A study on the melting and viscosity properties of the chromium-containing high-titanium melting slag(CaO–SiO2–MgO–Al2O3–TiO2–Cr2O3) with TiO2 contents ranging from 38.63 wt% to 42.63 wt% was conducted. The melti...A study on the melting and viscosity properties of the chromium-containing high-titanium melting slag(CaO–SiO2–MgO–Al2O3–TiO2–Cr2O3) with TiO2 contents ranging from 38.63 wt% to 42.63 wt% was conducted. The melting properties were investigated with a meltingpoint apparatus, and viscosity was measured using the rotating cylinder method. The FactSage 7.1 software and X-ray diffraction, in combination with scanning electron microscopy–energy-dispersive spectroscopy(SEM–EDS), were used to characterize the phase equilibrium and microstructure of chromium-containing high-titanium melting slags. The results indicated that an increase in the TiO2 content led to a decrease in the viscosity of the chromium-containing high-titanium melting slag. In addition, the softening temperature, hemispheric temperature, and flowing temperature decreased with increasing TiO2 content. The amount of crystallized anosovite and sphene phases gradually increased with increasing TiO2 content, whereas the amount of perovskite phase decreased. SEM observations revealed that the distribution of the anosovite phase was dominantly influenced by TiO2.展开更多
It is found that strong basic oxides including Li 2O, Na 2O, K 2O and BaO, which are used to replace a part of CaO in CaO based fluxes, can lower the melting point and the viscosity and enhance the dephosphorizing...It is found that strong basic oxides including Li 2O, Na 2O, K 2O and BaO, which are used to replace a part of CaO in CaO based fluxes, can lower the melting point and the viscosity and enhance the dephosphorizing ability. The mechanism was analysed and the addition of Li 2O to CaO based fluxes was recommended.展开更多
It is found that strong basic oxides including Li2O,Na2O,K2O and BaO,which are used to replace a part of CaO in CaO-based fluxes,can lower the melting point and the viscosity and enhance the dephosphorizing ability. T...It is found that strong basic oxides including Li2O,Na2O,K2O and BaO,which are used to replace a part of CaO in CaO-based fluxes,can lower the melting point and the viscosity and enhance the dephosphorizing ability. The mechanism was analysed and the addition of Li2O to CaO based fluxes was recommended.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51904066)the Fundamental Research Funds for the Central Universities,China(No.N182503032)+1 种基金the Postdoctoral Foundation of Northeastern University,China(No.20190201)the Postdoctoral International Exchange Program,China(Dispatch Project,20190075)
文摘A study on the melting and viscosity properties of the chromium-containing high-titanium melting slag(CaO–SiO2–MgO–Al2O3–TiO2–Cr2O3) with TiO2 contents ranging from 38.63 wt% to 42.63 wt% was conducted. The melting properties were investigated with a meltingpoint apparatus, and viscosity was measured using the rotating cylinder method. The FactSage 7.1 software and X-ray diffraction, in combination with scanning electron microscopy–energy-dispersive spectroscopy(SEM–EDS), were used to characterize the phase equilibrium and microstructure of chromium-containing high-titanium melting slags. The results indicated that an increase in the TiO2 content led to a decrease in the viscosity of the chromium-containing high-titanium melting slag. In addition, the softening temperature, hemispheric temperature, and flowing temperature decreased with increasing TiO2 content. The amount of crystallized anosovite and sphene phases gradually increased with increasing TiO2 content, whereas the amount of perovskite phase decreased. SEM observations revealed that the distribution of the anosovite phase was dominantly influenced by TiO2.
基金the support of Wong K C Education Foundation , Hong Kong
文摘It is found that strong basic oxides including Li 2O, Na 2O, K 2O and BaO, which are used to replace a part of CaO in CaO based fluxes, can lower the melting point and the viscosity and enhance the dephosphorizing ability. The mechanism was analysed and the addition of Li 2O to CaO based fluxes was recommended.
基金Item Sponsored by National Natural Science Foundation of China(59774015)
文摘It is found that strong basic oxides including Li2O,Na2O,K2O and BaO,which are used to replace a part of CaO in CaO-based fluxes,can lower the melting point and the viscosity and enhance the dephosphorizing ability. The mechanism was analysed and the addition of Li2O to CaO based fluxes was recommended.