P and RE complex modification of hypereutectic Al-Si alloys was conducted. The influences of P, RE content on the microstructure and mechanical properties of alloys were investigated. The complex modifications of P an...P and RE complex modification of hypereutectic Al-Si alloys was conducted. The influences of P, RE content on the microstructure and mechanical properties of alloys were investigated. The complex modifications of P and RE make the coarse block primary silicon obviously refined and the large needle eutectic silicon modified to the fine fibrous or lamella ones. P mainly refines the primary silicon, but excess P is unfavorable to the refinement of primary silicon. RE can well refine the primary and eutectic silicon, but its modification effect on the eutectic silicon is more obvious. P can repress the modification of RE on the eutectic silicon. The alloys with the additions of 0.08% P and 0.60% RE have the optimal microstructure and the highest mechanical properties. Compared with the unmodified alloy, the primary silicon of alloys can be refined from 66.4 μm to 23.3 μm and the eutectic silicon can be refined from 8.3 μm to 5.2 μm. The tensile strength is improved from 256 MPa to 306 MPa and the elongation is improved from 0.35% to 0.48%.展开更多
The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The r...The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.展开更多
The effect of the rare earth cerium （Ce） on the hypereutectic Al-Si alloy under different casting states have been studied by optical microscope and quantitative image analysis. It is found that the size and the qua...The effect of the rare earth cerium （Ce） on the hypereutectic Al-Si alloy under different casting states have been studied by optical microscope and quantitative image analysis. It is found that the size and the quantity of primary silicon in castings decrease with the increase of added Ce in the melt. Meanwhile primary silicon changes from branched shape to fine facetted shape. Although the modification on eutectic silicon in castings also improves with the increase of added Ce in the melt, the effect of modification on eutectic silicon away from primary silicon is more obvious than that on eutectic silicon close to primary silicon. The modification mechanism was analyzed in detail by means of scanning electron microscope equipped with energy dispersive analysis of X-ray and thermodynamics analysis, which included the analysis on the change in standard Gibbs energy of reaction and reaction equilibrium.展开更多
文摘P and RE complex modification of hypereutectic Al-Si alloys was conducted. The influences of P, RE content on the microstructure and mechanical properties of alloys were investigated. The complex modifications of P and RE make the coarse block primary silicon obviously refined and the large needle eutectic silicon modified to the fine fibrous or lamella ones. P mainly refines the primary silicon, but excess P is unfavorable to the refinement of primary silicon. RE can well refine the primary and eutectic silicon, but its modification effect on the eutectic silicon is more obvious. P can repress the modification of RE on the eutectic silicon. The alloys with the additions of 0.08% P and 0.60% RE have the optimal microstructure and the highest mechanical properties. Compared with the unmodified alloy, the primary silicon of alloys can be refined from 66.4 μm to 23.3 μm and the eutectic silicon can be refined from 8.3 μm to 5.2 μm. The tensile strength is improved from 256 MPa to 306 MPa and the elongation is improved from 0.35% to 0.48%.
文摘The microstructure and mechanical properties of Al-14.6Si castings modified by Cu-P master alloy under different conditions were studied with optical microscope（OM） and mechanical testing and simulation（MTS）.The results indicate that the Cu-P master alloy possesses not only obvious modification effect,but also longevity effect with more than 8 h on the hypereutectic Al-Si alloy.It is shown from thermal calculation,scanning electron microscope（SEM）,and energy dispersive analysis of X-rays（EDAX） that the modification mechanism of Cu-P on primary silicon in the castings is heterogeneous nucleation around AlP particles.The Cu-P master alloy has no or little modifying effect on eutectic silicon,even though it has obvious modification on primary silicon in the castings.This may be because of the fast transformation of eutectic silicon at a very narrow temperature,which will notably weaken the role of AlP particles as heterogeneous nuclei for eutectic silicon.
基金The work is financially supported by Shanghai Leading Academic Discipline Project (No. T0101)the Open Funds of Shanghai Key Laboratory of Metal Function Materials Research and Application.
文摘The effect of the rare earth cerium （Ce） on the hypereutectic Al-Si alloy under different casting states have been studied by optical microscope and quantitative image analysis. It is found that the size and the quantity of primary silicon in castings decrease with the increase of added Ce in the melt. Meanwhile primary silicon changes from branched shape to fine facetted shape. Although the modification on eutectic silicon in castings also improves with the increase of added Ce in the melt, the effect of modification on eutectic silicon away from primary silicon is more obvious than that on eutectic silicon close to primary silicon. The modification mechanism was analyzed in detail by means of scanning electron microscope equipped with energy dispersive analysis of X-ray and thermodynamics analysis, which included the analysis on the change in standard Gibbs energy of reaction and reaction equilibrium.