The non-grinding long afterglow material SrAl2O4：Eu^2＋ , Dy^3＋ was prepared by combustion method in home mierowave oven direetly, after dispersant, frother, eomburent, and mineralizer were added into the reacting s...The non-grinding long afterglow material SrAl2O4：Eu^2＋ , Dy^3＋ was prepared by combustion method in home mierowave oven direetly, after dispersant, frother, eomburent, and mineralizer were added into the reacting system. XRD analysis showed that the powders were nearly pure SrAl2O4 phase with few other phases, and the size of the grain was 41.1 nm. Fluoreseenee speetrum results indieated that there were 2 exeitation peaks loeated at 345 and 400 nm, and the emission peak loeated at 516 nm, afterglow lasted up to 30 min or more. The mierowave eombustion method has advantages of less time, low temperature and no grinding process, and the material made by the method has good luminescent property.展开更多
为了讨论H3BO3对S rA l2O4:Eu2+、D y3+、N d3+长余辉发光材料性能的影响,寻找最佳的H3BO3摩尔分数,采用燃烧法以尿素为还原剂在600℃下制备了掺入Eu2+、D y3+、N d3+的S rA l2O4长余辉发光材料.研究了不同摩尔分数的H3BO3对磷光体晶体...为了讨论H3BO3对S rA l2O4:Eu2+、D y3+、N d3+长余辉发光材料性能的影响,寻找最佳的H3BO3摩尔分数,采用燃烧法以尿素为还原剂在600℃下制备了掺入Eu2+、D y3+、N d3+的S rA l2O4长余辉发光材料.研究了不同摩尔分数的H3BO3对磷光体晶体结构、发光光谱、初始亮度和余辉性能的影响.结果表明:随着H3BO3量的增加激发和发射光谱“蓝移”,硼酸的最佳摩尔分数为0.08.可见H3BO3的含量对S rA l2O4:Eu2+、D y3+、N d3+长余辉发光材料的光学性质有很重要的影响.展开更多
基金Project supported by the National Natural Science Foundation of China (20476002)
文摘The non-grinding long afterglow material SrAl2O4：Eu^2＋ , Dy^3＋ was prepared by combustion method in home mierowave oven direetly, after dispersant, frother, eomburent, and mineralizer were added into the reacting system. XRD analysis showed that the powders were nearly pure SrAl2O4 phase with few other phases, and the size of the grain was 41.1 nm. Fluoreseenee speetrum results indieated that there were 2 exeitation peaks loeated at 345 and 400 nm, and the emission peak loeated at 516 nm, afterglow lasted up to 30 min or more. The mierowave eombustion method has advantages of less time, low temperature and no grinding process, and the material made by the method has good luminescent property.
文摘为了讨论H3BO3对S rA l2O4:Eu2+、D y3+、N d3+长余辉发光材料性能的影响,寻找最佳的H3BO3摩尔分数,采用燃烧法以尿素为还原剂在600℃下制备了掺入Eu2+、D y3+、N d3+的S rA l2O4长余辉发光材料.研究了不同摩尔分数的H3BO3对磷光体晶体结构、发光光谱、初始亮度和余辉性能的影响.结果表明:随着H3BO3量的增加激发和发射光谱“蓝移”,硼酸的最佳摩尔分数为0.08.可见H3BO3的含量对S rA l2O4:Eu2+、D y3+、N d3+长余辉发光材料的光学性质有很重要的影响.