable in water for at least 90 h under magnetic stirring condition and 24 h under ball milling condition,indicating that HPMA-modified AlN powder has good resistance to hydrolysis.The action mechanism of HPMA is revealed.Firstly,–COOH of the HPMA polymer and the oxide layer on the surface of the AlN powder underwent a dehydration condensation reaction to form a compound.Secondly,long chains of the polymer further coated the surface of the AlN powder,forming an anti-hydration layer with a thickness of about 7.0 nm on the surface of the AlN particles.In addition,AlN green sheets were successfully prepared by aqueous tape casting using the HPMA-modified AlN powder without additional dispersants.Subsequently,AlN ceramic substrates were obtained by sintering at 1750℃for 4 h under an N2 atmosphere with a pressure of 0.2 MPa.The relative density and thermal conductivity were tested to be 97.3%and 122 W/(m·K),respectively.