磁体的注射成形是一种高效生产的近净成形技术。为了制备出具有较好综合性能的注射成形粘结钕铁硼永磁材料,研究了粘结剂对注射成形磁体的磁性能、加工性能及力学性能的影响;分析了硅烷系列的偶联剂、复合润滑剂和抗氧剂等添加剂对注射...磁体的注射成形是一种高效生产的近净成形技术。为了制备出具有较好综合性能的注射成形粘结钕铁硼永磁材料,研究了粘结剂对注射成形磁体的磁性能、加工性能及力学性能的影响;分析了硅烷系列的偶联剂、复合润滑剂和抗氧剂等添加剂对注射成形磁体性能的影响。结果表明,用MQP-B快淬钕铁硼磁粉和尼龙12粘结剂制备出了剩余磁感应强度为0.539 T,磁感矫顽力为345.37 k A/m,内禀矫顽力为681.02 k A/m,最大磁能积为47.37 k J/m3的注射成形钕铁硼磁体。展开更多
In order to obtain ultrafine Nd-Fe-B powder, a spray-dried precursor was treated by reduction-diffusion (R/D) process. And, unlike the conventional R/D process, calcium reduction that is a crucial step for the formati...In order to obtain ultrafine Nd-Fe-B powder, a spray-dried precursor was treated by reduction-diffusion (R/D) process. And, unlike the conventional R/D process, calcium reduction that is a crucial step for the formation of Nd2Fe14B was performed without conglomerating the precursor with Ca powder. By adopting this modified process, it is possible to synthesize the hard magnetic Nd2Fe14B at the reaction temperature as low as 850 ℃. The average size of Nd2Fe14B particles that are uniformly distributed in the optimally treated powder was <<1 μm. Most Nd2Fe14B particles were enclosed with thin layers of Nd-rich phase. Typical magnetic properties of such powder without eliminating impurity CaO were iHc=～5.9 kOe, Br=～5.5 kG, and (BH)max=～6 MGOe.展开更多
Melt-spun Nd8Fe78B6Co4 magnetic powders and their bonded magnets were prepared with the optimization of compositions and preparation techniques. The microstructure change of alloy NdFeB and the relation between micros...Melt-spun Nd8Fe78B6Co4 magnetic powders and their bonded magnets were prepared with the optimization of compositions and preparation techniques. The microstructure change of alloy NdFeB and the relation between microstruc-ture and heat-treatment were studied. The heat-treatment temperature is 200 ~ 700℃. The as-cast structure of the alloy is typically amorphous. Different melt-spun speed and different heat treatment could result in different magnetic properties of NdFeB magnets. Magnetic properties of NdFeB increase with the addition of element Co. The magnetic properties of magnet alloy get the best when the melt-spun speed reaches 23 ~ 26 m·s-1, heat treatment temperature is 690℃and time is 30 min.展开更多
NdFeB coercive powder can be obtained directely by hydrogen treated ahoy ingots, The magnetic properties of the powder are comparable with that made by rapidsolidified process.An appreciable coercivity created during ...NdFeB coercive powder can be obtained directely by hydrogen treated ahoy ingots, The magnetic properties of the powder are comparable with that made by rapidsolidified process.An appreciable coercivity created during hydrogen treatment is closely related to the refined crystal grains.展开更多
文摘磁体的注射成形是一种高效生产的近净成形技术。为了制备出具有较好综合性能的注射成形粘结钕铁硼永磁材料,研究了粘结剂对注射成形磁体的磁性能、加工性能及力学性能的影响;分析了硅烷系列的偶联剂、复合润滑剂和抗氧剂等添加剂对注射成形磁体性能的影响。结果表明,用MQP-B快淬钕铁硼磁粉和尼龙12粘结剂制备出了剩余磁感应强度为0.539 T,磁感矫顽力为345.37 k A/m,内禀矫顽力为681.02 k A/m,最大磁能积为47.37 k J/m3的注射成形钕铁硼磁体。
文摘In order to obtain ultrafine Nd-Fe-B powder, a spray-dried precursor was treated by reduction-diffusion (R/D) process. And, unlike the conventional R/D process, calcium reduction that is a crucial step for the formation of Nd2Fe14B was performed without conglomerating the precursor with Ca powder. By adopting this modified process, it is possible to synthesize the hard magnetic Nd2Fe14B at the reaction temperature as low as 850 ℃. The average size of Nd2Fe14B particles that are uniformly distributed in the optimally treated powder was <<1 μm. Most Nd2Fe14B particles were enclosed with thin layers of Nd-rich phase. Typical magnetic properties of such powder without eliminating impurity CaO were iHc=～5.9 kOe, Br=～5.5 kG, and (BH)max=～6 MGOe.
文摘Melt-spun Nd8Fe78B6Co4 magnetic powders and their bonded magnets were prepared with the optimization of compositions and preparation techniques. The microstructure change of alloy NdFeB and the relation between microstruc-ture and heat-treatment were studied. The heat-treatment temperature is 200 ~ 700℃. The as-cast structure of the alloy is typically amorphous. Different melt-spun speed and different heat treatment could result in different magnetic properties of NdFeB magnets. Magnetic properties of NdFeB increase with the addition of element Co. The magnetic properties of magnet alloy get the best when the melt-spun speed reaches 23 ~ 26 m·s-1, heat treatment temperature is 690℃and time is 30 min.
文摘NdFeB coercive powder can be obtained directely by hydrogen treated ahoy ingots, The magnetic properties of the powder are comparable with that made by rapidsolidified process.An appreciable coercivity created during hydrogen treatment is closely related to the refined crystal grains.