Ni-Cr alloyed layer was formed on surface of Q235 steel by double glow plasma surface metallurgy to improve the corrosion resistance of substrate. The composition and microstructure of alloyed layer was analyzed by SE...Ni-Cr alloyed layer was formed on surface of Q235 steel by double glow plasma surface metallurgy to improve the corrosion resistance of substrate. The composition and microstructure of alloyed layer was analyzed by SEM and XRD. Potentiodynamic polarization and electrochemical impedance spectroscopy was applied to evaluate the corrosion resistance of the alloyed layer. The results showed working pressure had a great effect on structure of Ni-Cr alloyed layer, and the dense and smooth alloyed layer was prepared at 50 Pa working pressure. Compared with substrate, Ni-Cr alloyed layer exhibited higher corrosion potential, lower corrosion current density and larger charge transfer resistance, which indicated that Ni-Cr alloyed layer significantly modified the corrosion resistance of Q235 steel.展开更多
基金the Jiangsu Province Technology Results Transformation Special Funds (No. BA2007036)
文摘Ni-Cr alloyed layer was formed on surface of Q235 steel by double glow plasma surface metallurgy to improve the corrosion resistance of substrate. The composition and microstructure of alloyed layer was analyzed by SEM and XRD. Potentiodynamic polarization and electrochemical impedance spectroscopy was applied to evaluate the corrosion resistance of the alloyed layer. The results showed working pressure had a great effect on structure of Ni-Cr alloyed layer, and the dense and smooth alloyed layer was prepared at 50 Pa working pressure. Compared with substrate, Ni-Cr alloyed layer exhibited higher corrosion potential, lower corrosion current density and larger charge transfer resistance, which indicated that Ni-Cr alloyed layer significantly modified the corrosion resistance of Q235 steel.