Gd-Co alloy films were synthesized by potentiostatic electrolysis on Cu substrates in urea-acetamide-NaBr-KBr melt at 353 K. The electroreduction of Co^2＋ and Gd^3＋ was investigated by cyclic voltammetry. The reduct...Gd-Co alloy films were synthesized by potentiostatic electrolysis on Cu substrates in urea-acetamide-NaBr-KBr melt at 353 K. The electroreduction of Co^2＋ and Gd^3＋ was investigated by cyclic voltammetry. The reduction of Co^2＋ is an irreversible process. Gd^3＋ cannot be reduced alone, but it can be inductively co-deposited with Co^2＋. Both the Gd content and microstructure of the prepared Gd-Co alloy films can be controlled by the deposited potential. The content of Gd was analyzed using an inductively coupled plasma emission spectrometer （ICPES）, and the microstructure was observed by scanning electron micrograph （SEM）. The films were crystallized by heat-treatment at 823 K for 30 s in Ar atmosphere, and then were investigated by XRD. The hysteresis loops of the Gd-Co alloy films were measured by a vibrating sample magnetometer （VSM）. The experimental results reveal that the deposited Gd-Co alloy films are amorphous, while the annealing causes the samples to change from amorphous to polycrystalline, thus enhancing their magnetocrystalline anisotropy and coercivity. Moreover, the magnetic properties of the Gd-Co alloy films depend strongly on the Gd content.展开更多
基金financially supported by the Science Foundation of the Educational Department of Fujian Prov-ince (No. 2008F5021)the Natural Science Foundation of Fujian Province (No. A0510013)the National Natural Science Foundation of China (No. 60676055)
文摘Gd-Co alloy films were synthesized by potentiostatic electrolysis on Cu substrates in urea-acetamide-NaBr-KBr melt at 353 K. The electroreduction of Co^2＋ and Gd^3＋ was investigated by cyclic voltammetry. The reduction of Co^2＋ is an irreversible process. Gd^3＋ cannot be reduced alone, but it can be inductively co-deposited with Co^2＋. Both the Gd content and microstructure of the prepared Gd-Co alloy films can be controlled by the deposited potential. The content of Gd was analyzed using an inductively coupled plasma emission spectrometer （ICPES）, and the microstructure was observed by scanning electron micrograph （SEM）. The films were crystallized by heat-treatment at 823 K for 30 s in Ar atmosphere, and then were investigated by XRD. The hysteresis loops of the Gd-Co alloy films were measured by a vibrating sample magnetometer （VSM）. The experimental results reveal that the deposited Gd-Co alloy films are amorphous, while the annealing causes the samples to change from amorphous to polycrystalline, thus enhancing their magnetocrystalline anisotropy and coercivity. Moreover, the magnetic properties of the Gd-Co alloy films depend strongly on the Gd content.