The catalytic effect of K2SiF6 on MgH2 was first timely studied.The MgH2+5 wt.%K2SiF6 was prepared via the ball milling technique.The catalyst had lessened the initial decomposition temperature by 134℃ and 48℃ as co...The catalytic effect of K2SiF6 on MgH2 was first timely studied.The MgH2+5 wt.%K2SiF6 was prepared via the ball milling technique.The catalyst had lessened the initial decomposition temperature by 134℃ and 48℃ as compared to both pristine and milled MgH2 samples,respectively.In 2 minutes,4.5 wt.%of hydrogen was absorbed(250℃)by the doped composite,which was 0.8 wt.%higher than the milled MgH2.Meanwhile,for the desorption kinetics(320℃,1 atm),the amount of desorbed hydrogen was increased by 2.4 wt.%and 2.3 wt.%for the first 10 and 20 minutes.Besides,contracting volume and Johnson-Mehl-Avrami models were used to analyse the kinetics sorptions.The decomposition activation energy calculated based on Kissinger equation was 114 kJ/mol.As for the active species,Mg2Si,MgF2 and KH were formed during the heating process.These active species are speculated to be responsible for the improvement of the hydrogenation properties of the composite.展开更多
A temperature programmed decomposition (TPD) apparatus with metal tube structure, in which Ar is used as the carrier gas, is established and the TPD spectrum of titanium hydride is acquired. Using consulting table met...A temperature programmed decomposition (TPD) apparatus with metal tube structure, in which Ar is used as the carrier gas, is established and the TPD spectrum of titanium hydride is acquired. Using consulting table method (CTM), spectrum superposition method (SSM) and differential spectrum technique, TPD spectrum of titanium hydride is separated and a set of thermal decomposition kinetics equations are acquired. According to these equations, the relationship between decomposition quantity and time for titanium hydride at the temperature of 940 K is obtained and the result well coincides with the AI alloy melt foaming process.展开更多
基金the Universiti Malaysia Terengganu(UMT)through the Golden Goose Research Grant(GGRG)(VOT 55190).
文摘The catalytic effect of K2SiF6 on MgH2 was first timely studied.The MgH2+5 wt.%K2SiF6 was prepared via the ball milling technique.The catalyst had lessened the initial decomposition temperature by 134℃ and 48℃ as compared to both pristine and milled MgH2 samples,respectively.In 2 minutes,4.5 wt.%of hydrogen was absorbed(250℃)by the doped composite,which was 0.8 wt.%higher than the milled MgH2.Meanwhile,for the desorption kinetics(320℃,1 atm),the amount of desorbed hydrogen was increased by 2.4 wt.%and 2.3 wt.%for the first 10 and 20 minutes.Besides,contracting volume and Johnson-Mehl-Avrami models were used to analyse the kinetics sorptions.The decomposition activation energy calculated based on Kissinger equation was 114 kJ/mol.As for the active species,Mg2Si,MgF2 and KH were formed during the heating process.These active species are speculated to be responsible for the improvement of the hydrogenation properties of the composite.
基金This work was supported by the National Natural Science Foundation of China(Grant Nos.50231010,50081002,90205005 and 19982001).
文摘A temperature programmed decomposition (TPD) apparatus with metal tube structure, in which Ar is used as the carrier gas, is established and the TPD spectrum of titanium hydride is acquired. Using consulting table method (CTM), spectrum superposition method (SSM) and differential spectrum technique, TPD spectrum of titanium hydride is separated and a set of thermal decomposition kinetics equations are acquired. According to these equations, the relationship between decomposition quantity and time for titanium hydride at the temperature of 940 K is obtained and the result well coincides with the AI alloy melt foaming process.