The effect of dopant valence on oxygen desorption and oxygen permeability of SrCo0.4Fe0.5M0.1O3-δ （M = Ni, Al and Zr） mixed-conducting oxides were investigated in detail by O2-TPD and oxygen permeation measurement....The effect of dopant valence on oxygen desorption and oxygen permeability of SrCo0.4Fe0.5M0.1O3-δ （M = Ni, Al and Zr） mixed-conducting oxides were investigated in detail by O2-TPD and oxygen permeation measurement. The SrCo0.4Fe0.5M0.1O3-δ for M = Fe, Ni, Al and Zr were denoted as SCF, SCFN, SCFA and SCFZ, respectively. O2-TPD analysis revealed that the amount of α oxygen desorption decreased with increasing the valance of doped metal elements （SCFN 〉 SCFA SCF 〉 SCFZ）. The oxygen permeation flux at the temperature ≈igher than 1148 K decreased in the order of SCFN 〉 SCF 〉 SCFZ 〉 SCFA. Single activation for oxygen permeation was observed for SCFZ oxide and the activation energies of SCF and SCFA change at around 1073 K, while the change temoerature of SCFN was about 1173 K.展开更多
基金This work is sponsored by the National Basic Research Program of China （No. 2003CB615702）；National Natural Science Foundation of China （No. 20576051, 20636020）；Special Research Foundation for Doctoral Discipline of Higher Education （No. 20060291003）.
文摘The effect of dopant valence on oxygen desorption and oxygen permeability of SrCo0.4Fe0.5M0.1O3-δ （M = Ni, Al and Zr） mixed-conducting oxides were investigated in detail by O2-TPD and oxygen permeation measurement. The SrCo0.4Fe0.5M0.1O3-δ for M = Fe, Ni, Al and Zr were denoted as SCF, SCFN, SCFA and SCFZ, respectively. O2-TPD analysis revealed that the amount of α oxygen desorption decreased with increasing the valance of doped metal elements （SCFN 〉 SCFA SCF 〉 SCFZ）. The oxygen permeation flux at the temperature ≈igher than 1148 K decreased in the order of SCFN 〉 SCF 〉 SCFZ 〉 SCFA. Single activation for oxygen permeation was observed for SCFZ oxide and the activation energies of SCF and SCFA change at around 1073 K, while the change temoerature of SCFN was about 1173 K.