Terpyridine-capped poly（ethylene glycol） （PEG） was synthesized as a novel polymeric ligand and rare earth complex was prepared from Eu（NO3）3 and the telechelic macromolecules. The structure of the complex was ch...Terpyridine-capped poly（ethylene glycol） （PEG） was synthesized as a novel polymeric ligand and rare earth complex was prepared from Eu（NO3）3 and the telechelic macromolecules. The structure of the complex was characterized by 1H NMR, FT-IR, UV-vis and fluores-cence spectroscopy. Strong fluorescent emission of the complex was observed at 593 and 616 nm upon the excitation of 300 nm. The fluo-rescent emission was quenched upon addition of trace amount of diethyl chlorophosphate （DCP）. And the observed Ksv values for DCP were measured to be 0.568×10^3 and 0.89×10^3 L/mol for quenching at 593 and 616 nm, which indicated the detection limit for DCP was about 0.014 mmol/L. These results showed that the terpyridine-lanthanide complex could be an effective chemosensor with a potential application in the detection of organophosphates.展开更多
Eu3+ doped-CdTe(CdTe:Eu3+)nanocrystals were prepared via a facile hydrothermal method,and Eu3+ was successfully incorporated into the crystal lattice of CdTe and measured by X-ray powder diffraction(XRD),transmission ...Eu3+ doped-CdTe(CdTe:Eu3+)nanocrystals were prepared via a facile hydrothermal method,and Eu3+ was successfully incorporated into the crystal lattice of CdTe and measured by X-ray powder diffraction(XRD),transmission electron microscopy(TEM),ultraviolet-visible(UV-Vis) absorption spectroscopy and fluorescence emission.The CdTe:Eu^3+ nanocrystals still have a cubic crystal structure,and the corresponding XRD peaks of CdTe:Eu3+nanocrystals shift to larger angles compared with those of pure CdTe.The CdTe:Eu3+ nanocrystals are monodisperse and the particles size is about 2-4 nm.Compared with pure CdTe,the CdTe:Eu^3+ nanocrystals have larger band gap and thus exhibit blueshift in the emission spectra,which could be accounted for by the energy transfer between Eu^3+ and CdTe.To enhance the stability and functionality of CdTe:Eu3+nanocrystals,the CdTe:Eu3+nanocrystals were coated with SiO2 and the core-shell SiO2-coated CdTe:Eu3+nanocrystals(CdTe:Eu^3+@SiO2) were prepared via microemulsion method.TEM results show that CdTe:Eu3+nanocrystals are uniformly dispersed in the shell,and CdTe:Eu3+@SiO2 nanospheres are uniformly spherical with an average diameter of about 75 nm.The fluorescence emission of CdTe:Eu3+@SiO2(567 nm) shows a blueshift compared with that of CdTe:Eu^3+nanocrystals(632 nm),possibly because of altered surface properties after SiO2 coating.CdTe:Eu^3+and CdTe:Eu^3+@SiO2 with tunable photoluminescence are potentially useful in fabricating optical and bioimaging devices.展开更多
Three Schiff bases of 3-amino-5-mercapto-1,2,4-trizaole have been synthesized:5-benzylideneamino-4H-1,2,4-trizaole-3-thiol(Ia),5-(3-phenylallylideneamino)-4H-1,2,4-triazole-3-thiol(Ib),5-((5-mercapto-4H-1,2,4-triazol-...Three Schiff bases of 3-amino-5-mercapto-1,2,4-trizaole have been synthesized:5-benzylideneamino-4H-1,2,4-trizaole-3-thiol(Ia),5-(3-phenylallylideneamino)-4H-1,2,4-triazole-3-thiol(Ib),5-((5-mercapto-4H-1,2,4-triazol-3-ylimino)methyl)quinolin-8-ol(Ic).These compounds are characterized by UV-Vis,FT-IR,HPLC,1H-NMR and elementary analysis.The fluorescence spectra of compounds is investigated.We obtained different fluorescence spectra and compared the fluorescence of raw materials to products.Results show that the fluorescence is changed correspondingly when introduce the conjugated group.展开更多
A new copper coordination polymer[Cu2I(C7H5N4)2]n(1)with the 3-(pyridin-2-yl)-1,2,4-triazole(Hpt)and copper iodide was synthesized.It crystallizes in the triclinic space group P1 with a=8.6380(9),b=9.2434(9),c=11.8588...A new copper coordination polymer[Cu2I(C7H5N4)2]n(1)with the 3-(pyridin-2-yl)-1,2,4-triazole(Hpt)and copper iodide was synthesized.It crystallizes in the triclinic space group P1 with a=8.6380(9),b=9.2434(9),c=11.8588(12)A,α=99.5890(10)o,β=109.0990(10)o,γ=105.2800(10)o,V=829.25(15)A^3,Dc=2.180 g/cm3,Z=2,F(000)=522,GOOF=1.046,the final R=0.0245 and wR=0.0598.The crystal structure shows that two copper ions are bridged by twoμ2-η1:η0-3-(pyridin-2-yl)-1,2,4-triazole anions and two iodide ions.The coordination environments of the Cu ion are Cu(1)N5 and Cu(2)N2I2,giving distorted square pyramidal geometry and trigon pyramid geometry.The magnetic and fluorescent properties of 1 were studied.展开更多
基金Project supported by Research Foundation of the General Armament Department (2008CD012)
文摘Terpyridine-capped poly（ethylene glycol） （PEG） was synthesized as a novel polymeric ligand and rare earth complex was prepared from Eu（NO3）3 and the telechelic macromolecules. The structure of the complex was characterized by 1H NMR, FT-IR, UV-vis and fluores-cence spectroscopy. Strong fluorescent emission of the complex was observed at 593 and 616 nm upon the excitation of 300 nm. The fluo-rescent emission was quenched upon addition of trace amount of diethyl chlorophosphate （DCP）. And the observed Ksv values for DCP were measured to be 0.568×10^3 and 0.89×10^3 L/mol for quenching at 593 and 616 nm, which indicated the detection limit for DCP was about 0.014 mmol/L. These results showed that the terpyridine-lanthanide complex could be an effective chemosensor with a potential application in the detection of organophosphates.
