18Mn18Cr0.5N steel specimens were preheated at the temperatures from 1100 to 1250°C for 5 min,and then cooled to 950°C and compressed.The cracking behaviors were investigated using optical microscopy and sca...18Mn18Cr0.5N steel specimens were preheated at the temperatures from 1100 to 1250°C for 5 min,and then cooled to 950°C and compressed.The cracking behaviors were investigated using optical microscopy and scanning electron microscopy.The results showed that the hot workability of 18Mn18Cr0.5N steel gradually decreased with increasing preheating temperature between 1100 and 1200°C,and quickly deteriorated up to 1250°C.Above 1200°C,delta ferrite particles appeared in 18Mn18Cr0.5N steel,promoted cavity coalescence on grain boundary,and accelerated surface crack formation during the hot working process.展开更多
A novel process based on centrifugal casting was developed to produce martensitic stainless steel for guideroll materials. Centrifugal casting provides a lower production cost and less of the thermal cracking defects ...A novel process based on centrifugal casting was developed to produce martensitic stainless steel for guideroll materials. Centrifugal casting provides a lower production cost and less of the thermal cracking defects which normally occur in the overlaid welding process. In this study, the effects of Ni on the microstructure and mechanical properties of martensitic stainless steel were investigated. The results show that the addition of Ni resulted in a decrease in the volume fraction of delta ferrite and an increase in the volume fraction of the retained austenite, respectively. Moreover, a tensile strength of 1600 MPa with an elongation of 4% were obtained after tempering at 500℃ for 2 h. These values were higher than those obtained by using the conventional overlaid process.展开更多
Pitting and stress corrosion cracking(SCC) studies on the 316 N stainless steel(SS) weldments in aswelded(AW) and thermally aged(solution annealing(SA), 550C/4 h and 750C/1 h) conditions were carried out in acidic and...Pitting and stress corrosion cracking(SCC) studies on the 316 N stainless steel(SS) weldments in aswelded(AW) and thermally aged(solution annealing(SA), 550C/4 h and 750C/1 h) conditions were carried out in acidic and acidic chloride media. Pitting corrosion and SCC resistance was the highest for SA weldment, which was attributed to homogenization of microstructural and microchemical heterogeneities during solution annealing. SA specimen showed the most stable passive film as compared to AW weldment because of higher amount of delta-ferrite in AW weld metal, which resulted in an increased heterogeneity and inferior SCC resistance in AW. Stability of passive film was found to be adversely affected due to heat treatments(at 550C/4 h and 750C/1 h) because of the precipitation of carbide and sigma phases.展开更多
基金supported by the National Science and Technology Support Plan of China(No.2007BAF02B01-03)
文摘18Mn18Cr0.5N steel specimens were preheated at the temperatures from 1100 to 1250°C for 5 min,and then cooled to 950°C and compressed.The cracking behaviors were investigated using optical microscopy and scanning electron microscopy.The results showed that the hot workability of 18Mn18Cr0.5N steel gradually decreased with increasing preheating temperature between 1100 and 1200°C,and quickly deteriorated up to 1250°C.Above 1200°C,delta ferrite particles appeared in 18Mn18Cr0.5N steel,promoted cavity coalescence on grain boundary,and accelerated surface crack formation during the hot working process.
文摘A novel process based on centrifugal casting was developed to produce martensitic stainless steel for guideroll materials. Centrifugal casting provides a lower production cost and less of the thermal cracking defects which normally occur in the overlaid welding process. In this study, the effects of Ni on the microstructure and mechanical properties of martensitic stainless steel were investigated. The results show that the addition of Ni resulted in a decrease in the volume fraction of delta ferrite and an increase in the volume fraction of the retained austenite, respectively. Moreover, a tensile strength of 1600 MPa with an elongation of 4% were obtained after tempering at 500℃ for 2 h. These values were higher than those obtained by using the conventional overlaid process.
文摘Pitting and stress corrosion cracking(SCC) studies on the 316 N stainless steel(SS) weldments in aswelded(AW) and thermally aged(solution annealing(SA), 550C/4 h and 750C/1 h) conditions were carried out in acidic and acidic chloride media. Pitting corrosion and SCC resistance was the highest for SA weldment, which was attributed to homogenization of microstructural and microchemical heterogeneities during solution annealing. SA specimen showed the most stable passive film as compared to AW weldment because of higher amount of delta-ferrite in AW weld metal, which resulted in an increased heterogeneity and inferior SCC resistance in AW. Stability of passive film was found to be adversely affected due to heat treatments(at 550C/4 h and 750C/1 h) because of the precipitation of carbide and sigma phases.