The presence of stress is shown to have a significant impact on chloride ions in concrete. Reinforced concrete is usually durable and cost-effective which has resulted in its widespread use for construction, however, ...The presence of stress is shown to have a significant impact on chloride ions in concrete. Reinforced concrete is usually durable and cost-effective which has resulted in its widespread use for construction, however, the concrete subjected to environment and load has become increasingly apparently that attacked by aggressive agents such as chloride ion. In this study, the coupling influences are stress effects and environmental problems on the coastline concrete durability have been investigated. A series of cyclic of a wet-dry cycle and submersion tests were performed onto the stressed concrete to obtain an understanding of the physical mechanisms causing the accumulation of chlorides in the interior pores of concrete under different stress types and exposure environments, based on the same duration. Specimens were prepared and subjected to NaCl solution in a wet-dry cycle and submersion, the chloride in the tension zone is gradual with increasing the stress level, as well as the chloride ion in the wet-dry cycle, is increasing the number of cycles. The apparent diffusion coefficient of each specimen was calculated respectively, the profile of concentration at a different section of tension and compression zones were presented in influence factors of the number of cycles, the length of drying phase, and periodic wetting cycles with sodium solution was discussed. After employed Fick’s second law, the results suggested D<sub>a</sub> in a wet-dry cycle is much higher than the D<sub>a</sub> in submersion zones.展开更多
The effect of curing age on chloride diffusion coefficient of recycled aggregate concrete subjected to different compressive stresses was investigated.A compression loading setup was both designed and fabricated.The c...The effect of curing age on chloride diffusion coefficient of recycled aggregate concrete subjected to different compressive stresses was investigated.A compression loading setup was both designed and fabricated.The chloride diffusion coefficients of recycled aggregate concrete under compressive stresses were measured by the rapid chloride ion migration(RCM)method.The experimental results show that the chloride diffusion coefficients of recycled aggregate concrete(RAC)under different compressive stress ratios generally decrease with the increase of curing age.For RAC subjected to the same compressive stress ratios,the chloride diffusion coefficients approximately have power functions with curing ages and the relationship models are proposed.Moreover,the influence of curing age on chloride diffusion coefficient firstly decreases and then increases as the compressive stress ratio increases.展开更多
文摘The presence of stress is shown to have a significant impact on chloride ions in concrete. Reinforced concrete is usually durable and cost-effective which has resulted in its widespread use for construction, however, the concrete subjected to environment and load has become increasingly apparently that attacked by aggressive agents such as chloride ion. In this study, the coupling influences are stress effects and environmental problems on the coastline concrete durability have been investigated. A series of cyclic of a wet-dry cycle and submersion tests were performed onto the stressed concrete to obtain an understanding of the physical mechanisms causing the accumulation of chlorides in the interior pores of concrete under different stress types and exposure environments, based on the same duration. Specimens were prepared and subjected to NaCl solution in a wet-dry cycle and submersion, the chloride in the tension zone is gradual with increasing the stress level, as well as the chloride ion in the wet-dry cycle, is increasing the number of cycles. The apparent diffusion coefficient of each specimen was calculated respectively, the profile of concentration at a different section of tension and compression zones were presented in influence factors of the number of cycles, the length of drying phase, and periodic wetting cycles with sodium solution was discussed. After employed Fick’s second law, the results suggested D<sub>a</sub> in a wet-dry cycle is much higher than the D<sub>a</sub> in submersion zones.
基金supported by the Fundamental Research Funds for the Central UniversitiesFoundation of Graduate Innovation Center in Nanjing University of Aeronautics and Astronautics (No.kfjj20150105)the National Natural Science Foundation of China (No. 51279074)
文摘The effect of curing age on chloride diffusion coefficient of recycled aggregate concrete subjected to different compressive stresses was investigated.A compression loading setup was both designed and fabricated.The chloride diffusion coefficients of recycled aggregate concrete under compressive stresses were measured by the rapid chloride ion migration(RCM)method.The experimental results show that the chloride diffusion coefficients of recycled aggregate concrete(RAC)under different compressive stress ratios generally decrease with the increase of curing age.For RAC subjected to the same compressive stress ratios,the chloride diffusion coefficients approximately have power functions with curing ages and the relationship models are proposed.Moreover,the influence of curing age on chloride diffusion coefficient firstly decreases and then increases as the compressive stress ratio increases.