基金financially supported by the National Natural Science Foundation of China (No.21364007)the Natural Science Foundation of Inner Mongolia (No.2016MS0201)the Program for Young Talents of Science and Technology of Baotou Teachers College (No.01135003)
文摘Eu3+ doped-CdTe(CdTe:Eu3+)nanocrystals were prepared via a facile hydrothermal method,and Eu3+ was successfully incorporated into the crystal lattice of CdTe and measured by X-ray powder diffraction(XRD),transmission electron microscopy(TEM),ultraviolet-visible(UV-Vis) absorption spectroscopy and fluorescence emission.The CdTe:Eu^3+ nanocrystals still have a cubic crystal structure,and the corresponding XRD peaks of CdTe:Eu3+nanocrystals shift to larger angles compared with those of pure CdTe.The CdTe:Eu3+ nanocrystals are monodisperse and the particles size is about 2-4 nm.Compared with pure CdTe,the CdTe:Eu^3+ nanocrystals have larger band gap and thus exhibit blueshift in the emission spectra,which could be accounted for by the energy transfer between Eu^3+ and CdTe.To enhance the stability and functionality of CdTe:Eu3+nanocrystals,the CdTe:Eu3+nanocrystals were coated with SiO2 and the core-shell SiO2-coated CdTe:Eu3+nanocrystals(CdTe:Eu^3+@SiO2) were prepared via microemulsion method.TEM results show that CdTe:Eu3+nanocrystals are uniformly dispersed in the shell,and CdTe:Eu3+@SiO2 nanospheres are uniformly spherical with an average diameter of about 75 nm.The fluorescence emission of CdTe:Eu3+@SiO2(567 nm) shows a blueshift compared with that of CdTe:Eu^3+nanocrystals(632 nm),possibly because of altered surface properties after SiO2 coating.CdTe:Eu^3+and CdTe:Eu^3+@SiO2 with tunable photoluminescence are potentially useful in fabricating optical and bioimaging devices.
文摘Three Schiff bases of 3-amino-5-mercapto-1,2,4-trizaole have been synthesized:5-benzylideneamino-4H-1,2,4-trizaole-3-thiol(Ia),5-(3-phenylallylideneamino)-4H-1,2,4-triazole-3-thiol(Ib),5-((5-mercapto-4H-1,2,4-triazol-3-ylimino)methyl)quinolin-8-ol(Ic).These compounds are characterized by UV-Vis,FT-IR,HPLC,1H-NMR and elementary analysis.The fluorescence spectra of compounds is investigated.We obtained different fluorescence spectra and compared the fluorescence of raw materials to products.Results show that the fluorescence is changed correspondingly when introduce the conjugated group.
基金Supported by the Natural Science Foundation of Hunan Province(2019JJ60021)the Scientific Research Found of Hunan Provincial Education Department of China(17A049)Industry and Research Key Project of Hengyang City(2018k KJ016,2017KJ155,2017KJ193)
文摘A new copper coordination polymer[Cu2I(C7H5N4)2]n(1)with the 3-(pyridin-2-yl)-1,2,4-triazole(Hpt)and copper iodide was synthesized.It crystallizes in the triclinic space group P1 with a=8.6380(9),b=9.2434(9),c=11.8588(12)A,α=99.5890(10)o,β=109.0990(10)o,γ=105.2800(10)o,V=829.25(15)A^3,Dc=2.180 g/cm3,Z=2,F(000)=522,GOOF=1.046,the final R=0.0245 and wR=0.0598.The crystal structure shows that two copper ions are bridged by twoμ2-η1:η0-3-(pyridin-2-yl)-1,2,4-triazole anions and two iodide ions.The coordination environments of the Cu ion are Cu(1)N5 and Cu(2)N2I2,giving distorted square pyramidal geometry and trigon pyramid geometry.The magnetic and fluorescent properties of 1 were studied.